AKROMIDĀ®

B3 GF 35 S1 natural (920)

PA6-I GF35

AKROMIDĀ® B3 GF 35 S1 natural (920) is a 35% glass fibre reinforced, cold impact strength polyamide 6 with high stiffness and strength and light inherent color

Modulus

11.000MPa

Strength

190MPa

Impact

80kJ/mĀ²

AKROMIDĀ® B3 GF 35 S1 natural (920) is a 35% glass fibre reinforced, cold impact strength polyamide 6 with high stiffness and strength and light inherent color

AKROLENĀ®

Preliminary

PP ICF 30 AM black (8344)

PP CF30

AKROLENĀ® PP ICF 30 AM black (8344) - recycled carbon fibre reinforced polypropylene for additive manufacturing (3D-printing)

Modulus

12.500MPa

Strength

85MPa

Impact

50kJ/mĀ²

AKROLENĀ® PP ICF 30 AM black (8344) - recycled carbon fibre reinforced polypropylene for additive manufacturing (3D-printing)

AKROMIDĀ®

A3 CF 20 black (3132)

PA66 CF20

AKROMIDĀ® A3 CF 20 black (3132) is a 20% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties

Modulus

15.000MPa

Strength

200MPa

Impact

40kJ/mĀ²

AKROMIDĀ® A3 CF 20 black (3132) is a 20% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties

AKROMIDĀ®

A3 GK 30 6 black (6670)

PA66 GK30

AKROMIDĀ® A3 GK 30 6 black (6670) - 30% glass bead, inorganic high temperature stabilised, polyamide 6.6, low warpage, high surface appearance

Modulus

4.600MPa

Strength

86MPa

Impact

20kJ/mĀ²

AKROMIDĀ® A3 GK 30 6 black (6670) - 30% glass bead, inorganic high temperature stabilised, polyamide 6.6, low warpage, high surface appearance

AKROTEKĀ®

Preliminary

PK-VM GF 10 8 natural (6981)

PK GF10

AKROTEKĀ® PK-VM GF 10 8 natural (6981) - Polyketon, 10% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

Modulus

3.700MPa

Strength

80MPa

Impact

50kJ/mĀ²

AKROTEKĀ® PK-VM GF 10 8 natural (6981) - Polyketon, 10% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

AKROMIDĀ®

UL
Preliminary

B3 GF 30 1 HU LA black (2862)

PA6 GF30

AKROMIDĀ® B3 GF 30 1 HU LA black (2862) - PA 6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB, laser markable, automotive, E&E, industry.

Modulus

10.300MPa

Strength

185MPa

Impact

95kJ/mĀ²

AKROMIDĀ® B3 GF 30 1 HU LA black (2862) - PA 6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB, laser markable, automotive, E&E, industry.

AKROMIDĀ®

Preliminary

NEXT U28 ICF 40 1 black (8238)

PA11 CF40

AKROMIDĀ® NEXT U28 ICF 40 1 black (8238) - PA11 made of renewable raw materials, recycled carbon fibre, low density, 3D printing of large parts

Modulus

20.000MPa

Strength

190MPa

Impact

80kJ/mĀ²

AKROMIDĀ® NEXT U28 ICF 40 1 black (8238) - PA11 made of renewable raw materials, recycled carbon fibre, low density, 3D printing of large parts

169707180

AKROMIDĀ®

A3 ICF 30 5 black (6495)PA66 CF30

AKROMIDĀ® A3 ICF 30 5 black (6495) is a 30% carbon fibre reinforced, high heat stabilised polyamide 6.6 with high flexural strength and good sliding properties

Features

heat stabilised 230

Properties

Modulus

23.000MPa

Strength

235MPa

Impact

50kJ/mĀ²

Sustainability

Recycled content

30 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
23000 MPa
14500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
235 MPa
165 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
1,8 %
3 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
22000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
370 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2,5 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
50 kJ/mĀ²
65 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
30Ā°C | conditioned
-
8 kJ/mĀ²
11 kJ/mĀ²
6 kJ/mĀ²
6 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
250 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 Ā°C

Coefficient of linear thermal expansion

ISO 11359-1/2

23Ā°C to 80Ā°C | parallel
23Ā°C to 80Ā°C | transverse
0,06 10ā»ā“/K
0,72 10ā»ā“/K

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,27 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,9 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
104 ā„¦ x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
104 ā„¦

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more