AKROMID®

Preliminary

B3 GF 50 black (8524)

PA6 GF50

AKROMID® B3 GF 50 black (8524) is a 50% glass fibre reinforced, heat stabilised, easy flowing polyamide 6 with very high stiffness and strength.

Modulus

15.500MPa

Strength

230MPa

Impact

100kJ/m²

AKROMID® B3 GF 50 black (8524) is a 50% glass fibre reinforced, heat stabilised, easy flowing polyamide 6 with very high stiffness and strength.

AKROMID®

B3 1 natural (2499)

PA6

AKROMID® B3 1 natural (2499) is an unreinforced, heat stabilised polyamide 6 with light inherent color

Modulus

3.600MPa

Strength

85MPa

Impact

180kJ/m²

AKROMID® B3 1 natural (2499) is an unreinforced, heat stabilised polyamide 6 with light inherent color

AKROMID®

B3 GF 50 9 RM-M natural (3698)

PA6 + X GF50

AKROMID® B3 GF 50 9 RM-M natural (3698) is a 50% glass fibre reinforced, process improved polyamide 6 with very high stiffness and strength, limited moisture absorption and light inherent color.

Modulus

16.000MPa

Strength

210MPa

Impact

70kJ/m²

AKROMID® B3 GF 50 9 RM-M natural (3698) is a 50% glass fibre reinforced, process improved polyamide 6 with very high stiffness and strength, limited moisture absorption and light inherent color.

AKROMID®

S3 GF 30 4 natural (3552)

PA6.10

AKROMID® S3 GF 30 4 natural (3552) is a 30% glass fibre reinforced and hydrolysis stabilised polyamide 6.10 with high stiffness and strength as well as lower moisture absorption and very high chemical resistance

Modulus

8.600MPa

Strength

160MPa

Impact

110kJ/m²

AKROMID® S3 GF 30 4 natural (3552) is a 30% glass fibre reinforced and hydrolysis stabilised polyamide 6.10 with high stiffness and strength as well as lower moisture absorption and very high chemical resistance

AKROMID®

A3 1 L black (4652)

PA66 + PP

AKROMID® A3 1 L black (4652) - unreinforced PA6.6/PP-Blend lightweight, cost reduced

Modulus

2.300MPa

Strength

54MPa

Impact

180kJ/m²

AKROMID® A3 1 L black (4652) - unreinforced PA6.6/PP-Blend lightweight, cost reduced

AKROMID®

B3 GF 30 8 natural (5663)

PA6 GF30

AKROMID® B3 GF 30 8 natural (5663) - PA6, 30% glass fiber, food contact, kitchen and household appliances

Modulus

10.000MPa

Strength

185MPa

Impact

95kJ/m²

AKROMID® B3 GF 30 8 natural (5663) - PA6, 30% glass fiber, food contact, kitchen and household appliances

AKROLOY®

PA GF 20 black (5485)

PA66+PA6I/6T GF20

AKROLOY® PA GF 20 black (5485) is a 20% glass fibre reinforced, semi-aromatic polyamide blend with average stiffness and strength, even in conditioned state.

Modulus

7.000MPa

Strength

145MPa

Impact

40kJ/m²

AKROLOY® PA GF 20 black (5485) is a 20% glass fibre reinforced, semi-aromatic polyamide blend with average stiffness and strength, even in conditioned state.

171727380

AKROMID®

Preliminary
Internal

NEXT 5.6 3 GF 35 9 FR natural (8401)PA56 GF35 FR(40)

AKROMID® NEXT 5.6 3 GF 35 9 FR natural (8401) is a partially bio-based and flame retardant PA 5.6 and meets the requirement according to UL94 V0 @ 1.6 mm. The flame-retardant system is free of red phosphorus and halogens. PA 5.6 is a HMD-free (hexamethylenediamine) alternative to PA 6.6. With 35% glass fibre reinforcement, the material is suitable for components with high strength requirements for E&E and E-Mobility, such as busbar supports, switches, terminal strips and connector housings.

Features

Bio-based
heat stabilised 130
flame retardant
E&E

Properties

Modulus

12.000MPa

Strength

160MPa

Impact

71kJ/m²

Sustainability

Biobased carbon content

35 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
12000 MPa
7200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
160 MPa
105 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,5 %
4,1 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
12500 MPa
7700 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
255 MPa
160 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
2,8 %
4,0 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
71 kJ/m²
70 kJ/m²
69 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
12 kJ/m²
15 kJ/m²
11 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
230 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
254 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
3,2 mm Wall thickness
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
1,6 mm Wall thickness
960 °C
900 °C

GWIT

IEC 60695-2-13

0,8 mm Wall thickness
1,6 mm Wall thickness
725 °C
725 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,43 g/cm³

Water absorption

ISO 62

23°C, saturated
2,0 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more