HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
558 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

PRECITE®

Preliminary

P3 GF 25 9 FR natural (8212)

PBT GF25 FR(40)

PRECITE® P3 GF 25 9 FR natural (8212) - PBT, 25% glass fiber, flame retardant, high stiffness and strength, good long-term heat-aging, E-Mobility, E&E industry.

Modulus

8.500MPa

Strength

123MPa

Impact

53kJ/m²

PRECITE® P3 GF 25 9 FR natural (8212) - PBT, 25% glass fiber, flame retardant, high stiffness and strength, good long-term heat-aging, E-Mobility, E&E industry.

AKROMID®

A3 CF 20 black (3132)

PA66 CF20

AKROMID® A3 CF 20 black (3132) is a 20% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties

Modulus

15.000MPa

Strength

200MPa

Impact

40kJ/m²

AKROMID® A3 CF 20 black (3132) is a 20% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties

AKROMID®

A3 1 L natural (4800)

PA66 + PP

AKROMID® A3 1 L natural (4800) - unreinforced PA6.6/PP-Blend lightweight, cost reduced

Modulus

2.300MPa

Strength

55MPa

Impact

180kJ/m²

AKROMID® A3 1 L natural (4800) - unreinforced PA6.6/PP-Blend lightweight, cost reduced

AKROLOY®

Preliminary

PA GF 30 black (6415)

PA66+PA6I/6T GF30

AKROLOY® PA GF 30 black (6415) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.

Modulus

9.800MPa

Strength

200MPa

Impact

65kJ/m²

AKROLOY® PA GF 30 black (6415) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.

AKROMID®

UL

B3 1 black (6528)

PA6

AKROMID® B3 1 black (6528) is an unreinforced, heat stabilised polyamide 6

Modulus

3.600MPa

Strength

85MPa

Impact

180kJ/m²

AKROMID® B3 1 black (6528) is an unreinforced, heat stabilised polyamide 6

PRECITE®

Preliminary

P3 GF 40 natural (6943)

PBT GF 40

PRECITE® P3 GF 40 natural (6943) is a 40% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

Modulus

13.500MPa

Strength

175MPa

Impact

70kJ/m²

PRECITE® P3 GF 40 natural (6943) is a 40% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

AKROLOY®

PA GF 50 white (5137)

PA66+PA6I/6T GF50

AKROLOY® PA GF 50 white (5137) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

Modulus

20.000MPa

Strength

250MPa

Impact

105kJ/m²

AKROLOY® PA GF 50 white (5137) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

172737480

AKROMID®

A3 1 L natural (4800)PA66 + PP

AKROMID® A3 1 L natural (4800) is an unreinforced PA6.6/PP-blend with reduced density compared to standard PA6.6. The material can be used where weight and cost reduction is required.

Features

heat stabilised 130
reduced density

Properties

Modulus

2.300MPa

Strength

55MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
2300 MPa
1400 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
55 MPa
40 MPa

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
30 %
> 50 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2100 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
80 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
7 %

Standard bending strength RP 3,5

ISO 178

2mm/min | d.a.m.
65 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
7 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
65 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
150 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,04 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,7 %

Molding shrinkage

ISO 294-4

flow
transverse
1,3 - 1,5 %
1,5 - 1,7 %

Rheological Properties

MVR

ISO 1133

275°C/5kg
35 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more