AKROMIDĀ®

Preliminary

B28 GF 15 natural (6940)

PA6 GF 15

AKROMID B28 GF 15 natural (6940) - PA 6, glass fiber reinforced, easy flow, good surface, bus fire standard ECE R 118.03, medium stiffness and strength.

Modulus

5.300MPa

Strength

120MPa

Impact

39kJ/mĀ²

AKROMID B28 GF 15 natural (6940) - PA 6, glass fiber reinforced, easy flow, good surface, bus fire standard ECE R 118.03, medium stiffness and strength.

AKROMIDĀ®

Preliminary

B3 GF 30 5 black (8536)

PA6 GF30

AKROMIDĀ® B3 GF 30 5 black (8536) - PA6, 30% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.

Modulus

9.500MPa

Strength

170MPa

Impact

60kJ/mĀ²

AKROMIDĀ® B3 GF 30 5 black (8536) - PA6, 30% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.

AKROMIDĀ®

B3 GF 40 1 black (20016)

PA6 GF40

AKROMIDĀ® B3 GF 40 1 black (20016) is a 40% glass fibre reinforced, heat stabilised polyamide 6 with very high stiffness and strength

Modulus

12.500MPa

Strength

195MPa

Impact

95kJ/mĀ²

AKROMIDĀ® B3 GF 40 1 black (20016) is a 40% glass fibre reinforced, heat stabilised polyamide 6 with very high stiffness and strength

AKROTEKĀ®

PK-VM GF 10 grey (7344)

PK GF10

AKROTEKĀ® PK-VM GF 10 grey (7344) - Polyketon, 10% glass fiber reinforced, chemical resistance, RAL 7044

Modulus

3.600MPa

Strength

65MPa

Impact

50kJ/mĀ²

AKROTEKĀ® PK-VM GF 10 grey (7344) - Polyketon, 10% glass fiber reinforced, chemical resistance, RAL 7044

AKROTEKĀ®

Preliminary

PPS GF 40 natural (8064)

PPS GF40

AKROTEKĀ® PPS GF 40 natural (8064) is a 40% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

Modulus

12.000MPa

Strength

190MPa

Impact

50kJ/mĀ²

AKROTEKĀ® PPS GF 40 natural (8064) is a 40% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

AKROTEKĀ®

Preliminary

PPS CF 30 black (8612)

PPS CF30

AKROTEKĀ® PPS CF 30 black (8612) is a 30% carbon fibre reinforced, Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

Modulus

28.000MPa

Strength

230MPa

Impact

35kJ/mĀ²

AKROTEKĀ® PPS CF 30 black (8612) is a 30% carbon fibre reinforced, Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

AKROTEKĀ®

Preliminary

PK-VM GF 40 natural (8682)

PK GF40

AKROTEKĀ® PK-VM GF 40 natural (8682) - Polyketon, 40% glass fibre reinforced, chemical restistant

Modulus

11.000MPa

Strength

165MPa

Impact

78kJ/mĀ²

AKROTEKĀ® PK-VM GF 40 natural (8682) - Polyketon, 40% glass fibre reinforced, chemical restistant

173747580

AKROMIDĀ®

B3 GF 30 1 L natural (4684)PA6+PP GF30

AKROMIDĀ® B3 GF 30 1 L natural (4684) is a PA6/PP-blend with reduced density compared to standard PA6 with 30% glass fibre reinforcement. The material is suitable for components with high strength and stiffness where cost and weight reduction are required at the same time. The chemical resistance of AKROMIDĀ® B3 GF 30 1 L natural (4684) is particularly superior to calcium chloride (CaClā‚‚).

Features

heat stabilised 130
reduced density

Properties

Modulus

8.500MPa

Strength

150MPa

Impact

70kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
8500 MPa
6500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
150 MPa
100 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,2 %
3,7 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
8800 MPa
6500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
210 MPa
150 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
3 %
3,9 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
70 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
17 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
203 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 Ā°C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,26 g/cmĀ³

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Rheological Properties

MVR

ISO 1133

275Ā°C/5kg
14 cmĀ³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more