AKROLOY®

PA GF 50 white (5137)

PA66+PA6I/6T GF50

AKROLOY® PA GF 50 white (5137) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

Modulus

20.000MPa

Strength

250MPa

Impact

105kJ/m²

AKROLOY® PA GF 50 white (5137) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

AKROMID®

Preliminary

B3 1 S3 natural (8013)

PA6-I

AKROMID® B3 1 S3 natural (8013) - PA 6 unreinforced, impact modified, connecting and fixing systems.

Modulus

2.200MPa

Strength

55MPa

Impact

180kJ/m²

AKROMID® B3 1 S3 natural (8013) - PA 6 unreinforced, impact modified, connecting and fixing systems.

AKROMID®

A3 GF 50 4 natural (71090)

PA66 GF50

AKROMID® A3 GF 50 4 natural (71090) - PA6.6, 50% glass fiber, cooling water, hydrolysis resistant, DPPD free

Modulus

18.000MPa

Strength

260MPa

Impact

110kJ/m²

AKROMID® A3 GF 50 4 natural (71090) - PA6.6, 50% glass fiber, cooling water, hydrolysis resistant, DPPD free

AKROMID®

A3 CF 20 black (3132)

PA66 CF20

AKROMID® A3 CF 20 black (3132) is a 20% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties

Modulus

15.000MPa

Strength

200MPa

Impact

40kJ/m²

AKROMID® A3 CF 20 black (3132) is a 20% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties

AKROTEK®

PK-VM ICF 15 black (6074)

PK CF15

AKROTEK® PK-VM ICF 15 black (6074) is a 15% carbon fibre reinforced polyketon with good sliding properties.

Modulus

9.000MPa

Strength

90MPa

Impact

30kJ/m²

AKROTEK® PK-VM ICF 15 black (6074) is a 15% carbon fibre reinforced polyketon with good sliding properties.

AKROLOY®

Preliminary

PA GF 30 black (6415)

PA66+PA6I/6T GF30

AKROLOY® PA GF 30 black (6415) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.

Modulus

9.800MPa

Strength

200MPa

Impact

65kJ/m²

AKROLOY® PA GF 30 black (6415) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.

PRECITE®

Preliminary

P3 GF 40 natural (6943)

PBT GF 40

PRECITE® P3 GF 40 natural (6943) is a 40% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

Modulus

13.500MPa

Strength

175MPa

Impact

70kJ/m²

PRECITE® P3 GF 40 natural (6943) is a 40% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

172737480

AKROMID®

UL

A3 1 FR black (3051)PA66 FR(30)

AKROMID® A3 1 FR black (3051) is an unreinforced, flame retardant and heat stabilised PA6.6. Listed to UL 94 in all-colours, the material is based on a flame retardant system that is free of red phosphorus and halogens. This grade is suitable for switches, housing and fasteners in the electric industry.

Features

heat stabilised 130
flame retardant
E&E

Regulatory

ul

Properties

Modulus

3.500MPa

Strength

83MPa

Impact

70kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
3500 MPa
1500 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
83 MPa
55 MPa

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
> 5 %
> 20 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
70
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
4,5 kJ/m²
7 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
80 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
260 °C

Flammability

Burning rate

UL 94

0,4 mm Wall thickness
UL
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
V-0 Class
V-0 Class
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
960 °C
960 °C
960 °C
960 °C

GWIT

IEC 60695-2-13

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
775 °C
750 °C
750 °C
775 °C

HWI

UL 746A

UL
0,8 mm Wall thickness
4 PLC

HAI

UL 746A

UL
0,8 mm Wall thickness
0 PLC

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

Oxygen index

ISO 4589-2

> 32 %

General properties

Density

ISO 1183

23°C
1,18 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
1,3 - 1,6 %
1,3 - 1,6 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
> 600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more