PRECITE® P3 GF 30 S1 natural (6853) is a 30% glass fibre reinforced, impact modified, medium viscous poly(butylene terephthalate) (PBT) with high stiffness and strength and lower density compared to neat PBT.

Modulus

9.500MPa

Strength

135MPa

Impact

85kJ/m²

AKROTEK^®

Preliminary

PK-VM GF 40 8 natural (6988)

PK GF40

AKROTEK® PK-VM GF 40 8 natural (6988) - Polyketon, 40% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

Modulus

11.000MPa

Strength

150MPa

Impact

65kJ/m²

AKROTEK® PK-VM GF 40 8 natural (6988) - Polyketon, 40% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

AKROMID^®

Preliminary

B3 GF 30 8 black (8166)

PA6 GF30

AKROMID® B3 GF 30 8 black (8166) - PA6, 30% glass fiber, food contact, kitchen and household appliances

Modulus

10.000MPa

Strength

175MPa

Impact

95kJ/m²

AKROMID® B3 GF 30 8 black (8166) - PA6, 30% glass fiber, food contact, kitchen and household appliances

AKROMID^®

B3 GF 60 black (2497)

PA6 GF60

AKROMID® B3 GF 60 black (2497) is a 60% glass fibre reinforced polyamide 6 with very high rigidity and strength

Modulus

21.000MPa

Strength

240MPa

Impact

90kJ/m²

AKROMID® B3 GF 60 black (2497) is a 60% glass fibre reinforced polyamide 6 with very high rigidity and strength

AKROLOY^®

PA GF 20 black (5485)

PA66+PA6I/6T GF20

AKROLOY® PA GF 20 black (5485) is a 20% glass fibre reinforced, semi-aromatic polyamide blend with average stiffness and strength, even in conditioned state.

Modulus

7.000MPa

Strength

145MPa

Impact

40kJ/m²

AKROLOY® PA GF 20 black (5485) is a 20% glass fibre reinforced, semi-aromatic polyamide blend with average stiffness and strength, even in conditioned state.

1 71 72 7380

AKROLEN^®

PP GFM 25/15 LA black (3143)PP (GF25+MD15)

AKROLEN® PP GFM 25/15 LA black (3143) is a 25% glass fibre reinforced, 15% mineralfilled, laser markable polypropylene with good surface and dimensional stability. This material is mainly used for thin wall housings for electronic parts in the automotive industry.

Features

laser markable

surface modified

low warpage

Properties

Modulus

6.500MPa

Strength

Impact

45kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.

6500 MPa

Tensile stress at break

ISO 527-2

50 mm/min | d.a.m.

75 MPa

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.

3,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.

6600 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.

105 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.

3,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.

30°C | d.a.m.

45 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.

10 kJ/m²

Izod impact strength

ISO 180/1A

23°C | d.a.m.

10 kJ/m²

Ball indentation hardness

ISO 2039-1

358N/30s | d.a.m.

100 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa

150 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa

163 °C

Melting temperature

ISO 11357-3

DSC, 10K/min

167 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel

23°C to 80°C | transverse

0,2 10⁻⁴/K

1,25 10⁻⁴/K

Flammability

Burning rate

UL 94

1,6 mm Wall thickness

HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness

General properties

Density

ISO 1183

23°C

1,21 g/cm³

Molding shrinkage

ISO 294-4

flow

transverse

0,1 - 0,3 %

0,4 - 0,6 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A

600 V

Dielectric strength

IEC 60243

3 mm

18 kV/mm

Rheological Properties

MVR

ISO 1133

230°C/2,16kg

13,5 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Find the right compound

PP GFM 25/15 LA black (3143)PP (GF25+MD15)

Mechanical Properties

Tensile modulus

Tensile stress at break

Tensile strain at break

Flexural modulus

Flexural strength

Flexural strain at break

Charpy impact strength

Charpy notched impact strength

Izod impact strength

Ball indentation hardness

Thermal Properties

Temperature of deflection under load HDT/A

Temperature of deflection under load HDT/B

Melting temperature

Coefficient of linear thermal expansion

Flammability

Burning rate

Burning rate (<100 mm/min)

General properties

Density

Molding shrinkage

Electrical Properties

Comparative tracking index

Dielectric strength

Rheological Properties

MVR

Do you have any questions? We are happy to help.

Find the right compound

PP GFM 25/15 LA black (3143).css-117ixes{line-height:1.5;display:block;margin-top:var(--chakra-space-2);font-weight:var(--chakra-fontWeights-normal);font-size:var(--chakra-fontSizes-sm);color:var(--chakra-colors-kisPrimaryTextLight-700);}PP (GF25+MD15)

Mechanical Properties

Tensile modulus

Tensile stress at break

Tensile strain at break

Flexural modulus

Flexural strength

Flexural strain at break

Charpy impact strength

Charpy notched impact strength

Izod impact strength

Ball indentation hardness

Thermal Properties

Temperature of deflection under load HDT/A

Temperature of deflection under load HDT/B

Melting temperature

Coefficient of linear thermal expansion

Flammability

Burning rate

Burning rate (<100 mm/min)

General properties

Density

Molding shrinkage

Electrical Properties

Comparative tracking index

Dielectric strength

Rheological Properties

MVR

Do you have any questions? We are happy to help.

PP GFM 25/15 LA black (3143)PP (GF25+MD15)