HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/mĀ²
558 Compounds found
Recommended Ā 
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMIDĀ®

Preliminary

T5 GF 20 8 black (6456)

PPA GF20

AKROMIDĀ® T5 GF 20 8 black (6456) - PPA, 20% glass fiber, food contact, kitchen and household appliances, fitting, water meter, ACS, WRAS, NSF 61, EU 10/2011, FDA

Modulus

8.500MPa

Strength

160MPa

Impact

40kJ/mĀ²

AKROMIDĀ® T5 GF 20 8 black (6456) - PPA, 20% glass fiber, food contact, kitchen and household appliances, fitting, water meter, ACS, WRAS, NSF 61, EU 10/2011, FDA

AKROMIDĀ®

B3 GF 50 2 S1 black (3050)

PA6-I GF50

AKROMIDĀ® B3 GF 50 2 S1 black (3050) - PA 6, 50% glass fiber reinforced, impact modified, UV stabilised, housings and covers, automotive

Modulus

15.000MPa

Strength

195MPa

Impact

110kJ/mĀ²

AKROMIDĀ® B3 GF 50 2 S1 black (3050) - PA 6, 50% glass fiber reinforced, impact modified, UV stabilised, housings and covers, automotive

AKROMIDĀ®

Preliminary

T5 ICF 10 black (6772)

PPA CF10

AKROMIDĀ® T5 ICF 10 black (6772) is a 10% carbon fibre reinforced polyphthalamide with good flexural strength and good sliding properties

Modulus

12.000MPa

Strength

150MPa

Impact

25kJ/mĀ²

AKROMIDĀ® T5 ICF 10 black (6772) is a 10% carbon fibre reinforced polyphthalamide with good flexural strength and good sliding properties

AKROMIDĀ®

B3 ICF 20 1 L black (5296)

PA6 + PP CF20

AKROMIDĀ® B3 ICF 20 1 L black (5296) is a 20% carbon fibre reinforced, heat stabilised polyamide-blend with high flexural strength, good sliding properties and a reduced density compared to standard PA6 ICF 20

Modulus

14.200MPa

Strength

140MPa

Impact

50kJ/mĀ²

AKROMIDĀ® B3 ICF 20 1 L black (5296) is a 20% carbon fibre reinforced, heat stabilised polyamide-blend with high flexural strength, good sliding properties and a reduced density compared to standard PA6 ICF 20

AKROMIDĀ®

Preliminary

B25 GF 60 natural (8326)

PA6 GF60

AKROMIDĀ® B25 GF 60 natural (8326) - PA 6, easy flow, very high stiffness and strength, mechanical engineering, automotive.

Modulus

22.000MPa

Strength

255MPa

Impact

100kJ/mĀ²

AKROMIDĀ® B25 GF 60 natural (8326) - PA 6, easy flow, very high stiffness and strength, mechanical engineering, automotive.

AKROMIDĀ®

UL

C3 GF 25 1 FR grey (8605)

PA66+PA6 GF25 FR(40)

AKROMIDĀ® C3 GF 25 1 FR grey (8605) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, automotive, E&E.

Modulus

9.100MPa

Strength

125MPa

Impact

50kJ/mĀ²

AKROMIDĀ® C3 GF 25 1 FR grey (8605) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, automotive, E&E.

AKROMIDĀ®

A3 GF 25 9 FR black (7957)

PA66 GF25 FR(40)

AKROMIDĀ® A3 GF 25 9 FR black (7957) is a 25% glass fibre reinforced, halogen free flame retardant polyamide 6.6.

Modulus

9.000MPa

Strength

140MPa

Impact

65kJ/mĀ²

AKROMIDĀ® A3 GF 25 9 FR black (7957) is a 25% glass fibre reinforced, halogen free flame retardant polyamide 6.6.

177787980

AKROMIDĀ®

B3 GF 25 1 L black (4637)PA6+PP GF25

AKROMIDĀ® B3 GF 25 1 L black (4637) is a PA6/PP-blend with reduced density compared to standard PA6 with 25% glass fibre reinforcement. The material is suitable for components with high strength and stiffness where cost and weight reduction are required at the same time. The chemical resistance of AKROMIDĀ® B3 GF 25 1 L black (4637) is particularly superior to calcium chloride (CaClā‚‚).

Features

heat stabilised 130
reduced density

Properties

Modulus

7.500MPa

Strength

135MPa

Impact

68kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
7500 MPa
5600 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
135 MPa
88 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,3 %
4,5 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
30Ā°C | conditioned
-
68 kJ/mĀ²
58 kJ/mĀ²
67 kJ/mĀ²
54 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
30Ā°C | conditioned
-
15 kJ/mĀ²
15 kJ/mĀ²
13 kJ/mĀ²
10 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
198 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
217 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 Ā°C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
750 Ā°C
725 Ā°C
750 Ā°C

GWIT

IEC 60695-2-13

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
775 Ā°C
750 Ā°C
775 Ā°C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,22 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,55 - 0,75 %

Rheological Properties

MVR

ISO 1133

275Ā°C/5kg
10 cmĀ³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.