AKROMIDĀ®

Preliminary

B3 GF 30 8 black (8166)

PA6 GF30

AKROMIDĀ® B3 GF 30 8 black (8166) - PA6, 30% glass fiber, food contact, kitchen and household appliances

Modulus

10.000MPa

Strength

175MPa

Impact

95kJ/mĀ²

AKROMIDĀ® B3 GF 30 8 black (8166) - PA6, 30% glass fiber, food contact, kitchen and household appliances

AKROMIDĀ®

Preliminary

NEXT U28 ICF 40 1 black (8238)

PA11 CF40

AKROMIDĀ® NEXT U28 ICF 40 1 black (8238) - PA11 made of renewable raw materials, recycled carbon fibre, low density, 3D printing of large parts

Modulus

20.000MPa

Strength

190MPa

Impact

80kJ/mĀ²

AKROMIDĀ® NEXT U28 ICF 40 1 black (8238) - PA11 made of renewable raw materials, recycled carbon fibre, low density, 3D printing of large parts

AKROMIDĀ®

Preliminary

NEXT G3 GF 30 1 L CR black (8314)

PA6.9 + PP GF30

AKROMIDĀ® NEXT G3 GF 30 1 L CI black (8314) - PA 6.9/PP blend, bio-based, certified, low moisture absorption, weight reduction.

Modulus

8.000MPa

Strength

125MPa

Impact

65kJ/mĀ²

AKROMIDĀ® NEXT G3 GF 30 1 L CI black (8314) - PA 6.9/PP blend, bio-based, certified, low moisture absorption, weight reduction.

AKROMIDĀ®

Preliminary

NEXT 5.6 3 GF 30 S3 black (8444)

PA56 GF30

AKROMIDĀ® NEXT 5.6 3 GF 30 S3 black (8444) - partly bio-based and HMD-free PA 5.6, 30 % GF, impact modified, high strength and stiffness.

Modulus

8.600MPa

Strength

180MPa

Impact

96kJ/mĀ²

AKROMIDĀ® NEXT 5.6 3 GF 30 S3 black (8444) - partly bio-based and HMD-free PA 5.6, 30 % GF, impact modified, high strength and stiffness.

AKROMIDĀ®

Preliminary

T5 8 black (6454)

PPA

AKROMIDĀ® T5 8 black (6454) - PPA, unreinforced, food contact, kitchen and household appliances, fitting, ACS, WRAS, NSF 61, EU 10/2011, FDA

Modulus

3.800MPa

Strength

75MPa

Impact

40kJ/mĀ²

AKROMIDĀ® T5 8 black (6454) - PPA, unreinforced, food contact, kitchen and household appliances, fitting, ACS, WRAS, NSF 61, EU 10/2011, FDA

PRECITEĀ®

Preliminary

P3 GF 30 S1 natural (6853)

PBT-GF 30

PRECITEĀ® P3 GF 30 S1 natural (6853) is a 30% glass fibre reinforced, impact modified, medium viscous poly(butylene terephthalate) (PBT) with high stiffness and strength and lower density compared to neat PBT.

Modulus

9.500MPa

Strength

135MPa

Impact

85kJ/mĀ²

PRECITEĀ® P3 GF 30 S1 natural (6853) is a 30% glass fibre reinforced, impact modified, medium viscous poly(butylene terephthalate) (PBT) with high stiffness and strength and lower density compared to neat PBT.

PRECITEĀ®

Preliminary

E GF 20 natural (7301)

PET GF 20

PRECITEĀ® E GF 20 natural (7301) - PET, 20% glass fibre, good stiffness, good toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

7.800MPa

Strength

145MPa

Impact

40kJ/mĀ²

PRECITEĀ® E GF 20 natural (7301) - PET, 20% glass fibre, good stiffness, good toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

172737480

AKROMIDĀ®

A3 GF 30 S1 black (1365)PA66-I GF30

AKROMIDĀ® A3 GF 30 S1 black (1365) is a 30% glass fiber reinforced, impact modified Polyamide 6.6. It is characterised by high stiffness and strength as well as a higher impact strength compared to a standard PA 6.6 GF 30. The material is perfectly suitable for connecting and fixing systems as well as for precision parts in the automotive industry.

Features

impact modified

Properties

Modulus

9.600MPa

Strength

180MPa

Impact

105kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
9600 MPa
8000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
180 MPa
120 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
5 %
6 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
30Ā°C | conditioned
-
105 kJ/mĀ²
110 kJ/mĀ²
85 kJ/mĀ²
100 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
30Ā°C | conditioned
-
17 kJ/mĀ²
20 kJ/mĀ²
12 kJ/mĀ²
12 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
255 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,34 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,7 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,7 - 0,9 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more