AKROMID®
S3 GF 30 4 black (3429)
PA610 GF30
AKROMID® S3 GF 30 4 black (3429) is a 30% glass fibre reinforced and hydrolysis stabilised polyamide 6.10 with high stiffness and strength as well as lower moisture absorption and very high chemical resistance.
8.600MPa
160MPa
110kJ/m²
AKROMID® S3 GF 30 4 black (3429) is a 30% glass fibre reinforced and hydrolysis stabilised polyamide 6.10 with high stiffness and strength as well as lower moisture absorption and very high chemical resistance.
AKROTEK®
PK-VM GF 40 8 black (6995)
PK GF40
AKROTEK® PK-VM GF 40 8 black (6995) - Polyketon, 40% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA
11.000MPa
150MPa
50kJ/m²
AKROTEK® PK-VM GF 40 8 black (6995) - Polyketon, 40% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA
AKROMID®
NEXT U3 ICF 20 1 black (8232)
PA11 CF20
AKROMID® NEXT U3 ICF 20 1 black (8232) - PA11 made of renewable raw materials, recycled carbon fibre, low density, Fused Filament Fabrication
9.300MPa
110MPa
60kJ/m²
AKROMID® NEXT U3 ICF 20 1 black (8232) - PA11 made of renewable raw materials, recycled carbon fibre, low density, Fused Filament Fabrication
PRECITE®
P3 GF 25 9 FR natural (8212)
PBT GF25 FR(40)
PRECITE® P3 GF 25 9 FR natural (8212) - PBT, 25% glass fiber, flame retardant, high stiffness and strength, good long-term heat-aging, E-Mobility, E&E industry.
8.500MPa
123MPa
53kJ/m²
PRECITE® P3 GF 25 9 FR natural (8212) - PBT, 25% glass fiber, flame retardant, high stiffness and strength, good long-term heat-aging, E-Mobility, E&E industry.
AKROMID®
B3 GF 30 1 HU LA black (2862)
PA6 GF30
AKROMID® B3 GF 30 1 HU LA black (2862) - PA 6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB, laser markable, automotive, E&E, industry.
10.300MPa
185MPa
95kJ/m²
AKROMID® B3 GF 30 1 HU LA black (2862) - PA 6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB, laser markable, automotive, E&E, industry.
AKROTEK®
PPS GF 40 black (8609)
PPS GF40
AKROTEK® PPS GF 40 black (8609) is a 40% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.
16.000MPa
180MPa
50kJ/m²
AKROTEK® PPS GF 40 black (8609) is a 40% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.
AKROTEK®
PK-VM GF 60 natural (8684)
PK GF60
AKROTEK® PK-VM GF 60 natural (8684) - Polyketon, 60% glass fibre reinforced, chemical and hydrolysis resistance
17.500MPa
180MPa
70kJ/m²
AKROTEK® PK-VM GF 60 natural (8684) - Polyketon, 60% glass fibre reinforced, chemical and hydrolysis resistance
AKROMID®
NEXT B3 GF 30 1 L CI black (8375)PA6 + PP GF30
AKROMID® NEXT B3 GF 30 1 L CI schwarz (8375) is a PA6/PP-blend with reduced density compared to standard PA6 GF 30. With 30% glass fibre reinforcement, the material is suitable for components with high strength and stiffness where weight reduction are required. The chemical resistance is particularly superior to calcium chloride (CaCl₂). The material is certified according to ISCC PLUS. 34% of the fossil raw materials required for manufacturing this product were replaced by sustainable biomass-balanced PP (≙ allocation factor).
Features
Regulatory
Properties
8.800MPa
140MPa
70kJ/m²
Sustainability
Allocation factor
only valid for ISCC PLUS/REDcert² certified products
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Flexural strain at break
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Ball indentation hardness
ISO 2039-1
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/B
ISO 75
Melting temperature
ISO 11357-3
Coefficient of linear thermal expansion
ISO 11359-1/2
Flammability
Burning rate
UL 94
GWFI
IEC 60695-2-12
GWIT
IEC 60695-2-13
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Electrical Properties
Comparative tracking index
IEC 60112
Rheological Properties
MVR
ISO 1133
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.