AKROMID®

A3 GK 30 6 black (6670)

PA66 GK30

AKROMID® A3 GK 30 6 black (6670) - 30% glass bead, inorganic high temperature stabilised, polyamide 6.6, low warpage, high surface appearance

Modulus

4.600MPa

Strength

86MPa

Impact

20kJ/m²

AKROMID® A3 GK 30 6 black (6670) - 30% glass bead, inorganic high temperature stabilised, polyamide 6.6, low warpage, high surface appearance

AKROMID®

A3 GK 30 6 natural (6774)

PA66 GB30

AKROMID® A3 GK 30 6 natural (6774) - 30% glass bead, inorganic high temperature stabilised, polyamide 6.6, low warpage, high surface appearance

Modulus

4.600MPa

Strength

90MPa

Impact

25kJ/m²

AKROMID® A3 GK 30 6 natural (6774) - 30% glass bead, inorganic high temperature stabilised, polyamide 6.6, low warpage, high surface appearance

AKROTEK®

Preliminary

PPS GF 40 natural (8064)

PPS GF40

AKROTEK® PPS GF 40 natural (8064) is a 40% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

Modulus

12.000MPa

Strength

190MPa

Impact

50kJ/m²

AKROTEK® PPS GF 40 natural (8064) is a 40% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

AKROMID®

A3 GF 25 3 black (3094)

PA66 GF25

AKROMID® A3 GF 25 3 black (3094) is a 25% glass fibre reinforced, nucleated polyamide 6.6 with high stiffness and strength

Modulus

8.500MPa

Strength

160MPa

Impact

50kJ/m²

AKROMID® A3 GF 25 3 black (3094) is a 25% glass fibre reinforced, nucleated polyamide 6.6 with high stiffness and strength

AKROMID®

A3 GF 40 1 L black (4671)

PA66+PP GF40

AKROMID® A3 GF 40 1 L black (4671) - PA6.6/PP-Blend, 40% glass fibre reinforced, lower density, cost reduced, zinc chloride

Modulus

11.800MPa

Strength

170MPa

Impact

80kJ/m²

AKROMID® A3 GF 40 1 L black (4671) - PA6.6/PP-Blend, 40% glass fibre reinforced, lower density, cost reduced, zinc chloride

AKROLOY®

Preliminary

PA GF 30 black (6415)

PA66+PA6I/6T GF30

AKROLOY® PA GF 30 black (6415) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.

Modulus

9.800MPa

Strength

200MPa

Impact

65kJ/m²

AKROLOY® PA GF 30 black (6415) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.

AKROTEK®

Preliminary

PK-VM GF 50 8 natural (6989)

PK GF50

AKROTEK® PK-VM GF 50 8 natural (6989) - Polyketon, 50% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

Modulus

14.000MPa

Strength

160MPa

Impact

60kJ/m²

AKROTEK® PK-VM GF 50 8 natural (6989) - Polyketon, 50% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

172737480

AKROMID®

UL

NEXT S3 GF 50 1 HU black (8827)PA6.10 GF50

AKROMID® NEXT S3 GF 50 1 black (8827) is a partially biobased and heat-stabilised PA6.10. With 50% glass fibre reinforcement, the material is suitable for household and industrial applications with high demands on strength and stiffness. This sustainable and UL listed grade is characterised by its low moisture absorption and high chemical resistance compared to classic PA6 and PA 6.6.

Features

Bio-based
heat stabilised 130
reduced moisture

Regulatory

ul

Properties

Modulus

14.500MPa

Strength

200MPa

Impact

100kJ/m²

Sustainability

Biobased carbon content

58 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
14500 MPa
11000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
200 MPa
150 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,5 %
4,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
13800 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
310 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
3,6 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
100 kJ/m²
100 kJ/m²
105 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
30°C | d.a.m.
-
20 kJ/m²
16 kJ/m²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
230 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
205 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
170 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

UL
0,8 mm Wall thickness
UL
3,2 mm Wall thickness
HB Class
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,51 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,8 - 1,0 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,6 - 0,8 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.