AKROMID®

B3 GF 60 black (2497)

PA6 GF60

AKROMID® B3 GF 60 black (2497) is a 60% glass fibre reinforced polyamide 6 with very high rigidity and strength

Modulus

21.000MPa

Strength

240MPa

Impact

90kJ/m²

AKROMID® B3 GF 60 black (2497) is a 60% glass fibre reinforced polyamide 6 with very high rigidity and strength

AKROMID®

A3 CF 20 black (3132)

PA66 CF20

AKROMID® A3 CF 20 black (3132) is a 20% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties

Modulus

15.000MPa

Strength

200MPa

Impact

40kJ/m²

AKROMID® A3 CF 20 black (3132) is a 20% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties

AKROMID®

A3 GF 25 3 black (3094)

PA66 GF25

AKROMID® A3 GF 25 3 black (3094) is a 25% glass fibre reinforced, nucleated polyamide 6.6 with high stiffness and strength

Modulus

8.500MPa

Strength

160MPa

Impact

50kJ/m²

AKROMID® A3 GF 25 3 black (3094) is a 25% glass fibre reinforced, nucleated polyamide 6.6 with high stiffness and strength

AKROMID®

A3 GK 30 natural (3689)

PA66 GB30

AKROMID® A3 GK 30 natural (3689) - PA 6.6, 30% glass beads reinforced, good surface, low warpage

Modulus

5.000MPa

Strength

90MPa

Impact

28kJ/m²

AKROMID® A3 GK 30 natural (3689) - PA 6.6, 30% glass beads reinforced, good surface, low warpage

AKROMID®

A3 1 L black (4652)

PA66 + PP

AKROMID® A3 1 L black (4652) - unreinforced PA6.6/PP-Blend lightweight, cost reduced

Modulus

2.300MPa

Strength

54MPa

Impact

180kJ/m²

AKROMID® A3 1 L black (4652) - unreinforced PA6.6/PP-Blend lightweight, cost reduced

AKROMID®

A3 GK 30 6 black (6670)

PA66 GK30

AKROMID® A3 GK 30 6 black (6670) - 30% glass bead, inorganic high temperature stabilised, polyamide 6.6, low warpage, high surface appearance

Modulus

4.600MPa

Strength

86MPa

Impact

20kJ/m²

AKROMID® A3 GK 30 6 black (6670) - 30% glass bead, inorganic high temperature stabilised, polyamide 6.6, low warpage, high surface appearance

AKROTEK®

Preliminary

PK-VM GF 20 natural (6982)

PK GF20

AKROTEK® PK-VM GF 20 8 natural (6982) is a 20% glass fibre reinforced, low viscous polyketone with average stiffness and strength and light inherent color. Please note that the material is NOT suitable anymore for drinking water contact and does NOT meet the requirements according to KTW, DVGW W270, ACS, WRAS as well as NSF61 and does NOT correspond to the European food guideline EU 10/2011 as well as to the American FDA 21 CFR guideline.

Modulus

5.800MPa

Strength

100MPa

Impact

50kJ/m²

AKROTEK® PK-VM GF 20 8 natural (6982) is a 20% glass fibre reinforced, low viscous polyketone with average stiffness and strength and light inherent color. Please note that the material is NOT suitable anymore for drinking water contact and does NOT meet the requirements according to KTW, DVGW W270, ACS, WRAS as well as NSF61 and does NOT correspond to the European food guideline EU 10/2011 as well as to the American FDA 21 CFR guideline.

168697080

AKROMID®

C28 GF 25 FRT grey (8133)PA-Blend

AKROMID® C28 GF 25 FRT grey (8133) is a 25 % glass fiber reinforced, flame retardant and easy flowing PA blend, colored in grey similar to RAL 7011. The material is based on a flame retardant system that is free of red phosphorus and halogens. This grade is suitable for railroad applications and certified to EN 45545-2 R6 and EN 45545-2 R1. To achieve an excellent surface quality a mould temperature of at least 120°C is necessary.

Features

flame retardant
surface modified
easy flow
public transportation

Regulatory

en45545-2

Properties

Modulus

11.000MPa

Strength

150MPa

Impact

Na

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
11000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
150 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2,1 %

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
238 °C

Flammability

Burning rate

UL 94

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
V-0 Class
V-0 Class
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
960 °C
960 °C
960 °C
960 °C

GWIT

IEC 60695-2-13

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
825 °C
800 °C
800 °C
850 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

Protection Train

EN 45545-2

R1/6/7 HL2

General properties

Density

ISO 1183

23°C
1,44 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,9 - 1,1 %

Molding shrinkage

ISO 294-4

flow
transverse
< 0,2 %
0,1 - 0,3 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
> 600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.