AKROLEN®

Preliminary

PP ICF 30 AM black (8344)

PP CF30

AKROLEN® PP ICF 30 AM black (8344) - recycled carbon fibre reinforced polypropylene for additive manufacturing (3D-printing)

Modulus

12.500MPa

Strength

85MPa

Impact

50kJ/m²

AKROLEN® PP ICF 30 AM black (8344) - recycled carbon fibre reinforced polypropylene for additive manufacturing (3D-printing)

AKROMID®

S3 1 black (3317)

PA610

AKROMID® S3 1 black (3317) is a nonreinforced and heat stabilised polyamide 6.10 with lower moisture absorption and high chemical resistance.

Modulus

2.400MPa

Strength

70MPa

Impact

180kJ/m²

AKROMID® S3 1 black (3317) is a nonreinforced and heat stabilised polyamide 6.10 with lower moisture absorption and high chemical resistance.

AKROTEK®

PK-HM 8 natural (6145)

PK

AKROTEK® PK-HM 8 natural (6145) - Polyketon, unreinforced, Tribology, friction and wear, chemical resistance, EU 10/2011, FDA 21 CFR

Modulus

1.400MPa

Strength

60MPa

Impact

180kJ/m²

AKROTEK® PK-HM 8 natural (6145) - Polyketon, unreinforced, Tribology, friction and wear, chemical resistance, EU 10/2011, FDA 21 CFR

AKROMID®

Preliminary

T5 8 black (6454)

PPA

AKROMID® T5 8 black (6454) - PPA, unreinforced, food contact, kitchen and household appliances, fitting, ACS, WRAS, NSF 61, EU 10/2011, FDA

Modulus

3.800MPa

Strength

75MPa

Impact

40kJ/m²

AKROMID® T5 8 black (6454) - PPA, unreinforced, food contact, kitchen and household appliances, fitting, ACS, WRAS, NSF 61, EU 10/2011, FDA

AKROTEK®

Preliminary

PK-VM GF 15 8 black (6991)

PK GF15

AKROTEK® PK-VM GF 15 8 black (6991) - Polyketon, 15% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

Modulus

4.500MPa

Strength

95MPa

Impact

55kJ/m²

AKROTEK® PK-VM GF 15 8 black (6991) - Polyketon, 15% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

AKROMID®

B3 GF 35 S1 natural (920)

PA6-I GF35

AKROMID® B3 GF 35 S1 natural (920) is a 35% glass fibre reinforced, cold impact strength polyamide 6 with high stiffness and strength and light inherent color

Modulus

11.000MPa

Strength

190MPa

Impact

80kJ/m²

AKROMID® B3 GF 35 S1 natural (920) is a 35% glass fibre reinforced, cold impact strength polyamide 6 with high stiffness and strength and light inherent color

AKROTEK®

PK-VM GF 10 grey (7344)

PK GF10

AKROTEK® PK-VM GF 10 grey (7344) - Polyketon, 10% glass fiber reinforced, chemical resistance, RAL 7044

Modulus

3.600MPa

Strength

65MPa

Impact

50kJ/m²

AKROTEK® PK-VM GF 10 grey (7344) - Polyketon, 10% glass fiber reinforced, chemical resistance, RAL 7044

173747580

AKROMID®

UL

B3 1 black (6528)PA6

AKROMID® B3 1 black (6528) is an unreinforced, heat stabilised polyamide 6

Features

heat stabilised 130

Regulatory

ul

Properties

Modulus

3.600MPa

Strength

85MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
3600 MPa
1200 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
85 MPa
45 MPa

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
20 %
> 50 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
3100 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
120 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
no break
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
5 kJ/m²
16 kJ/m²
2 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
60 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
180 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
100 - 140 °C
90 - 120 °C

Flammability

Burning rate

UL 94

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
HB Class
HB Class
V-2 Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
750 °C

GWIT

IEC 60695-2-13

1,6 mm Wall thickness
675 °C

HWI

UL 746A

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
4 PLC
3 PLC
3 PLC

HAI

UL 746A

UL
0,8 mm Wall thickness
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
1 PLC
1 PLC
0 PLC

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,13 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,6 - 3,4 %

Molding shrinkage

ISO 294-4

flow
transverse
1,0 - 1,2 %
1,1 - 1,3 %

Electrical Properties

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
1012 Ω
1010 Ω

Comparative tracking index

IEC 60112

UL
Test liquid A
600 V

Comparative tracking index

ASTM D3638

UL
0 PLC

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more