AKROTEK®

PK-VM GF 50 8 black (6936)

PK GF50

AKROTEK® PK-VM GF 50 8 black (6939) - Polyketon, 50% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

Modulus

14.000MPa

Strength

170MPa

Impact

50kJ/m²

AKROTEK® PK-VM GF 50 8 black (6939) - Polyketon, 50% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

AKROTEK®

Preliminary

PK-VM GF 10 8 natural (6981)

PK GF10

AKROTEK® PK-VM GF 10 8 natural (6981) - Polyketon, 10% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

Modulus

3.700MPa

Strength

80MPa

Impact

50kJ/m²

AKROTEK® PK-VM GF 10 8 natural (6981) - Polyketon, 10% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

AKROMID®

Preliminary

B3 GF 30 8 black (8166)

PA6 GF30

AKROMID® B3 GF 30 8 black (8166) - PA6, 30% glass fiber, food contact, kitchen and household appliances

Modulus

10.000MPa

Strength

175MPa

Impact

95kJ/m²

AKROMID® B3 GF 30 8 black (8166) - PA6, 30% glass fiber, food contact, kitchen and household appliances

PRECITE®

Preliminary

P3 GF 25 9 FR natural (8212)

PBT GF25 FR(40)

PRECITE® P3 GF 25 9 FR natural (8212) - PBT, 25% glass fiber, flame retardant, high stiffness and strength, good long-term heat-aging, E-Mobility, E&E industry.

Modulus

8.500MPa

Strength

123MPa

Impact

53kJ/m²

PRECITE® P3 GF 25 9 FR natural (8212) - PBT, 25% glass fiber, flame retardant, high stiffness and strength, good long-term heat-aging, E-Mobility, E&E industry.

AKROMID®

Preliminary

NEXT U28 ICF 40 1 black (8238)

PA11 CF40

AKROMID® NEXT U28 ICF 40 1 black (8238) - PA11 made of renewable raw materials, recycled carbon fibre, low density, 3D printing of large parts

Modulus

20.000MPa

Strength

190MPa

Impact

80kJ/m²

AKROMID® NEXT U28 ICF 40 1 black (8238) - PA11 made of renewable raw materials, recycled carbon fibre, low density, 3D printing of large parts

AKROMID®

B3 black (2502)

PA6

AKROMID® B3 black (2502) is an unreinforced polyamide 6.

Modulus

3.600MPa

Strength

85MPa

Impact

180kJ/m²

AKROMID® B3 black (2502) is an unreinforced polyamide 6.

AKROTEK®

PK-HM 8 natural (6145)

PK

AKROTEK® PK-HM 8 natural (6145) - Polyketon, unreinforced, Tribology, friction and wear, chemical resistance, EU 10/2011, FDA 21 CFR

Modulus

1.400MPa

Strength

60MPa

Impact

180kJ/m²

AKROTEK® PK-HM 8 natural (6145) - Polyketon, unreinforced, Tribology, friction and wear, chemical resistance, EU 10/2011, FDA 21 CFR

170717280

AKROMID®

A3 GF 40 1 LT black (5709)PA66 GF40

AKROMID® A3 GF 40 1 LT black (5709) is a 40% glass fiber reinforced polyamide 6.6. It is characterised by a very high stiffness and strength. Furthermore, the material is heat stabilised as well as laser transparent and therefore perfectly suitable for technical plastic components in the automotive and electrical industry that have to be joined by laser welding.

Features

heat stabilised 130
laser transparent

Properties

Modulus

13.000MPa

Strength

225MPa

Impact

100kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
13000 MPa
9800 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
225 MPa
160 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
4 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
12000 MPa
9300 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
360 MPa
260 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
100 kJ/m²
105 kJ/m²
95 kJ/m²
95 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
17 kJ/m²
20 kJ/m²
15 kJ/m²
15 kJ/m²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
270 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
260 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
225 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel
23°C to 80°C | transverse
0,16 10⁻⁴/K
0,86 10⁻⁴/K

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
150 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,46 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,7 - 1,9 %

Water absorption

ISO 62

23°C, saturated
4,3 - 4,7 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,6 - 0,8 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more