AKROLOY®

PA GF 50 white (5137)

PA66+PA6I/6T GF50

AKROLOY® PA GF 50 white (5137) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

Modulus

20.000MPa

Strength

250MPa

Impact

105kJ/m²

AKROLOY® PA GF 50 white (5137) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

AKROMID®

A3 1 L natural (4800)

PA66 + PP

AKROMID® A3 1 L natural (4800) - unreinforced PA6.6/PP-Blend lightweight, cost reduced

Modulus

2.300MPa

Strength

55MPa

Impact

180kJ/m²

AKROMID® A3 1 L natural (4800) - unreinforced PA6.6/PP-Blend lightweight, cost reduced

AKROTEK®

PK-HM 8 natural (6145)

PK

AKROTEK® PK-HM 8 natural (6145) - Polyketon, unreinforced, Tribology, friction and wear, chemical resistance, EU 10/2011, FDA 21 CFR

Modulus

1.400MPa

Strength

60MPa

Impact

180kJ/m²

AKROTEK® PK-HM 8 natural (6145) - Polyketon, unreinforced, Tribology, friction and wear, chemical resistance, EU 10/2011, FDA 21 CFR

AKROMID®

Preliminary

T5 8 black (6454)

PPA

AKROMID® T5 8 black (6454) - PPA, unreinforced, food contact, kitchen and household appliances, fitting, ACS, WRAS, NSF 61, EU 10/2011, FDA

Modulus

3.800MPa

Strength

75MPa

Impact

40kJ/m²

AKROMID® T5 8 black (6454) - PPA, unreinforced, food contact, kitchen and household appliances, fitting, ACS, WRAS, NSF 61, EU 10/2011, FDA

AKROTEK®

PK-VM 8 black (6466)

PK

AKROTEK® PK-VM 8 black (6466) - Polyketon, Tribology, friction and wear, chemical resistance, food, drinking water, EU 10/2011

Modulus

1.600MPa

Strength

60MPa

Impact

180kJ/m²

AKROTEK® PK-VM 8 black (6466) - Polyketon, Tribology, friction and wear, chemical resistance, food, drinking water, EU 10/2011

PRECITE®

Preliminary

P3 GF 40 natural (6943)

PBT GF 40

PRECITE® P3 GF 40 natural (6943) is a 40% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

Modulus

13.500MPa

Strength

175MPa

Impact

70kJ/m²

PRECITE® P3 GF 40 natural (6943) is a 40% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

AKROMID®

UL
Preliminary

B3 GF 30 1 HU LA black (2862)

PA6 GF30

AKROMID® B3 GF 30 1 HU LA black (2862) - PA 6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB, laser markable, automotive, E&E, industry.

Modulus

10.300MPa

Strength

185MPa

Impact

95kJ/m²

AKROMID® B3 GF 30 1 HU LA black (2862) - PA 6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB, laser markable, automotive, E&E, industry.

173747580

AKROMID®

B3 GF 50 S1 natural (3694)PA6-I GF50

AKROMID® B3 GF 50 S1 natural (3694) is a 50% glass fiber reinforced, impact modified Polyamide 6. It is characterised by very high stiffness and strength as well as a higher notched impact strength compared to a standard PA 6 GF 50. The material is therefore perfectly suitable for industrial applications and for housings and covers in the automotive industry. The material has a light inherent color.

Features

impact modified

Properties

Modulus

14.500MPa

Strength

190MPa

Impact

110kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
14500 MPa
7800 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
190 MPa
120 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
5 %
8 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
110 kJ/m²
> 110 kJ/m²
100 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30 kJ/m²
40 kJ/m²
20 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
210 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
225 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
222 °C

Temperature index for 50% loss of tensile strength

IEC 60216

20.000 h
115 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,54 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,3 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,4 - 0,6 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.