PK-VM GF 20 natural (8681)

PK GF20

AKROTEK® PK-VM GF 20 natural (8681) - Polyketon, 20% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

5.700MPa

Strength

117MPa

Impact

65kJ/m²

AKROTEK® PK-VM GF 20 natural (8681) - Polyketon, 20% glass fibre reinforced, chemical and hydrolysis resistance

AKROTEK®

Preliminary

PPS CF 30 black (8612)

PPS CF30

AKROTEK® PPS CF 30 black (8612) is a 30% carbon fibre reinforced, Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

Modulus

28.000MPa

Strength

230MPa

Impact

35kJ/m²

AKROTEK® PPS CF 30 black (8612) is a 30% carbon fibre reinforced, Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

AKROTEK®

Preliminary

PPS GF 40 natural (8064)

PPS GF40

AKROTEK® PPS GF 40 natural (8064) is a 40% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

Modulus

12.000MPa

Strength

190MPa

Impact

50kJ/m²

AKROTEK® PPS GF 40 natural (8064) is a 40% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

AKROTEK®

Preliminary

PPS GF 40 black (8609)

PPS GF40

AKROTEK® PPS GF 40 black (8609) is a 40% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

Modulus

16.000MPa

Strength

180MPa

Impact

50kJ/m²

AKROTEK® PPS GF 40 black (8609) is a 40% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

AKROTEK®

Preliminary

PK-VM GF 10 natural (8679)

PK GF10

AKROTEK® PK-VM GF 10 natural (8679) - Polyketon, 10% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

3.600MPa

Strength

75MPa

Impact

61kJ/m²

AKROTEK® PK-VM GF 10 natural (8679) - Polyketon, 10% glass fibre reinforced, chemical and hydrolysis resistance

AKROTEK®

Preliminary

AM ICF 20 black (8723)

ASACF20

AKROTEK® AM ICF 20 black (8723) - recycled carbon fibre reinforced for additive manufacturing (3D-printing)

Modulus

13.400MPa

Strength

105MPa

Impact

25kJ/m²

AKROTEK® AM ICF 20 black (8723) - recycled carbon fibre reinforced for additive manufacturing (3D-printing)

AKROMID®

A3 S3 natural (1176)

PA66-I

AKROMID® A3 S3 natural (1176) - PA 6.6, unreinforced, dry impact modified, for connecting and fixing systems, automotive, E&E

Modulus

2.800MPa

Strength

67MPa

Impact

180kJ/m²

AKROMID® A3 S3 natural (1176) - PA 6.6, unreinforced, dry impact modified, for connecting and fixing systems, automotive, E&E

176777880

AKROLOY®

UL
Internal

PA GF 60 7 black (2844)PA6+PA6I/6T GF60

AKROLOY® PA GF 60 7 black (2844) is a 60% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state. The advanced version of this Product is AKROLOY® PA GF 60 black (6418) with a modern stabilization technology, featuring improved weld-line strength and an even wider process window. UL listed grade.

Regulatory

ul

Properties

Modulus

22.000MPa

Strength

275MPa

Impact

90kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
22000 MPa
20000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
275 MPa
210 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,5 %
3,3 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
23000 MPa
21200 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
435 MPa
370 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
90 kJ/m²
90 kJ/m²
95 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
18 kJ/m²
17 kJ/m²
18 kJ/m²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
330 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
240 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
245 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
200 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
255 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel
23°C to 80°C | transverse
0,15 10⁻⁴/K
0,55 10⁻⁴/K

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
140 - 150 °C
110 - 130 °C

Flammability

Burning rate

UL 94

UL
0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,72 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,1 %

Molding shrinkage

ISO 294-4

flow
transverse
0,0 - 0,2 %
0,2 - 0,4 %

Electrical Properties

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1017 Ω

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.