AKROLOY^®

PA GF 40 natural (6413)

PA66+PA6I/6T GF40

AKROLOY® PA GF 40 natural (6413) is a 40% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

Modulus

13.000MPa

Strength

235MPa

Impact

95kJ/m²

AKROLOY® PA GF 40 natural (6413) is a 40% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

AKROMID^®

A3 GK 30 6 natural (6774)

PA66 GB30

AKROMID® A3 GK 30 6 natural (6774) - 30% glass bead, inorganic high temperature stabilised, polyamide 6.6, low warpage, high surface appearance

Modulus

4.600MPa

Strength

90MPa

Impact

25kJ/m²

AKROMID® A3 GK 30 6 natural (6774) - 30% glass bead, inorganic high temperature stabilised, polyamide 6.6, low warpage, high surface appearance

AKROTEK^®

PK-VM GF 30 8 natural (6983)

PK GF30

AKROTEK® PK-VM GF 30 8 natural (6983) - Polyketon, 30% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

Modulus

8.200MPa

Strength

130MPa

Impact

60kJ/m²

AKROTEK® PK-VM GF 30 8 natural (6983) - Polyketon, 30% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

PRECITE^®

Preliminary

P3 GF 40 natural (6943)

PBT GF 40

PRECITE® P3 GF 40 natural (6943) is a 40% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

Modulus

13.500MPa

Strength

175MPa

Impact

70kJ/m²

AKROMID^®

A3 GF 50 4 black (7282)

PA66 GF50

AKROMID® A3 GF 50 4 black (7282) is a 50% glass fibre reinforced, hydrolysis/chemical stabilised polyamide 6.6 with very high rigidity and strength

Modulus

17.000MPa

Strength

250MPa

Impact

110kJ/m²

AKROMID® A3 GF 50 4 black (7282) is a 50% glass fibre reinforced, hydrolysis/chemical stabilised polyamide 6.6 with very high rigidity and strength

AKROMID^®

Preliminary

A3 black (7557)

PA66

AKROMID® A3 black (7557) is an unreinforced, UV stabilised polyamide 6.6.

Modulus

3.200MPa

Strength

80MPa

Impact

180kJ/m²

AKROMID® A3 black (7557) is an unreinforced, UV stabilised polyamide 6.6.

AKROLOY^®

Preliminary

PA GF 60 LA black (8168)

PA66 + PA6I/6T GF60

AKROLOY® PA GF 60 LA black (8168) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

Modulus

21.400MPa

Strength

275MPa

Impact

95kJ/m²

AKROLOY® PA GF 60 LA black (8168) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

1 72 73 7480

AKROMID^®

A3 1 S3 black (1139)PA66-I

AKROMID® A3 1 S3 black (1139) is an unreinforced, impact modified Polyamide 6.6. It is characterised by a medium dry impact strength whilst maintaining good flowability. Furthermore, the material is heat stabilised and therefore perfectly suitable for connecting and fixing systems which are used at elevated temperatures in the automotive and electro industry. Its good flowability qualifies the material for processing in multi-cavity moulds. For new projects, please consider our successor grade A3 1 S3 schwarz (11392).

Features

heat stabilised 130

impact modified

Properties

Modulus

2.700MPa

Strength

63MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.

1 mm/min | conditioned

2700 MPa

1300 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.

50 mm/min | conditioned

63 MPa

45 MPa

Tensile strain at yield

ISO 527-2

50 mm/min | d.a.m.

50 mm/min | conditioned

5,6 %

> 20 %

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.

50 mm/min | conditioned

> 35 %

> 100 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.

2500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.

90 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.

7,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.

23°C | conditioned

30°C | d.a.m.

30°C | conditioned

no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.

23°C | conditioned

30°C | d.a.m.

30°C | conditioned

17 kJ/m²

95 kJ/m²

10 kJ/m²

13 kJ/m²

Izod notched impact strength

ISO 180/1A

23°C | d.a.m.

20°C | d.a.m.

40°C | d.a.m.

15 kJ/m²

12 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa

70 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa

213 °C

Melting temperature

ISO 11357-3

DSC, 10K/min

262 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel

23°C to 80°C | transverse

0,87 10⁻⁴/K

Flammability

Burning rate

UL 94

1,6 mm Wall thickness

HB Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness

650 °C

GWIT

IEC 60695-2-13

1,6 mm Wall thickness

675 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness

General properties

Density

ISO 1183

23°C

1,1 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.

2,0 - 2,2 %

Molding shrinkage

ISO 294-4

flow

transverse

1,3 - 1,5 %

1,5 - 1,7 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.

10¹⁵ Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.

10¹⁴ Ω

Comparative tracking index

IEC 60112

Test liquid A

600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Find the right compound

A3 1 S3 black (1139)PA66-I

Mechanical Properties

Tensile modulus

Tensile stress at yield

Tensile strain at yield

Tensile strain at break

Flexural modulus

Flexural strength

Flexural strain at break

Charpy impact strength

Charpy notched impact strength

Izod notched impact strength

Thermal Properties

Temperature of deflection under load HDT/A

Temperature of deflection under load HDT/B

Melting temperature

Coefficient of linear thermal expansion

Flammability

Burning rate

GWFI

GWIT

Burning rate (<100 mm/min)

General properties

Density

Humidity absorption

Molding shrinkage

Electrical Properties

Volume resistivity IEC

Surface resistivity

Comparative tracking index

Do you have any questions? We are happy to help.

Find the right compound

A3 1 S3 black (1139).css-117ixes{line-height:1.5;display:block;margin-top:var(--chakra-space-2);font-weight:var(--chakra-fontWeights-normal);font-size:var(--chakra-fontSizes-sm);color:var(--chakra-colors-kisPrimaryTextLight-700);}PA66-I

Mechanical Properties

Tensile modulus

Tensile stress at yield

Tensile strain at yield

Tensile strain at break

Flexural modulus

Flexural strength

Flexural strain at break

Charpy impact strength

Charpy notched impact strength

Izod notched impact strength

Thermal Properties

Temperature of deflection under load HDT/A

Temperature of deflection under load HDT/B

Melting temperature

Coefficient of linear thermal expansion

Flammability

Burning rate

GWFI

GWIT

Burning rate (<100 mm/min)

General properties

Density

Humidity absorption

Molding shrinkage

Electrical Properties

Volume resistivity IEC

Surface resistivity

Comparative tracking index

Do you have any questions? We are happy to help.

A3 1 S3 black (1139)PA66-I