AKROMID®

B3 GF 50 2 S1 black (3050)

PA6-I GF50

AKROMID® B3 GF 50 2 S1 black (3050) - PA 6, 50% glass fiber reinforced, impact modified, UV stabilised, housings and covers, automotive

Modulus

15.000MPa

Strength

195MPa

Impact

110kJ/m²

AKROMID® B3 GF 50 2 S1 black (3050) - PA 6, 50% glass fiber reinforced, impact modified, UV stabilised, housings and covers, automotive

AKROMID®

Preliminary

T5 GF 20 8 black (6456)

PPA GF20

AKROMID® T5 GF 20 8 black (6456) - PPA, 20% glass fiber, food contact, kitchen and household appliances, fitting, water meter, ACS, WRAS, NSF 61, EU 10/2011, FDA

Modulus

8.500MPa

Strength

160MPa

Impact

40kJ/m²

AKROMID® T5 GF 20 8 black (6456) - PPA, 20% glass fiber, food contact, kitchen and household appliances, fitting, water meter, ACS, WRAS, NSF 61, EU 10/2011, FDA

AKROMID®

Preliminary

T5 ICF 10 black (6772)

PPA CF10

AKROMID® T5 ICF 10 black (6772) is a 10% carbon fibre reinforced polyphthalamide with good flexural strength and good sliding properties

Modulus

12.000MPa

Strength

150MPa

Impact

25kJ/m²

AKROMID® T5 ICF 10 black (6772) is a 10% carbon fibre reinforced polyphthalamide with good flexural strength and good sliding properties

AKROMID®

B3 ICF 20 1 L black (5296)

PA6 + PP CF20

AKROMID® B3 ICF 20 1 L black (5296) is a 20% carbon fibre reinforced, heat stabilised polyamide-blend with high flexural strength, good sliding properties and a reduced density compared to standard PA6 ICF 20

Modulus

14.200MPa

Strength

140MPa

Impact

50kJ/m²

AKROMID® B3 ICF 20 1 L black (5296) is a 20% carbon fibre reinforced, heat stabilised polyamide-blend with high flexural strength, good sliding properties and a reduced density compared to standard PA6 ICF 20

AKROMID®

Preliminary

B25 GF 60 natural (8326)

PA6 GF60

AKROMID® B25 GF 60 natural (8326) - PA 6, easy flow, very high stiffness and strength, mechanical engineering, automotive.

Modulus

22.000MPa

Strength

255MPa

Impact

100kJ/m²

AKROMID® B25 GF 60 natural (8326) - PA 6, easy flow, very high stiffness and strength, mechanical engineering, automotive.

AKROMID®

UL

C3 GF 25 1 FR grey (8605)

PA66+PA6 GF25 FR(40)

AKROMID® C3 GF 25 1 FR grey (8605) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, automotive, E&E.

Modulus

9.100MPa

Strength

125MPa

Impact

50kJ/m²

AKROMID® C3 GF 25 1 FR grey (8605) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, automotive, E&E.

AKROMID®

UL
Preliminary

NEXT S3 GF 15 1 HU natural (8822)

PA6.10 GF15

AKROMID® NEXT S3 GF 15 1 HU natural (8822) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

Modulus

5.000MPa

Strength

110MPa

Impact

75kJ/m²

AKROMID® NEXT S3 GF 15 1 HU natural (8822) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, household, industrial application.

177787980

AKROMID®

A3 S3 natural (1176)PA66-I

AKROMID® A3 S3 natural (1176) is an unreinforced, dry impact modified Polyamide 6.6. The material is characterised by a very high impact strength and therefore perfectly suitable for connecting and fixing systems which are used in the automotive and electro industry and that are exposed to high loading speeds. The material has a light inherent color.

Features

impact modified

Properties

Modulus

2.800MPa

Strength

67MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
2800 MPa
1700 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
67 MPa
45 MPa

Tensile strain at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
6 %
26 %

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
> 30 %
> 50 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
2850 MPa
1600 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
no break
no break
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
17 kJ/m²
95 kJ/m²
8 kJ/m²

Ball indentation hardness

ISO 2039-1

358N/30s | d.a.m.
93 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
67 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
213 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
263 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,1 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,1 %

Molding shrinkage

ISO 294-4

flow
transverse
1,8 %
2,1 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
1015 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1014 Ω

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.