HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
558 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMID®

Preliminary

C3 GF 30 8 black (5657)

PA66 + PA6 GF30

AKROMID® C3 GF 30 8 black (5657) - PA6.6/6 Blend, GF 30, FDA, EU 10/2010, food contact, kitchen and household appliances

Modulus

9.400MPa

Strength

190MPa

Impact

82kJ/m²

AKROMID® C3 GF 30 8 black (5657) - PA6.6/6 Blend, GF 30, FDA, EU 10/2010, food contact, kitchen and household appliances

AKROTEK®

Preliminary

PK-VM GF 10 natural (8679)

PK GF10

AKROTEK® PK-VM GF 10 natural (8679) - Polyketon, 10% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

3.600MPa

Strength

75MPa

Impact

61kJ/m²

AKROTEK® PK-VM GF 10 natural (8679) - Polyketon, 10% glass fibre reinforced, chemical and hydrolysis resistance

AKROTEK®

Preliminary

PPS CF 30 black (8612)

PPS CF30

AKROTEK® PPS CF 30 black (8612) is a 30% carbon fibre reinforced, Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

Modulus

28.000MPa

Strength

230MPa

Impact

35kJ/m²

AKROTEK® PPS CF 30 black (8612) is a 30% carbon fibre reinforced, Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

AKROTEK®

Preliminary

PK-VM GF 10 8 natural (6981)

PK GF10

AKROTEK® PK-VM GF 10 8 natural (6981) - Polyketon, 10% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

Modulus

3.700MPa

Strength

80MPa

Impact

50kJ/m²

AKROTEK® PK-VM GF 10 8 natural (6981) - Polyketon, 10% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

AKROMID®

A3 GF 50 4 black (7282)

PA66 GF50

AKROMID® A3 GF 50 4 black (7282) is a 50% glass fibre reinforced, hydrolysis/chemical stabilised polyamide 6.6 with very high rigidity and strength

Modulus

17.000MPa

Strength

250MPa

Impact

110kJ/m²

AKROMID® A3 GF 50 4 black (7282) is a 50% glass fibre reinforced, hydrolysis/chemical stabilised polyamide 6.6 with very high rigidity and strength

AKROMID®

B3 GF 40 1 black (20016)

PA6 GF40

AKROMID® B3 GF 40 1 black (20016) is a 40% glass fibre reinforced, heat stabilised polyamide 6 with very high stiffness and strength

Modulus

12.500MPa

Strength

195MPa

Impact

95kJ/m²

AKROMID® B3 GF 40 1 black (20016) is a 40% glass fibre reinforced, heat stabilised polyamide 6 with very high stiffness and strength

AKROLOY®

Preliminary

PA GF 60 LA black (8168)

PA66 + PA6I/6T GF60

AKROLOY® PA GF 60 LA black (8168) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

Modulus

21.400MPa

Strength

275MPa

Impact

95kJ/m²

AKROLOY® PA GF 60 LA black (8168) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

170717280

AKROTEK®

UL
Preliminary

PK-VM GF 30 FR black (8604)PK GF30 FR(40)

AKROTEK® PK-VM GF 30 FR black (8604) is a 30% glass fibre reinforced, flame retardant and process improved Polyketone compound, colored in black. The flame retardant system is free of red phosphorous and halogens. Due to its good chemical resistance, good dimensional stability and high elongation at break it is suitable for high voltage components in e-mobility. The compound is laser markable.

Features

hydrolysis / chemically stabilised
flame retardant
laser markable
process improved
E&E
E-Mobility

Regulatory

ul

Properties

Modulus

8.600MPa

Strength

125MPa

Impact

70kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
8600 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
125 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
3,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
70 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
13 kJ/m²

Thermal Properties

RTI electrical

UL 746B

UL
0,8mm Wall thickness
UL
1,6mm Wall thickness
UL
3,2mm Wall thickness
105 °C
105 °C
105 °C

RTI impact

UL 746B

UL
0,8mm Wall thickness
UL
1,6mm Wall thickness
UL
3,2mm Wall thickness
70 °C
70 °C
80 °C

RTI strength

UL 746B

UL
0,8mm Wall thickness
UL
1,6mm Wall thickness
UL
3,2mm Wall thickness
115 °C
115 °C
125 °C

Flammability

Burning rate

UL 94

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
V-0 Class
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
960 °C
960 °C
960 °C

GWIT

IEC 60695-2-13

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
825 °C
825 °C
850 °C

HWI

UL 746A

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
0 PLC
0 PLC
0 PLC

HAI

UL 746A

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
0 PLC
0 PLC
0 PLC

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,48 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,3 - 0,5 %
0,8 - 1,0 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

UL
d.a.m.
1010 Ω x cm

Surface resistivity

DIN EN 62631-3-2

UL
d.a.m.
1013 Ω

Comparative tracking index

IEC 60112

UL
Test liquid A
600 V

Comparative tracking index

ASTM D3638

UL
0 PLC

Dielectric strength

IEC 60243

1 mm
29 kV/mm

Inclined-Plane Tracking, IPT

ASTM D2303-13

UL
1 kV

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more