HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/mĀ²
558 Compounds found
Recommended Ā 
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMIDĀ®

A3 5 black (4701)

PA66

AKROMIDĀ® A3 5 black (4701) is an unreinforced, high temperature stabilised polyamide 6.6

Modulus

3.500MPa

Strength

90MPa

Impact

180kJ/mĀ²

AKROMIDĀ® A3 5 black (4701) is an unreinforced, high temperature stabilised polyamide 6.6

AKROLOYĀ®

PA GF 60 black (7789)

PA66+PA6I/6T GF60

AKROLOYĀ® PA GF 60 black (7789) is a 60% glass fibre reinforced, easyflow, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

Modulus

21.400MPa

Strength

290MPa

Impact

100kJ/mĀ²

AKROLOYĀ® PA GF 60 black (7789) is a 60% glass fibre reinforced, easyflow, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

AKROMIDĀ®

B3 GF 35 S1 natural (920)

PA6-I GF35

AKROMIDĀ® B3 GF 35 S1 natural (920) is a 35% glass fibre reinforced, cold impact strength polyamide 6 with high stiffness and strength and light inherent color

Modulus

11.000MPa

Strength

190MPa

Impact

80kJ/mĀ²

AKROMIDĀ® B3 GF 35 S1 natural (920) is a 35% glass fibre reinforced, cold impact strength polyamide 6 with high stiffness and strength and light inherent color

AKROLOYĀ®

Preliminary

PA GF 60 LA black (8168)

PA66 + PA6I/6T GF60

AKROLOYĀ® PA GF 60 LA black (8168) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

Modulus

21.400MPa

Strength

275MPa

Impact

95kJ/mĀ²

AKROLOYĀ® PA GF 60 LA black (8168) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

AKROMIDĀ®

Preliminary

NEXT G3 GF 30 1 L CR black (8314)

PA6.9 + PP GF30

AKROMIDĀ® NEXT G3 GF 30 1 L CI black (8314) - PA 6.9/PP blend, bio-based, certified, low moisture absorption, weight reduction.

Modulus

8.000MPa

Strength

125MPa

Impact

65kJ/mĀ²

AKROMIDĀ® NEXT G3 GF 30 1 L CI black (8314) - PA 6.9/PP blend, bio-based, certified, low moisture absorption, weight reduction.

AKROLENĀ®

Preliminary

PP ICF 30 AM black (8344)

PP CF30

AKROLENĀ® PP ICF 30 AM black (8344) - recycled carbon fibre reinforced polypropylene for additive manufacturing (3D-printing)

Modulus

12.500MPa

Strength

85MPa

Impact

50kJ/mĀ²

AKROLENĀ® PP ICF 30 AM black (8344) - recycled carbon fibre reinforced polypropylene for additive manufacturing (3D-printing)

AKROMIDĀ®

A3 GF 50 4 natural (71090)

PA66 GF50

AKROMIDĀ® A3 GF 50 4 natural (71090) - PA6.6, 50% glass fiber, cooling water, hydrolysis resistant, DPPD free

Modulus

18.000MPa

Strength

260MPa

Impact

110kJ/mĀ²

AKROMIDĀ® A3 GF 50 4 natural (71090) - PA6.6, 50% glass fiber, cooling water, hydrolysis resistant, DPPD free

169707180

AKROMIDĀ®

B3 GF 25 1 L black (4637)PA6+PP GF25

AKROMIDĀ® B3 GF 25 1 L black (4637) is a PA6/PP-blend with reduced density compared to standard PA6 with 25% glass fibre reinforcement. The material is suitable for components with high strength and stiffness where cost and weight reduction are required at the same time. The chemical resistance of AKROMIDĀ® B3 GF 25 1 L black (4637) is particularly superior to calcium chloride (CaClā‚‚).

Features

heat stabilised 130
reduced density

Properties

Modulus

7.500MPa

Strength

135MPa

Impact

68kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
7500 MPa
5600 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
135 MPa
88 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,3 %
4,5 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
30Ā°C | conditioned
-
68 kJ/mĀ²
58 kJ/mĀ²
67 kJ/mĀ²
54 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
30Ā°C | conditioned
-
15 kJ/mĀ²
15 kJ/mĀ²
13 kJ/mĀ²
10 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
198 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
217 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 Ā°C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
750 Ā°C
725 Ā°C
750 Ā°C

GWIT

IEC 60695-2-13

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
775 Ā°C
750 Ā°C
775 Ā°C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,22 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,55 - 0,75 %

Rheological Properties

MVR

ISO 1133

275Ā°C/5kg
10 cmĀ³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.