AKROMID®
A3 GK 30 natural (3689)
PA66 GB30
AKROMID® A3 GK 30 natural (3689) - PA 6.6, 30% glass beads reinforced, good surface, low warpage
5.000MPa
90MPa
28kJ/m²
AKROMID® A3 GK 30 natural (3689) - PA 6.6, 30% glass beads reinforced, good surface, low warpage
AKROTEK®
PK-HM black (4953)
PK
AKROTEK® PK-HM black (4953) - Polyketon, Tribology, friction and wear, chemical resistance
1.500MPa
60MPa
180kJ/m²
AKROTEK® PK-HM black (4953) - Polyketon, Tribology, friction and wear, chemical resistance
AKROMID®
B3 1 black (6528)
PA6
AKROMID® B3 1 black (6528) is an unreinforced, heat stabilised polyamide 6
3.600MPa
85MPa
180kJ/m²
AKROMID® B3 1 black (6528) is an unreinforced, heat stabilised polyamide 6
AKROTEK®
PK-VM GF 30 8 natural (6983)
PK GF30
AKROTEK® PK-VM GF 30 8 natural (6983) - Polyketon, 30% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA
8.200MPa
130MPa
60kJ/m²
AKROTEK® PK-VM GF 30 8 natural (6983) - Polyketon, 30% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA
AKROMID®
A3 CF 20 black (3132)
PA66 CF20
AKROMID® A3 CF 20 black (3132) is a 20% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties
15.000MPa
200MPa
40kJ/m²
AKROMID® A3 CF 20 black (3132) is a 20% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties
AKROMID®
S3 GF 30 4 natural (3552)
PA6.10
AKROMID® S3 GF 30 4 natural (3552) is a 30% glass fibre reinforced and hydrolysis stabilised polyamide 6.10 with high stiffness and strength as well as lower moisture absorption and very high chemical resistance
8.600MPa
160MPa
110kJ/m²
AKROMID® S3 GF 30 4 natural (3552) is a 30% glass fibre reinforced and hydrolysis stabilised polyamide 6.10 with high stiffness and strength as well as lower moisture absorption and very high chemical resistance
AKROLOY®
PA GF 30 black (6415)
PA66+PA6I/6T GF30
AKROLOY® PA GF 30 black (6415) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.
9.800MPa
200MPa
65kJ/m²
AKROLOY® PA GF 30 black (6415) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.
AKROTEK®
PK-VM GF 10 natural (8679)PK GF10
AKROTEK® PK-VM GF 10 natural (8679) is a 10% glass fibre reinforced Polyketone with average stiffness and strength. Due to its very good media resistance, the material is suitable for use in applications that carry cooling water. This type was developed as the successor to PK-VM GF 10 natural (8534) in order to meet the requirements for a larger processing window during processing.
Features
Properties
3.600MPa
75MPa
61kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Charpy impact strength
ISO 179-1/1eU
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
Burning rate (<100 mm/min)
FMVSS 302
General properties
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.