PA GF 60 black (7789)

PA66+PA6I/6T GF60

AKROLOYĀ® PA GF 60 black (7789) is a 60% glass fibre reinforced, easyflow, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

Modulus

21.400MPa

Strength

290MPa

Impact

100kJ/mĀ²

AKROLOYĀ® PA GF 60 black (7789) is a 60% glass fibre reinforced, easyflow, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

AKROTEKĀ®

PK-VM GF 10 grey (7344)

PK GF10

AKROTEKĀ® PK-VM GF 10 grey (7344) - Polyketon, 10% glass fiber reinforced, chemical resistance, RAL 7044

Modulus

3.600MPa

Strength

65MPa

Impact

50kJ/mĀ²

AKROTEKĀ® PK-VM GF 10 grey (7344) - Polyketon, 10% glass fiber reinforced, chemical resistance, RAL 7044

AKROMIDĀ®

Preliminary

NEXT G3 GF 30 1 L CI natural (8377)

PA6.9 + PP GF30

AKROMIDĀ® NEXT G3 GF 30 1 L CI natural (8377) - PA 6.9/PP blend, bio-based, certified, low moisture absorption, weight reduction.

Modulus

8.000MPa

Strength

125MPa

Impact

65kJ/mĀ²

AKROMIDĀ® NEXT G3 GF 30 1 L CI natural (8377) - PA 6.9/PP blend, bio-based, certified, low moisture absorption, weight reduction.

AKROMIDĀ®

Preliminary

C3 GF 30 8 black (5657)

PA66 + PA6 GF30

AKROMIDĀ® C3 GF 30 8 black (5657) - PA6.6/6 Blend, GF 30, FDA, EU 10/2010, food contact, kitchen and household appliances

Modulus

9.400MPa

Strength

190MPa

Impact

82kJ/mĀ²

AKROMIDĀ® C3 GF 30 8 black (5657) - PA6.6/6 Blend, GF 30, FDA, EU 10/2010, food contact, kitchen and household appliances

AKROTEKĀ®

Preliminary

PK-VM GF 20 natural (8681)

PK GF20

AKROTEKĀ® PK-VM GF 20 natural (8681) - Polyketon, 20% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

5.700MPa

Strength

117MPa

Impact

65kJ/mĀ²

AKROTEKĀ® PK-VM GF 20 natural (8681) - Polyketon, 20% glass fibre reinforced, chemical and hydrolysis resistance

AKROMIDĀ®

B3 GF 35 S1 natural (920)

PA6-I GF35

AKROMIDĀ® B3 GF 35 S1 natural (920) is a 35% glass fibre reinforced, cold impact strength polyamide 6 with high stiffness and strength and light inherent color

Modulus

11.000MPa

Strength

190MPa

Impact

80kJ/mĀ²

AKROMIDĀ® B3 GF 35 S1 natural (920) is a 35% glass fibre reinforced, cold impact strength polyamide 6 with high stiffness and strength and light inherent color

AKROMIDĀ®

Preliminary

NEXT U3 ICF 20 1 black (8232)

PA11 CF20

AKROMIDĀ® NEXT U3 ICF 20 1 black (8232) - PA11 made of renewable raw materials, recycled carbon fibre, low density, Fused Filament Fabrication

Modulus

9.300MPa

Strength

110MPa

Impact

60kJ/mĀ²

AKROMIDĀ® NEXT U3 ICF 20 1 black (8232) - PA11 made of renewable raw materials, recycled carbon fibre, low density, Fused Filament Fabrication

172737480

AKROMIDĀ®

T5 GF 50 8 black (6205)PPA GF50

AKROMIDĀ® T5 GF 50 8 black (6205) is a 50% glass fibre reinforced polyphthalamide with very high rigidity and strength, as well as high temperature and chemical resistance. This aromatic PPA keeps mechanical performance even at elevated temperatures as well as moisture pic-up. The material fulfills the requirements according to ACS, WRAS and NSF 61. It is suitable for applications that are in contact with cold and hot drinking water. This material corresponds to the European food guideline EU 10/2011 and to the American FDA 21 CFR and is suitable for parts of kitchen and household appliances.

Regulatory

acseu102011fdansf-coldnsf-hotwras

Properties

Modulus

19.000MPa

Strength

270MPa

Impact

85kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
19000 MPa
19000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
270 MPa
270 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,1 %
2,1 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
18500 MPa
18500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
410 MPa
350 MPa

Standard bending strength RP 3,5

ISO 178

2mm/min | d.a.m.
2,5 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
30Ā°C | conditioned
-
85 kJ/mĀ²
85 kJ/mĀ²
75 kJ/mĀ²
75 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
13 kJ/mĀ²
13 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
280 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
325 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

General properties

Density

ISO 1183

23Ā°C
1,65 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
0,8 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,4 - 0,6 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more