AKROMID®
A3 GF 40 1 L black (4671)
PA66+PP GF40
AKROMID® A3 GF 40 1 L black (4671) - PA6.6/PP-Blend, 40% glass fibre reinforced, lower density, cost reduced, zinc chloride
11.800MPa
170MPa
80kJ/m²
AKROMID® A3 GF 40 1 L black (4671) - PA6.6/PP-Blend, 40% glass fibre reinforced, lower density, cost reduced, zinc chloride
AKROLOY®
PA GF 30 black (6415)
PA66+PA6I/6T GF30
AKROLOY® PA GF 30 black (6415) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.
9.800MPa
200MPa
65kJ/m²
AKROLOY® PA GF 30 black (6415) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.
AKROMID®
A3 GK 30 6 natural (6774)
PA66 GB30
AKROMID® A3 GK 30 6 natural (6774) - 30% glass bead, inorganic high temperature stabilised, polyamide 6.6, low warpage, high surface appearance
4.600MPa
90MPa
25kJ/m²
AKROMID® A3 GK 30 6 natural (6774) - 30% glass bead, inorganic high temperature stabilised, polyamide 6.6, low warpage, high surface appearance
AKROTEK®
PK-VM GF 50 8 black (6936)
PK GF50
AKROTEK® PK-VM GF 50 8 black (6939) - Polyketon, 50% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA
14.000MPa
170MPa
50kJ/m²
AKROTEK® PK-VM GF 50 8 black (6939) - Polyketon, 50% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA
AKROMID®
A3 1 black (2417)
PA66
AKROMID® A3 1 black (2417) is a heat stabilised, unreinforced polyamide 6.6
3.200MPa
85MPa
180kJ/m²
AKROMID® A3 1 black (2417) is a heat stabilised, unreinforced polyamide 6.6
AKROMID®
B3 1 natural (2499)
PA6
AKROMID® B3 1 natural (2499) is an unreinforced, heat stabilised polyamide 6 with light inherent color
3.600MPa
85MPa
180kJ/m²
AKROMID® B3 1 natural (2499) is an unreinforced, heat stabilised polyamide 6 with light inherent color
AKROMID®
B3 GF 50 9 RM-M natural (3698)
PA6 + X GF50
AKROMID® B3 GF 50 9 RM-M natural (3698) is a 50% glass fibre reinforced, process improved polyamide 6 with very high stiffness and strength, limited moisture absorption and light inherent color.
16.000MPa
210MPa
70kJ/m²
AKROMID® B3 GF 50 9 RM-M natural (3698) is a 50% glass fibre reinforced, process improved polyamide 6 with very high stiffness and strength, limited moisture absorption and light inherent color.
AKROMID®
T9 ICF 30 6 black (7908)PPA
AKROMID® T9 ICF 30 6 black (7908) is a 30% carbon fibre polyphthalamide with high stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
Properties
26.000MPa
235MPa
40kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Flexural strain at break
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
General properties
Density
ISO 1183
Molding shrinkage
ISO 294-4
Electrical Properties
Surface resistivity
DIN EN 62631-3-2
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.