AKROTEK®

Preliminary

PK-VM GF 10 natural (8679)

PK GF10

AKROTEK® PK-VM GF 10 natural (8679) - Polyketon, 10% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

3.600MPa

Strength

75MPa

Impact

61kJ/m²

AKROTEK® PK-VM GF 10 natural (8679) - Polyketon, 10% glass fibre reinforced, chemical and hydrolysis resistance

AKROTEK®

Preliminary

PPS CF 30 black (8612)

PPS CF30

AKROTEK® PPS CF 30 black (8612) is a 30% carbon fibre reinforced, Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

Modulus

28.000MPa

Strength

230MPa

Impact

35kJ/m²

AKROTEK® PPS CF 30 black (8612) is a 30% carbon fibre reinforced, Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

AKROTEK®

Preliminary

PK-VM GF 15 natural (8680)

PK GF15

AKROTEK® PK-VM GF 15 natural (8680) - Polyketon, 15% glass fiber reinforced, chemical and hydrolysis resistance

Modulus

4.600MPa

Strength

100MPa

Impact

65kJ/m²

AKROTEK® PK-VM GF 15 natural (8680) - Polyketon, 15% glass fiber reinforced, chemical and hydrolysis resistance

AKROMID®

B3 GF 30 1 grey (7574)

PA6 GF30

AKROMID® B3 GF 30 1 grey (7574) is a 30% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength

Modulus

9.900MPa

Strength

168MPa

Impact

NA

AKROMID® B3 GF 30 1 grey (7574) is a 30% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength

AKROTEK®

Preliminary

PK-VM GF 20 natural (8681)

PK GF20

AKROTEK® PK-VM GF 20 natural (8681) - Polyketon, 20% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

5.700MPa

Strength

117MPa

Impact

65kJ/m²

AKROTEK® PK-VM GF 20 natural (8681) - Polyketon, 20% glass fibre reinforced, chemical and hydrolysis resistance

AKROTEK®

Preliminary

AM ICF 20 black (8723)

ASACF20

AKROTEK® AM ICF 20 black (8723) - recycled carbon fibre reinforced for additive manufacturing (3D-printing)

Modulus

13.400MPa

Strength

105MPa

Impact

25kJ/m²

AKROTEK® AM ICF 20 black (8723) - recycled carbon fibre reinforced for additive manufacturing (3D-printing)

AKROMID®

A3 S3 natural (1176)

PA66-I

AKROMID® A3 S3 natural (1176) - PA 6.6, unreinforced, dry impact modified, for connecting and fixing systems, automotive, E&E

Modulus

2.800MPa

Strength

67MPa

Impact

180kJ/m²

AKROMID® A3 S3 natural (1176) - PA 6.6, unreinforced, dry impact modified, for connecting and fixing systems, automotive, E&E

176777880

PRECITE®

Preliminary

P3 GF 30 9 FR natural (8053)PBT GF30 FR(40)

PRECITE® P3 GF 30 9 FR natural (8053) is a 30% glass fibre reinforced, flame retardant polybutylene terephthalate (PBT) with high stiffness and strength. The material offers outstanding long-term heat-aging stability as well as mechanical advantages to conventional products. It achieves V0 classification at thicknesses of 1.6 mm and above by using a flame retardant system which is free of red phosphorous and halogens. Due to its low moisture absorption, this material has very good dimensional stability and it is particularly suitable for precision parts in E-Mobility or E&E industry.

Features

heat stabilised 130
flame retardant
low warpage
E&E
E-Mobility

Properties

Modulus

10.500MPa

Strength

122MPa

Impact

50kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
10500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
122 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2,4 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
10500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
197 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2,6 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
30°C | d.a.m.
-
50 kJ/m²
59 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
30°C | d.a.m.
-
9 kJ/m²
9 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
205 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
222 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
224 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
V-0 Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
1,6 mm Wall thickness
960 °C
960 °C

GWIT

IEC 60695-2-13

0,8 mm Wall thickness
1,6 mm Wall thickness
750 °C
750 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

Oxygen index

ISO 4589-2

> 30 %

General properties

Density

ISO 1183

23°C
1,53 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,1 - 0,3 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
350 V

Rheological Properties

MVR

ISO 1133

275°C/2,16kg
25,5 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more