AKROMID®

Preliminary

B28 GF 15 natural (6940)

PA6 GF 15

AKROMID B28 GF 15 natural (6940) - PA 6, glass fiber reinforced, easy flow, good surface, bus fire standard ECE R 118.03, medium stiffness and strength.

Modulus

5.300MPa

Strength

120MPa

Impact

39kJ/m²

AKROMID B28 GF 15 natural (6940) - PA 6, glass fiber reinforced, easy flow, good surface, bus fire standard ECE R 118.03, medium stiffness and strength.

AKROMID®

Preliminary

B3 GF 30 5 black (8536)

PA6 GF30

AKROMID® B3 GF 30 5 black (8536) - PA6, 30% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.

Modulus

9.500MPa

Strength

170MPa

Impact

60kJ/m²

AKROMID® B3 GF 30 5 black (8536) - PA6, 30% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.

AKROMID®

B3 GF 40 1 black (20016)

PA6 GF40

AKROMID® B3 GF 40 1 black (20016) is a 40% glass fibre reinforced, heat stabilised polyamide 6 with very high stiffness and strength

Modulus

12.500MPa

Strength

195MPa

Impact

95kJ/m²

AKROMID® B3 GF 40 1 black (20016) is a 40% glass fibre reinforced, heat stabilised polyamide 6 with very high stiffness and strength

AKROTEK®

PK-VM GF 10 grey (7344)

PK GF10

AKROTEK® PK-VM GF 10 grey (7344) - Polyketon, 10% glass fiber reinforced, chemical resistance, RAL 7044

Modulus

3.600MPa

Strength

65MPa

Impact

50kJ/m²

AKROTEK® PK-VM GF 10 grey (7344) - Polyketon, 10% glass fiber reinforced, chemical resistance, RAL 7044

AKROTEK®

Preliminary

PPS GF 40 natural (8064)

PPS GF40

AKROTEK® PPS GF 40 natural (8064) is a 40% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

Modulus

12.000MPa

Strength

190MPa

Impact

50kJ/m²

AKROTEK® PPS GF 40 natural (8064) is a 40% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

AKROTEK®

Preliminary

PPS CF 30 black (8612)

PPS CF30

AKROTEK® PPS CF 30 black (8612) is a 30% carbon fibre reinforced, Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

Modulus

28.000MPa

Strength

230MPa

Impact

35kJ/m²

AKROTEK® PPS CF 30 black (8612) is a 30% carbon fibre reinforced, Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

AKROTEK®

Preliminary

PK-VM GF 40 natural (8682)

PK GF40

AKROTEK® PK-VM GF 40 natural (8682) - Polyketon, 40% glass fibre reinforced, chemical restistant

Modulus

11.000MPa

Strength

165MPa

Impact

78kJ/m²

AKROTEK® PK-VM GF 40 natural (8682) - Polyketon, 40% glass fibre reinforced, chemical restistant

173747580

AKROLOY®

Preliminary

PA GF 30 black (6415)PA66+PA6I/6T GF30

AKROLOY® PA GF 30 black (6415) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.

Properties

Modulus

9.800MPa

Strength

200MPa

Impact

65kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
9800 MPa
9000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
200 MPa
135 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,8 %
2,8 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
9500 MPa
9500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
280 MPa
230 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
3,4 %
3,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
65 kJ/m²
65 kJ/m²
60 kJ/m²
60 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
11 kJ/m²
11 kJ/m²
10 kJ/m²
10 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
235 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
120 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
255 °C

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
150 °C
115 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,36 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,9 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Rheological Properties

Flowability

AKRO

1 mm Thickness
2 mm Thickness
160 mm
500 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.