T5 GF 20 8 black (6456)

PPA GF20

AKROMIDĀ® T5 GF 20 8 black (6456) - PPA, 20% glass fiber, food contact, kitchen and household appliances, fitting, water meter, ACS, WRAS, NSF 61, EU 10/2011, FDA

Modulus

8.500MPa

Strength

160MPa

Impact

40kJ/mĀ²

AKROMIDĀ® T5 GF 20 8 black (6456) - PPA, 20% glass fiber, food contact, kitchen and household appliances, fitting, water meter, ACS, WRAS, NSF 61, EU 10/2011, FDA

AKROMIDĀ®

B3 ICF 20 1 L black (5296)

PA6 + PP CF20

AKROMIDĀ® B3 ICF 20 1 L black (5296) is a 20% carbon fibre reinforced, heat stabilised polyamide-blend with high flexural strength, good sliding properties and a reduced density compared to standard PA6 ICF 20

Modulus

14.200MPa

Strength

140MPa

Impact

50kJ/mĀ²

AKROMIDĀ® B3 ICF 20 1 L black (5296) is a 20% carbon fibre reinforced, heat stabilised polyamide-blend with high flexural strength, good sliding properties and a reduced density compared to standard PA6 ICF 20

AKROMIDĀ®

B3 GF 50 2 S1 black (3050)

PA6-I GF50

AKROMIDĀ® B3 GF 50 2 S1 black (3050) - PA 6, 50% glass fiber reinforced, impact modified, UV stabilised, housings and covers, automotive

Modulus

15.000MPa

Strength

195MPa

Impact

110kJ/mĀ²

AKROMIDĀ® B3 GF 50 2 S1 black (3050) - PA 6, 50% glass fiber reinforced, impact modified, UV stabilised, housings and covers, automotive

AKROMIDĀ®

Preliminary

T5 ICF 10 black (6772)

PPA CF10

AKROMIDĀ® T5 ICF 10 black (6772) is a 10% carbon fibre reinforced polyphthalamide with good flexural strength and good sliding properties

Modulus

12.000MPa

Strength

150MPa

Impact

25kJ/mĀ²

AKROMIDĀ® T5 ICF 10 black (6772) is a 10% carbon fibre reinforced polyphthalamide with good flexural strength and good sliding properties

AKROMIDĀ®

Preliminary

B25 GF 60 natural (8326)

PA6 GF60

AKROMIDĀ® B25 GF 60 natural (8326) - PA 6, easy flow, very high stiffness and strength, mechanical engineering, automotive.

Modulus

22.000MPa

Strength

255MPa

Impact

100kJ/mĀ²

AKROMIDĀ® B25 GF 60 natural (8326) - PA 6, easy flow, very high stiffness and strength, mechanical engineering, automotive.

AKROMIDĀ®

Preliminary

NEXT B28 GF 30 9 FR black (8342BMBCI)

PA6 GF30 FR(40)

AKROMIDĀ® NEXT B28 GF 30 9 FR schwarz (8342BMBCI) - PA6, 30% glass fibre, sustainable, biomass-balanced, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, V0 from 1,6 mm, e-mobility.

Modulus

10.200MPa

Strength

148MPa

Impact

75kJ/mĀ²

AKROMIDĀ® NEXT B28 GF 30 9 FR schwarz (8342BMBCI) - PA6, 30% glass fibre, sustainable, biomass-balanced, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, V0 from 1,6 mm, e-mobility.

AKROTEKĀ®

Preliminary

PK-VM GF 30 8 black (8783)

PK GF30

AKROTEKĀ® PK-VM GF 30 8 black (8783) - Polyketon, 30% glass fiber, Tribology, friction and wear, chemical resistance, food contact

Modulus

8.100MPa

Strength

130MPa

Impact

65kJ/mĀ²

AKROTEKĀ® PK-VM GF 30 8 black (8783) - Polyketon, 30% glass fiber, Tribology, friction and wear, chemical resistance, food contact

177787980

AKROMIDĀ®

A3 ICF 30 5 black (6495)PA66 CF30

AKROMIDĀ® A3 ICF 30 5 black (6495) is a 30% carbon fibre reinforced, high heat stabilised polyamide 6.6 with high flexural strength and good sliding properties

Features

heat stabilised 230

Properties

Modulus

23.000MPa

Strength

235MPa

Impact

50kJ/mĀ²

Sustainability

Recycled content

30 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
23000 MPa
14500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
235 MPa
165 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
1,8 %
3 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
22000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
370 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2,5 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
50 kJ/mĀ²
65 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
30Ā°C | conditioned
-
8 kJ/mĀ²
11 kJ/mĀ²
6 kJ/mĀ²
6 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
250 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 Ā°C

Coefficient of linear thermal expansion

ISO 11359-1/2

23Ā°C to 80Ā°C | parallel
23Ā°C to 80Ā°C | transverse
0,06 10ā»ā“/K
0,72 10ā»ā“/K

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,27 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,9 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
104 ā„¦ x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
104 ā„¦

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more