AKROMID®

Preliminary

A3 black (7557)

PA66

AKROMID® A3 black (7557) is an unreinforced, UV stabilised polyamide 6.6.

Modulus

3.200MPa

Strength

80MPa

Impact

180kJ/m²

AKROMID® A3 black (7557) is an unreinforced, UV stabilised polyamide 6.6.

AKROMID®

UL

C3 GF 30 1 FR orange (7855)

PA6+PA66 GF30 FR(40)

AKROMID® C3 GF 30 1 FR orange (7855) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, RAL 2003, E&E, Public transportation EN 45545-2.

Modulus

10.600MPa

Strength

135MPa

Impact

65kJ/m²

AKROMID® C3 GF 30 1 FR orange (7855) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, RAL 2003, E&E, Public transportation EN 45545-2.

AKROTEK®

PK-VM GF 10 grey (7344)

PK GF10

AKROTEK® PK-VM GF 10 grey (7344) - Polyketon, 10% glass fiber reinforced, chemical resistance, RAL 7044

Modulus

3.600MPa

Strength

65MPa

Impact

50kJ/m²

AKROTEK® PK-VM GF 10 grey (7344) - Polyketon, 10% glass fiber reinforced, chemical resistance, RAL 7044

AKROMID®

UL

B3 GF 35 1 HU red (8416)

PA6 GF35

AKROMID® B3 GF 35 1 HU red (8416) - PA 6, 35% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB.

Modulus

12.000MPa

Strength

190MPa

Impact

NA

AKROMID® B3 GF 35 1 HU red (8416) - PA 6, 35% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB.

AKROTEK®

Preliminary

PPS GF 40 natural (8064)

PPS GF40

AKROTEK® PPS GF 40 natural (8064) is a 40% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

Modulus

12.000MPa

Strength

190MPa

Impact

50kJ/m²

AKROTEK® PPS GF 40 natural (8064) is a 40% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

AKROMID®

B3 GF 30 1 grey (7574)

PA6 GF30

AKROMID® B3 GF 30 1 grey (7574) is a 30% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength

Modulus

9.900MPa

Strength

168MPa

Impact

NA

AKROMID® B3 GF 30 1 grey (7574) is a 30% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength

AKROTEK®

Preliminary

AM ICF 20 black (8723)

ASACF20

AKROTEK® AM ICF 20 black (8723) - recycled carbon fibre reinforced for additive manufacturing (3D-printing)

Modulus

13.400MPa

Strength

105MPa

Impact

25kJ/m²

AKROTEK® AM ICF 20 black (8723) - recycled carbon fibre reinforced for additive manufacturing (3D-printing)

174757680

AKROMID®

Preliminary
Internal

NEXT 5.6 3 GF 35 9 FR natural (8401)PA56 GF35 FR(40)

AKROMID® NEXT 5.6 3 GF 35 9 FR natural (8401) is a partially bio-based and flame retardant PA 5.6 and meets the requirement according to UL94 V0 @ 1.6 mm. The flame-retardant system is free of red phosphorus and halogens. PA 5.6 is a HMD-free (hexamethylenediamine) alternative to PA 6.6. With 35% glass fibre reinforcement, the material is suitable for components with high strength requirements for E&E and E-Mobility, such as busbar supports, switches, terminal strips and connector housings.

Features

Bio-based
heat stabilised 130
flame retardant
E&E

Properties

Modulus

12.000MPa

Strength

160MPa

Impact

71kJ/m²

Sustainability

Biobased carbon content

35 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
12000 MPa
7200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
160 MPa
105 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,5 %
4,1 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
12500 MPa
7700 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
255 MPa
160 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
2,8 %
4,0 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
71 kJ/m²
70 kJ/m²
69 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
12 kJ/m²
15 kJ/m²
11 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
230 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
254 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
3,2 mm Wall thickness
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
1,6 mm Wall thickness
960 °C
900 °C

GWIT

IEC 60695-2-13

0,8 mm Wall thickness
1,6 mm Wall thickness
725 °C
725 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,43 g/cm³

Water absorption

ISO 62

23°C, saturated
2,0 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more