AKROMID®
S3 GF 30 4 natural (3552)
PA6.10
AKROMID® S3 GF 30 4 natural (3552) is a 30% glass fibre reinforced and hydrolysis stabilised polyamide 6.10 with high stiffness and strength as well as lower moisture absorption and very high chemical resistance
8.600MPa
160MPa
110kJ/m²
AKROMID® S3 GF 30 4 natural (3552) is a 30% glass fibre reinforced and hydrolysis stabilised polyamide 6.10 with high stiffness and strength as well as lower moisture absorption and very high chemical resistance
AKROMID®
S3 GF 30 4 black (3429)
PA610 GF30
AKROMID® S3 GF 30 4 black (3429) is a 30% glass fibre reinforced and hydrolysis stabilised polyamide 6.10 with high stiffness and strength as well as lower moisture absorption and very high chemical resistance.
8.600MPa
160MPa
110kJ/m²
AKROMID® S3 GF 30 4 black (3429) is a 30% glass fibre reinforced and hydrolysis stabilised polyamide 6.10 with high stiffness and strength as well as lower moisture absorption and very high chemical resistance.
AKROLOY®
PA GF 20 black (5485)
PA66+PA6I/6T GF20
AKROLOY® PA GF 20 black (5485) is a 20% glass fibre reinforced, semi-aromatic polyamide blend with average stiffness and strength, even in conditioned state.
7.000MPa
145MPa
40kJ/m²
AKROLOY® PA GF 20 black (5485) is a 20% glass fibre reinforced, semi-aromatic polyamide blend with average stiffness and strength, even in conditioned state.
AKROLOY®
PA GF 40 natural (6413)
PA66+PA6I/6T GF40
AKROLOY® PA GF 40 natural (6413) is a 40% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.
13.000MPa
235MPa
95kJ/m²
AKROLOY® PA GF 40 natural (6413) is a 40% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.
AKROMID®
A3 CF 20 black (3132)
PA66 CF20
AKROMID® A3 CF 20 black (3132) is a 20% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties
15.000MPa
200MPa
40kJ/m²
AKROMID® A3 CF 20 black (3132) is a 20% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties
AKROMID®
A3 GK 30 natural (3689)
PA66 GB30
AKROMID® A3 GK 30 natural (3689) - PA 6.6, 30% glass beads reinforced, good surface, low warpage
5.000MPa
90MPa
28kJ/m²
AKROMID® A3 GK 30 natural (3689) - PA 6.6, 30% glass beads reinforced, good surface, low warpage
AKROLOY®
PA GF 30 black (6415)
PA66+PA6I/6T GF30
AKROLOY® PA GF 30 black (6415) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.
9.800MPa
200MPa
65kJ/m²
AKROLOY® PA GF 30 black (6415) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.
AKROMID®
AKROMID® T91 GF 30 FR natural (8667) is an easy flow, flame retardant and 30% glass fiber reinforced Polyamide 9T with high stiffness and strength. This material is based on the latest flame retardant technology, that is free of red phosphorous, melamine, PFAS and halogenes. This product is characterised by very high flowability for thin walled parts. Due its high melting point and low water uptake it is a perfect candidate for SMT devices.
Features
Properties
10.500MPa
150MPa
55kJ/m²
ISO 527-2
ISO 527-2
ISO 527-2
ISO 179-1/1eU
ISO 179-1/1eA
ISO 75
ISO 75
UL 94
ISO 1183
ISO 1110
ISO 294-4
IEC 60112
IEC 60243
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.