AKROLOYĀ®

Preliminary

PA GF 60 LA black (8168)

PA66 + PA6I/6T GF60

AKROLOYĀ® PA GF 60 LA black (8168) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

Modulus

21.400MPa

Strength

275MPa

Impact

95kJ/mĀ²

AKROLOYĀ® PA GF 60 LA black (8168) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

AKROMIDĀ®

Preliminary

NEXT U28 ICF 40 1 black (8238)

PA11 CF40

AKROMIDĀ® NEXT U28 ICF 40 1 black (8238) - PA11 made of renewable raw materials, recycled carbon fibre, low density, 3D printing of large parts

Modulus

20.000MPa

Strength

190MPa

Impact

80kJ/mĀ²

AKROMIDĀ® NEXT U28 ICF 40 1 black (8238) - PA11 made of renewable raw materials, recycled carbon fibre, low density, 3D printing of large parts

AKROLENĀ®

Preliminary

PP ICF 30 AM black (8344)

PP CF30

AKROLENĀ® PP ICF 30 AM black (8344) - recycled carbon fibre reinforced polypropylene for additive manufacturing (3D-printing)

Modulus

12.500MPa

Strength

85MPa

Impact

50kJ/mĀ²

AKROLENĀ® PP ICF 30 AM black (8344) - recycled carbon fibre reinforced polypropylene for additive manufacturing (3D-printing)

AKROMIDĀ®

B28 GF 30 S3 black (8438)

PA6-I GF30

AKROMIDĀ® B28 GF 30 S3 black (8438) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

Modulus

9.000MPa

Strength

155MPa

Impact

100kJ/mĀ²

AKROMIDĀ® B28 GF 30 S3 black (8438) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

AKROTEKĀ®

Preliminary

PPS CF 30 black (8612)

PPS CF30

AKROTEKĀ® PPS CF 30 black (8612) is a 30% carbon fibre reinforced, Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

Modulus

28.000MPa

Strength

230MPa

Impact

35kJ/mĀ²

AKROTEKĀ® PPS CF 30 black (8612) is a 30% carbon fibre reinforced, Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

AKROTEKĀ®

Preliminary

AM ICF 20 black (8723)

ASACF20

AKROTEKĀ® AM ICF 20 black (8723) - recycled carbon fibre reinforced for additive manufacturing (3D-printing)

Modulus

13.400MPa

Strength

105MPa

Impact

25kJ/mĀ²

AKROTEKĀ® AM ICF 20 black (8723) - recycled carbon fibre reinforced for additive manufacturing (3D-printing)

AKROMIDĀ®

A3 S3 natural (1176)

PA66-I

AKROMIDĀ® A3 S3 natural (1176) - PA 6.6, unreinforced, dry impact modified, for connecting and fixing systems, automotive, E&E

Modulus

2.800MPa

Strength

67MPa

Impact

180kJ/mĀ²

AKROMIDĀ® A3 S3 natural (1176) - PA 6.6, unreinforced, dry impact modified, for connecting and fixing systems, automotive, E&E

176777880

AKROTEKĀ®

PK-VM GF 30 black (8655)PK GF30

AKROTEKĀ® PK-VM GF 30 black (8655) is a 30% glass fiber reinforced Polyketone with average stiffness and strength. Due to its very good media resistance, the material is suitable for the use in applications that carry cooling water. The material can be laser marked. This type was developed as the successor to PK-VM GF 30 black (4896) in order to meet the requirements for a larger processing window during processing.

Features

hydrolysis / chemically stabilised
E-Mobility

Properties

Modulus

8.500MPa

Strength

130MPa

Impact

70kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
8500 MPa
8200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
130 MPa
130 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,0 %
3,0 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
8200 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
210 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
30Ā°C | d.a.m.
-
40Ā°C | d.a.m.
-
70 kJ/mĀ²
75 kJ/mĀ²
70 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
40Ā°C | d.a.m.
-
11 kJ/mĀ²
14 kJ/mĀ²
11 kJ/mĀ²
10 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
215 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 Ā°C

Coefficient of linear thermal expansion

ISO 11359-1/2

23Ā°C to 80Ā°C | parallel
23Ā°C to 80Ā°C | transverse
0,18 10ā»ā“/K
1,16 10ā»ā“/K

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
1,6 mm Wall thickness
725 Ā°C
725 Ā°C

HWI

UL 746A

1,6 mm Wall thickness
1 PLC

General properties

Density

ISO 1183

23Ā°C
1,48 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
0,6 - 0,7 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 - 0,5 %
0,8 - 1,0 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
1013 ā„¦ x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1012 ā„¦

Comparative tracking index

IEC 60112

Test liquid A
600 V

Rheological Properties

MVR

ISO 1133

240Ā°C/2,16kg
4 cmĀ³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more