Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/mĀ²
558 Compounds found
Recommended Ā 
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMIDĀ®

B3 GF 50 2 S1 black (3050)

PA6-I GF50

AKROMIDĀ® B3 GF 50 2 S1 black (3050) - PA 6, 50% glass fiber reinforced, impact modified, UV stabilised, housings and covers, automotive


Modulus

15.000MPa

Strength

195MPa

Impact

110kJ/mĀ²

AKROMIDĀ® B3 GF 50 2 S1 black (3050) - PA 6, 50% glass fiber reinforced, impact modified, UV stabilised, housings and covers, automotive

AKROMIDĀ®

Preliminary

T5 ICF 10 black (6772)

PPA CF10

AKROMIDĀ® T5 ICF 10 black (6772) is a 10% carbon fibre reinforced polyphthalamide with good flexural strength and good sliding properties


Modulus

12.000MPa

Strength

150MPa

Impact

25kJ/mĀ²

AKROMIDĀ® T5 ICF 10 black (6772) is a 10% carbon fibre reinforced polyphthalamide with good flexural strength and good sliding properties

AKROMIDĀ®

Preliminary

T5 GF 20 8 black (6456)

PPA GF20

AKROMIDĀ® T5 GF 20 8 black (6456) - PPA, 20% glass fiber, food contact, kitchen and household appliances, fitting, water meter, ACS, WRAS, NSF 61, EU 10/2011, FDA


Modulus

8.500MPa

Strength

160MPa

Impact

40kJ/mĀ²

AKROMIDĀ® T5 GF 20 8 black (6456) - PPA, 20% glass fiber, food contact, kitchen and household appliances, fitting, water meter, ACS, WRAS, NSF 61, EU 10/2011, FDA

AKROMIDĀ®

Preliminary

B25 GF 60 natural (8326)

PA6 GF60

AKROMIDĀ® B25 GF 60 natural (8326) - PA 6, easy flow, very high stiffness and strength, mechanical engineering, automotive.


Modulus

22.000MPa

Strength

255MPa

Impact

100kJ/mĀ²

AKROMIDĀ® B25 GF 60 natural (8326) - PA 6, easy flow, very high stiffness and strength, mechanical engineering, automotive.

AKROMIDĀ®

B3 ICF 20 1 L black (5296)

PA6 + PP CF20

AKROMIDĀ® B3 ICF 20 1 L black (5296) is a 20% carbon fibre reinforced, heat stabilised polyamide-blend with high flexural strength, good sliding properties and a reduced density compared to standard PA6 ICF 20


Modulus

14.200MPa

Strength

140MPa

Impact

50kJ/mĀ²

AKROMIDĀ® B3 ICF 20 1 L black (5296) is a 20% carbon fibre reinforced, heat stabilised polyamide-blend with high flexural strength, good sliding properties and a reduced density compared to standard PA6 ICF 20

AKROTEKĀ®

Preliminary

PK-VM GF 30 8 black (8783)

PK GF30

AKROTEKĀ® PK-VM GF 30 8 black (8783) - Polyketon, 30% glass fiber, Tribology, friction and wear, chemical resistance, food contact


Modulus

8.100MPa

Strength

130MPa

Impact

65kJ/mĀ²

AKROTEKĀ® PK-VM GF 30 8 black (8783) - Polyketon, 30% glass fiber, Tribology, friction and wear, chemical resistance, food contact

AKROTEKĀ®

Preliminary

PK-VM GF 10 FR orange (8745)

PK GF10 FR(40)

AKROTEKĀ® PK-VM GF 10 FR orange (8745) - Polyketon, 10% GF, chemical and hydrolysis resistance, flame retardant, halogen free, orange RAL 2003, process improved, good dimensional stability. high voltage components, e-mobility.


Modulus

4.000MPa

Strength

70MPa

Impact

48kJ/mĀ²

AKROTEKĀ® PK-VM GF 10 FR orange (8745) - Polyketon, 10% GF, chemical and hydrolysis resistance, flame retardant, halogen free, orange RAL 2003, process improved, good dimensional stability. high voltage components, e-mobility.

177787980

PRECITEĀ®

P3 GF 30 black (6924)PBT GF 30

PRECITEĀ® P3 GF 30 black (6924) is a 30% glass fibre reinforced, medium viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

Properties

Modulus

10.000MPa

Strength

145MPa

Impact

68kJ/mĀ²

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
10000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
145 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
3,2 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
10500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
230 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
68 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
11 kJ/mĀ²

Thermal Properties


Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
205 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
225 Ā°C

Flammability


Burning rate

UL 94

0,8 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
725 Ā°C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties


Density

ISO 1183

23Ā°C
1,53 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
0,1 - 0,3 %

Water absorption

ISO 62

23Ā°C, saturated
0,4 %

Molding shrinkage

ISO 294-4

flow
transverse
0,2 - 0,4 %
0,8 - 1,0 %

Electrical Properties


Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
> 1013 ā„¦ x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
> 1015 ā„¦

Rheological Properties


MVR

ISO 1133

250Ā°C/2,16kg
9 cmĀ³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.