AKROLOY® PA GF 60 black (7789) is a 60% glass fibre reinforced, easyflow, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

Modulus

21.400MPa

Strength

290MPa

Impact

100kJ/m²

AKROLOY® PA GF 60 black (7789) is a 60% glass fibre reinforced, easyflow, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

AKROMID^®

Preliminary

B3 GF 30 1 HU LA black (2862)

PA6 GF30

AKROMID® B3 GF 30 1 HU LA black (2862) - PA 6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB, laser markable, automotive, E&E, industry.

Modulus

10.300MPa

Strength

185MPa

Impact

95kJ/m²

AKROMID® B3 GF 30 1 HU LA black (2862) - PA 6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB, laser markable, automotive, E&E, industry.

AKROTEK^®

PK-VM GF 10 grey (7344)

PK GF10

AKROTEK® PK-VM GF 10 grey (7344) - Polyketon, 10% glass fiber reinforced, chemical resistance, RAL 7044

Modulus

3.600MPa

Strength

65MPa

Impact

50kJ/m²

AKROTEK® PK-VM GF 10 grey (7344) - Polyketon, 10% glass fiber reinforced, chemical resistance, RAL 7044

AKROMID^®

Preliminary

NEXT 5.6 3 GF 30 S3 black (8444)

PA56 GF30

AKROMID® NEXT 5.6 3 GF 30 S3 black (8444) - partly bio-based and HMD-free PA 5.6, 30 % GF, impact modified, high strength and stiffness.

Modulus

8.600MPa

Strength

180MPa

Impact

96kJ/m²

AKROMID® NEXT 5.6 3 GF 30 S3 black (8444) - partly bio-based and HMD-free PA 5.6, 30 % GF, impact modified, high strength and stiffness.

AKROMID^®

Preliminary

B3 GF 50 black (8524)

PA6 GF50

AKROMID® B3 GF 50 black (8524) is a 50% glass fibre reinforced, heat stabilised, easy flowing polyamide 6 with very high stiffness and strength.

Modulus

15.500MPa

Strength

230MPa

Impact

100kJ/m²

AKROMID® B3 GF 50 black (8524) is a 50% glass fibre reinforced, heat stabilised, easy flowing polyamide 6 with very high stiffness and strength.

1 74 75 7680

AKROMID^®

Internal

B3 GF 15 S1 black (3228)PA6-I GF15

AKROMID® B3 GF 15 S1 black (3228) is a 15% glass fiber reinforced, impact modified Polyamide 6. It is characterised by medium stiffness and strength as well as a higher impact strength compared to a standard PA 6 GF 15. It also has good surface properties. The material is therefore perfectly suitable for toughness demanding but high integrated parts with a good surface appearance in the automotive, electro, and furniture industry.

Features

impact modified

Properties

Modulus

5.500MPa

Strength

110MPa

Impact

70kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.

1 mm/min | conditioned

5500 MPa

3100 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.

5 mm/min | conditioned

110 MPa

75 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.

5 mm/min | conditioned

4 %

10 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.

5300 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.

175 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.

5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.

23°C | conditioned

30°C | d.a.m.

30°C | conditioned

70 kJ/m²

95 kJ/m²

50 kJ/m²

45 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.

23°C | conditioned

30°C | d.a.m.

30°C | conditioned

6 kJ/m²

14 kJ/m²

6 kJ/m²

5 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa

200 °C

Melting temperature

ISO 11357-3

DSC, 10K/min

222 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel

23°C to 80°C | transverse

0,3 10⁻⁴/K

1,3 10⁻⁴/K

Flammability

Burning rate

UL 94

1,6 mm Wall thickness

HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness

General properties

Density

ISO 1183

23°C

1,22 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.

2,3 %

Molding shrinkage

ISO 294-4

flow

transverse

0,2 - 0,4 %

0,6 - 0,8 %

Rheological Properties

MVR

ISO 1133

275°C/5kg

45 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Find the right compound

B3 GF 15 S1 black (3228)PA6-I GF15

Mechanical Properties

Tensile modulus

Tensile stress at break

Tensile strain at break

Flexural modulus

Flexural strength

Flexural strain at break

Charpy impact strength

Charpy notched impact strength

Thermal Properties

Temperature of deflection under load HDT/A

Melting temperature

Coefficient of linear thermal expansion

Flammability

Burning rate

Burning rate (<100 mm/min)

General properties

Density

Humidity absorption

Molding shrinkage

Rheological Properties

MVR

Do you have any questions? We are happy to help.

Find the right compound

B3 GF 15 S1 black (3228).css-117ixes{line-height:1.5;display:block;margin-top:var(--chakra-space-2);font-weight:var(--chakra-fontWeights-normal);font-size:var(--chakra-fontSizes-sm);color:var(--chakra-colors-kisPrimaryTextLight-700);}PA6-I GF15

Mechanical Properties

Tensile modulus

Tensile stress at break

Tensile strain at break

Flexural modulus

Flexural strength

Flexural strain at break

Charpy impact strength

Charpy notched impact strength

Thermal Properties

Temperature of deflection under load HDT/A

Melting temperature

Coefficient of linear thermal expansion

Flammability

Burning rate

Burning rate (<100 mm/min)

General properties

Density

Humidity absorption

Molding shrinkage

Rheological Properties

MVR

Do you have any questions? We are happy to help.

B3 GF 15 S1 black (3228)PA6-I GF15