Description

AKROMIDĀ®

S3 GF 30 4 natural (3552)

PA6.10

AKROMIDĀ® S3 GF 30 4 natural (3552) is a 30% glass fibre reinforced and hydrolysis stabilised polyamide 6.10 with high stiffness and strength as well as lower moisture absorption and very high chemical resistance

Modulus

8.600MPa

Strength

160MPa

Impact

110kJ/mĀ²

AKROMIDĀ® S3 GF 30 4 natural (3552) is a 30% glass fibre reinforced and hydrolysis stabilised polyamide 6.10 with high stiffness and strength as well as lower moisture absorption and very high chemical resistance

AKROMIDĀ®

Preliminary

S3 GF 30 4 black (3429)

PA610 GF30

AKROMIDĀ® S3 GF 30 4 black (3429) is a 30% glass fibre reinforced and hydrolysis stabilised polyamide 6.10 with high stiffness and strength as well as lower moisture absorption and very high chemical resistance.

Modulus

8.600MPa

Strength

160MPa

Impact

110kJ/mĀ²

AKROMIDĀ® S3 GF 30 4 black (3429) is a 30% glass fibre reinforced and hydrolysis stabilised polyamide 6.10 with high stiffness and strength as well as lower moisture absorption and very high chemical resistance.

AKROLOYĀ®

PA GF 20 black (5485)

PA66+PA6I/6T GF20

AKROLOYĀ® PA GF 20 black (5485) is a 20% glass fibre reinforced, semi-aromatic polyamide blend with average stiffness and strength, even in conditioned state.

Modulus

7.000MPa

Strength

145MPa

Impact

40kJ/mĀ²

AKROLOYĀ® PA GF 20 black (5485) is a 20% glass fibre reinforced, semi-aromatic polyamide blend with average stiffness and strength, even in conditioned state.

AKROLOYĀ®

Preliminary

PA GF 40 natural (6413)

PA66+PA6I/6T GF40

AKROLOYĀ® PA GF 40 natural (6413) is a 40% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

Modulus

13.000MPa

Strength

235MPa

Impact

95kJ/mĀ²

AKROLOYĀ® PA GF 40 natural (6413) is a 40% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

AKROMIDĀ®

A3 CF 20 black (3132)

PA66 CF20

AKROMIDĀ® A3 CF 20 black (3132) is a 20% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties

Modulus

15.000MPa

Strength

200MPa

Impact

40kJ/mĀ²

AKROMIDĀ® A3 CF 20 black (3132) is a 20% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties

AKROMIDĀ®

A3 GK 30 natural (3689)

PA66 GB30

AKROMIDĀ® A3 GK 30 natural (3689) - PA 6.6, 30% glass beads reinforced, good surface, low warpage

Modulus

5.000MPa

Strength

90MPa

Impact

28kJ/mĀ²

AKROMIDĀ® A3 GK 30 natural (3689) - PA 6.6, 30% glass beads reinforced, good surface, low warpage

AKROLOYĀ®

Preliminary

PA GF 30 black (6415)

PA66+PA6I/6T GF30

AKROLOYĀ® PA GF 30 black (6415) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.

Modulus

9.800MPa

Strength

200MPa

Impact

65kJ/mĀ²

AKROLOYĀ® PA GF 30 black (6415) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.

168697080

AKROMIDĀ®

A3 GF 30 S1 black (1365)PA66-I GF30

AKROMIDĀ® A3 GF 30 S1 black (1365) is a 30% glass fiber reinforced, impact modified Polyamide 6.6. It is characterised by high stiffness and strength as well as a higher impact strength compared to a standard PA 6.6 GF 30. The material is perfectly suitable for connecting and fixing systems as well as for precision parts in the automotive industry.

Features

impact modified

Properties

Modulus

9.600MPa

Strength

180MPa

Impact

105kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
9600 MPa
8000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
180 MPa
120 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
5 %
6 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
30Ā°C | conditioned
-
105 kJ/mĀ²
110 kJ/mĀ²
85 kJ/mĀ²
100 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
30Ā°C | conditioned
-
17 kJ/mĀ²
20 kJ/mĀ²
12 kJ/mĀ²
12 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
255 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,34 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,7 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,7 - 0,9 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.