AKROLOY®
PA GF 60 LA black (8168)
PA66 + PA6I/6T GF60
AKROLOY® PA GF 60 LA black (8168) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.
21.400MPa
275MPa
95kJ/m²
AKROLOY® PA GF 60 LA black (8168) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.
AKROMID®
NEXT U3 ICF 20 1 black (8232)
PA11 CF20
AKROMID® NEXT U3 ICF 20 1 black (8232) - PA11 made of renewable raw materials, recycled carbon fibre, low density, Fused Filament Fabrication
9.300MPa
110MPa
60kJ/m²
AKROMID® NEXT U3 ICF 20 1 black (8232) - PA11 made of renewable raw materials, recycled carbon fibre, low density, Fused Filament Fabrication
AKROTEK®
AM ICF 20 black (8723)
ASACF20
AKROTEK® AM ICF 20 black (8723) - recycled carbon fibre reinforced for additive manufacturing (3D-printing)
13.400MPa
105MPa
25kJ/m²
AKROTEK® AM ICF 20 black (8723) - recycled carbon fibre reinforced for additive manufacturing (3D-printing)
AKROTEK®
AM ICF 20 black (8722)
ABSCF20
AKROTEK® AM ICF 20 black (8722) - recycled carbon fibre reinforced for additive manufacturing (3D-printing)
13.400MPa
100MPa
20kJ/m²
AKROTEK® AM ICF 20 black (8722) - recycled carbon fibre reinforced for additive manufacturing (3D-printing)
AKROMID®
A3 black (7557)
PA66
AKROMID® A3 black (7557) is an unreinforced, UV stabilised polyamide 6.6.
3.200MPa
80MPa
180kJ/m²
AKROMID® A3 black (7557) is an unreinforced, UV stabilised polyamide 6.6.
AKROMID®
B3 GF 30 1 HU LA black (2862)
PA6 GF30
AKROMID® B3 GF 30 1 HU LA black (2862) - PA 6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB, laser markable, automotive, E&E, industry.
10.300MPa
185MPa
95kJ/m²
AKROMID® B3 GF 30 1 HU LA black (2862) - PA 6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB, laser markable, automotive, E&E, industry.
AKROMID®
NEXT G3 GF 30 1 L CR black (8314)
PA6.9 + PP GF30
AKROMID® NEXT G3 GF 30 1 L CI black (8314) - PA 6.9/PP blend, bio-based, certified, low moisture absorption, weight reduction.
8.000MPa
125MPa
65kJ/m²
AKROMID® NEXT G3 GF 30 1 L CI black (8314) - PA 6.9/PP blend, bio-based, certified, low moisture absorption, weight reduction.
PRECITE®
P3 GF 40 natural (6943)PBT GF 40
PRECITE® P3 GF 40 natural (6943) is a 40% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.
Properties
13.500MPa
175MPa
70kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
GWFI
IEC 60695-2-12
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Water absorption
ISO 62
Molding shrinkage
ISO 294-4
Electrical Properties
Volume resistivity IEC
DIN EN IEC 62631-3-2
Surface resistivity
DIN EN 62631-3-2
Comparative tracking index
IEC 60112
Rheological Properties
MVR
ISO 1133
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.