AKROMIDĀ®

Preliminary

A3 black (7557)

PA66

AKROMIDĀ® A3 black (7557) is an unreinforced, UV stabilised polyamide 6.6.

Modulus

3.200MPa

Strength

80MPa

Impact

180kJ/mĀ²

AKROMIDĀ® A3 black (7557) is an unreinforced, UV stabilised polyamide 6.6.

AKROMIDĀ®

A3 GFM 25/15 1 black (3335)

PA66 (GF25+MD15)

AKROMIDĀ® A3 GFM 25/15 1 black (3335) is a 25% glass fibre reinforced, 15% mineral filled, heat stabilised polyamide 6.6 with good surface and dimensional stability

Modulus

10.000MPa

Strength

150MPa

Impact

50kJ/mĀ²

AKROMIDĀ® A3 GFM 25/15 1 black (3335) is a 25% glass fibre reinforced, 15% mineral filled, heat stabilised polyamide 6.6 with good surface and dimensional stability

AKROTEKĀ®

PK-VM 8 black (6466)

PK

AKROTEKĀ® PK-VM 8 black (6466) - Polyketon, Tribology, friction and wear, chemical resistance, food, drinking water, EU 10/2011

Modulus

1.600MPa

Strength

60MPa

Impact

180kJ/mĀ²

AKROTEKĀ® PK-VM 8 black (6466) - Polyketon, Tribology, friction and wear, chemical resistance, food, drinking water, EU 10/2011

AKROTEKĀ®

PK-VM GF 50 8 black (6936)

PK GF50

AKROTEKĀ® PK-VM GF 50 8 black (6939) - Polyketon, 50% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

Modulus

14.000MPa

Strength

170MPa

Impact

50kJ/mĀ²

AKROTEKĀ® PK-VM GF 50 8 black (6939) - Polyketon, 50% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

AKROMIDĀ®

A3 GK 30 6 natural (6774)

PA66 GB30

AKROMIDĀ® A3 GK 30 6 natural (6774) - 30% glass bead, inorganic high temperature stabilised, polyamide 6.6, low warpage, high surface appearance

Modulus

4.600MPa

Strength

90MPa

Impact

25kJ/mĀ²

AKROMIDĀ® A3 GK 30 6 natural (6774) - 30% glass bead, inorganic high temperature stabilised, polyamide 6.6, low warpage, high surface appearance

AKROMIDĀ®

A3 GF 50 4 black (7282)

PA66 GF50

AKROMIDĀ® A3 GF 50 4 black (7282) is a 50% glass fibre reinforced, hydrolysis/chemical stabilised polyamide 6.6 with very high rigidity and strength

Modulus

17.000MPa

Strength

250MPa

Impact

110kJ/mĀ²

AKROMIDĀ® A3 GF 50 4 black (7282) is a 50% glass fibre reinforced, hydrolysis/chemical stabilised polyamide 6.6 with very high rigidity and strength

AKROLOYĀ®

Preliminary

PA GF 60 LA black (8168)

PA66 + PA6I/6T GF60

AKROLOYĀ® PA GF 60 LA black (8168) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

Modulus

21.400MPa

Strength

275MPa

Impact

95kJ/mĀ²

AKROLOYĀ® PA GF 60 LA black (8168) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

170717280

AKROMIDĀ®

A3 GF 30 S1 black (1365)PA66-I GF30

AKROMIDĀ® A3 GF 30 S1 black (1365) is a 30% glass fiber reinforced, impact modified Polyamide 6.6. It is characterised by high stiffness and strength as well as a higher impact strength compared to a standard PA 6.6 GF 30. The material is perfectly suitable for connecting and fixing systems as well as for precision parts in the automotive industry.

Features

impact modified

Properties

Modulus

9.600MPa

Strength

180MPa

Impact

105kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
9600 MPa
8000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
180 MPa
120 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
5 %
6 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
30Ā°C | conditioned
-
105 kJ/mĀ²
110 kJ/mĀ²
85 kJ/mĀ²
100 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
30Ā°C | conditioned
-
17 kJ/mĀ²
20 kJ/mĀ²
12 kJ/mĀ²
12 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
255 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,34 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,7 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,7 - 0,9 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more