AKROMID®

Preliminary

B3 GF 30 5 black (8536)

PA6 GF30

AKROMID® B3 GF 30 5 black (8536) - PA6, 30% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.

Modulus

9.500MPa

Strength

170MPa

Impact

60kJ/m²

AKROMID® B3 GF 30 5 black (8536) - PA6, 30% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.

AKROMID®

UL

C3 GF 30 1 FR orange (7855)

PA6+PA66 GF30 FR(40)

AKROMID® C3 GF 30 1 FR orange (7855) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, RAL 2003, E&E, Public transportation EN 45545-2.

Modulus

10.600MPa

Strength

135MPa

Impact

65kJ/m²

AKROMID® C3 GF 30 1 FR orange (7855) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, RAL 2003, E&E, Public transportation EN 45545-2.

AKROTEK®

Preliminary

PPS GF 40 natural (8064)

PPS GF40

AKROTEK® PPS GF 40 natural (8064) is a 40% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

Modulus

12.000MPa

Strength

190MPa

Impact

50kJ/m²

AKROTEK® PPS GF 40 natural (8064) is a 40% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

AKROMID®

B28 GF 30 S3 black (8438)

PA6-I GF30

AKROMID® B28 GF 30 S3 black (8438) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

Modulus

9.000MPa

Strength

155MPa

Impact

100kJ/m²

AKROMID® B28 GF 30 S3 black (8438) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

AKROTEK®

Preliminary

PPS GF 40 black (8609)

PPS GF40

AKROTEK® PPS GF 40 black (8609) is a 40% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

Modulus

16.000MPa

Strength

180MPa

Impact

50kJ/m²

AKROTEK® PPS GF 40 black (8609) is a 40% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

AKROMID®

B3 GF 30 1 grey (7574)

PA6 GF30

AKROMID® B3 GF 30 1 grey (7574) is a 30% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength

Modulus

9.900MPa

Strength

168MPa

Impact

NA

AKROMID® B3 GF 30 1 grey (7574) is a 30% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength

AKROTEK®

Preliminary

PK-VM GF 60 natural (8684)

PK GF60

AKROTEK® PK-VM GF 60 natural (8684) - Polyketon, 60% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

17.500MPa

Strength

180MPa

Impact

70kJ/m²

AKROTEK® PK-VM GF 60 natural (8684) - Polyketon, 60% glass fibre reinforced, chemical and hydrolysis resistance

174757680

AKROMID®

UL

B3 1 black (6528)PA6

AKROMID® B3 1 black (6528) is an unreinforced, heat stabilised polyamide 6

Features

heat stabilised 130

Regulatory

ul

Properties

Modulus

3.600MPa

Strength

85MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
3600 MPa
1200 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
85 MPa
45 MPa

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
20 %
> 50 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
3100 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
120 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
no break
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
5 kJ/m²
16 kJ/m²
2 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
60 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
180 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
100 - 140 °C
90 - 120 °C

Flammability

Burning rate

UL 94

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
HB Class
HB Class
V-2 Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
750 °C

GWIT

IEC 60695-2-13

1,6 mm Wall thickness
675 °C

HWI

UL 746A

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
4 PLC
3 PLC
3 PLC

HAI

UL 746A

UL
0,8 mm Wall thickness
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
1 PLC
1 PLC
0 PLC

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,13 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,6 - 3,4 %

Molding shrinkage

ISO 294-4

flow
transverse
1,0 - 1,2 %
1,1 - 1,3 %

Electrical Properties

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
1012 Ω
1010 Ω

Comparative tracking index

IEC 60112

UL
Test liquid A
600 V

Comparative tracking index

ASTM D3638

UL
0 PLC

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more