AKROMIDĀ®

A3 GFM 25/15 1 black (3335)

PA66 (GF25+MD15)

AKROMIDĀ® A3 GFM 25/15 1 black (3335) is a 25% glass fibre reinforced, 15% mineral filled, heat stabilised polyamide 6.6 with good surface and dimensional stability

Modulus

10.000MPa

Strength

150MPa

Impact

50kJ/mĀ²

AKROMIDĀ® A3 GFM 25/15 1 black (3335) is a 25% glass fibre reinforced, 15% mineral filled, heat stabilised polyamide 6.6 with good surface and dimensional stability

AKROTEKĀ®

Preliminary

PK-VM GF 15 8 natural (6324)

PK GF15

AKROTEKĀ® PK-VM GF 15 8 natural (6324) - Polyketon, 15% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

Modulus

4.500MPa

Strength

95MPa

Impact

55kJ/mĀ²

AKROTEKĀ® PK-VM GF 15 8 natural (6324) - Polyketon, 15% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

AKROMIDĀ®

A3 GF 50 4 black (7282)

PA66 GF50

AKROMIDĀ® A3 GF 50 4 black (7282) is a 50% glass fibre reinforced, hydrolysis/chemical stabilised polyamide 6.6 with very high rigidity and strength

Modulus

17.000MPa

Strength

250MPa

Impact

110kJ/mĀ²

AKROMIDĀ® A3 GF 50 4 black (7282) is a 50% glass fibre reinforced, hydrolysis/chemical stabilised polyamide 6.6 with very high rigidity and strength

AKROMIDĀ®

B3 GF 40 1 black (20016)

PA6 GF40

AKROMIDĀ® B3 GF 40 1 black (20016) is a 40% glass fibre reinforced, heat stabilised polyamide 6 with very high stiffness and strength

Modulus

12.500MPa

Strength

195MPa

Impact

95kJ/mĀ²

AKROMIDĀ® B3 GF 40 1 black (20016) is a 40% glass fibre reinforced, heat stabilised polyamide 6 with very high stiffness and strength

AKROMIDĀ®

Preliminary

A3 black (7557)

PA66

AKROMIDĀ® A3 black (7557) is an unreinforced, UV stabilised polyamide 6.6.

Modulus

3.200MPa

Strength

80MPa

Impact

180kJ/mĀ²

AKROMIDĀ® A3 black (7557) is an unreinforced, UV stabilised polyamide 6.6.

AKROMIDĀ®

Preliminary

B3 1 S3 natural (8013)

PA6-I

AKROMIDĀ® B3 1 S3 natural (8013) - PA 6 unreinforced, impact modified, connecting and fixing systems.

Modulus

2.200MPa

Strength

55MPa

Impact

180kJ/mĀ²

AKROMIDĀ® B3 1 S3 natural (8013) - PA 6 unreinforced, impact modified, connecting and fixing systems.

PRECITEĀ®

Preliminary

P3 GF 25 9 FR natural (8212)

PBT GF25 FR(40)

PRECITEĀ® P3 GF 25 9 FR natural (8212) - PBT, 25% glass fiber, flame retardant, high stiffness and strength, good long-term heat-aging, E-Mobility, E&E industry.

Modulus

8.500MPa

Strength

123MPa

Impact

53kJ/mĀ²

PRECITEĀ® P3 GF 25 9 FR natural (8212) - PBT, 25% glass fiber, flame retardant, high stiffness and strength, good long-term heat-aging, E-Mobility, E&E industry.

173747580

AKROMIDĀ®

B3 GF 30 6 black (20009)PA6 GF30

AKROMIDĀ® B3 GF 30 6 black (20009) is a 30% glass fiber reinforced polyamide 6. It is characterised by a high stiffness and strength. Furthermore, the material is inorganically high heat stabilised and therefore perfectly suitable for technical parts in industrial engineering and in the automotive industry.

Features

heat stabilised 160

Properties

Modulus

10.000MPa

Strength

180MPa

Impact

80kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
10000 MPa
6500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
180 MPa
105 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
8000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
250 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
80 kJ/mĀ²
90 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
13 kJ/mĀ²
18 kJ/mĀ²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
230 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
210 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,36 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
2,1 - 2,3 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
conditioned
1013 ā„¦ x cm
1010 ā„¦ x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
1012 ā„¦
1010 ā„¦

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more