AKROMID®

Preliminary

B3 GF 50 black (8524)

PA6 GF50

AKROMID® B3 GF 50 black (8524) is a 50% glass fibre reinforced, heat stabilised, easy flowing polyamide 6 with very high stiffness and strength.

Modulus

15.500MPa

Strength

230MPa

Impact

100kJ/m²

AKROMID® B3 GF 50 black (8524) is a 50% glass fibre reinforced, heat stabilised, easy flowing polyamide 6 with very high stiffness and strength.

AKROMID®

B3 1 natural (2499)

PA6

AKROMID® B3 1 natural (2499) is an unreinforced, heat stabilised polyamide 6 with light inherent color

Modulus

3.600MPa

Strength

85MPa

Impact

180kJ/m²

AKROMID® B3 1 natural (2499) is an unreinforced, heat stabilised polyamide 6 with light inherent color

AKROMID®

B3 GF 50 9 RM-M natural (3698)

PA6 + X GF50

AKROMID® B3 GF 50 9 RM-M natural (3698) is a 50% glass fibre reinforced, process improved polyamide 6 with very high stiffness and strength, limited moisture absorption and light inherent color.

Modulus

16.000MPa

Strength

210MPa

Impact

70kJ/m²

AKROMID® B3 GF 50 9 RM-M natural (3698) is a 50% glass fibre reinforced, process improved polyamide 6 with very high stiffness and strength, limited moisture absorption and light inherent color.

AKROMID®

S3 GF 30 4 natural (3552)

PA6.10

AKROMID® S3 GF 30 4 natural (3552) is a 30% glass fibre reinforced and hydrolysis stabilised polyamide 6.10 with high stiffness and strength as well as lower moisture absorption and very high chemical resistance

Modulus

8.600MPa

Strength

160MPa

Impact

110kJ/m²

AKROMID® S3 GF 30 4 natural (3552) is a 30% glass fibre reinforced and hydrolysis stabilised polyamide 6.10 with high stiffness and strength as well as lower moisture absorption and very high chemical resistance

AKROMID®

A3 1 L black (4652)

PA66 + PP

AKROMID® A3 1 L black (4652) - unreinforced PA6.6/PP-Blend lightweight, cost reduced

Modulus

2.300MPa

Strength

54MPa

Impact

180kJ/m²

AKROMID® A3 1 L black (4652) - unreinforced PA6.6/PP-Blend lightweight, cost reduced

AKROMID®

B3 GF 30 8 natural (5663)

PA6 GF30

AKROMID® B3 GF 30 8 natural (5663) - PA6, 30% glass fiber, food contact, kitchen and household appliances

Modulus

10.000MPa

Strength

185MPa

Impact

95kJ/m²

AKROMID® B3 GF 30 8 natural (5663) - PA6, 30% glass fiber, food contact, kitchen and household appliances

AKROLOY®

PA GF 20 black (5485)

PA66+PA6I/6T GF20

AKROLOY® PA GF 20 black (5485) is a 20% glass fibre reinforced, semi-aromatic polyamide blend with average stiffness and strength, even in conditioned state.

Modulus

7.000MPa

Strength

145MPa

Impact

40kJ/m²

AKROLOY® PA GF 20 black (5485) is a 20% glass fibre reinforced, semi-aromatic polyamide blend with average stiffness and strength, even in conditioned state.

171727380

AKROLOY®

PA LGF 50 natural (5504)PA66+PA6I/6T LGF50

AKROLOY® PA LGF 50 natural (5504) is a 50% long glass fibre reinforced, semi-aromatic polyamide blend with extraordinary high stiffness and strength even at high temperature and very high impact and notched impact strength at elevated and low temperature even in conditioned state. PA LGF 50 natural (5504) distinguish due to isotropic mechanical properties, low shrinkage, higher heat deflection temperature and very good fatigue performance. The material has very good surface properties.

Features

low warpage
reduced moisture

Properties

Modulus

19.000MPa

Strength

290MPa

Impact

100kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
19000 MPa
18500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
290 MPa
265 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,3 %
2,3 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
17500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
440 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2,8 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
100 kJ/m²
105 kJ/m²
85 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
42 kJ/m²
42 kJ/m²
45 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
230 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
200 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
255 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

General properties

Density

ISO 1183

23°C
1,59 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,2 - 1,4 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 - 0,5 %
0,6 - 0,8 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.