AKROMIDĀ®
NEXT U3 ICF 20 1 black (8232)
PA11 CF20
AKROMIDĀ® NEXT U3 ICF 20 1 black (8232) - PA11 made of renewable raw materials, recycled carbon fibre, low density, Fused Filament Fabrication
9.300MPa
110MPa
60kJ/mĀ²
AKROMIDĀ® NEXT U3 ICF 20 1 black (8232) - PA11 made of renewable raw materials, recycled carbon fibre, low density, Fused Filament Fabrication
AKROTEKĀ®
PPS GF 40 natural (8064)
PPS GF40
AKROTEKĀ® PPS GF 40 natural (8064) is a 40% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.
12.000MPa
190MPa
50kJ/mĀ²
AKROTEKĀ® PPS GF 40 natural (8064) is a 40% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.
AKROMIDĀ®
B3 GF 25 natural (2471)
PA6 GF25
AKROMIDĀ® B3 GF 25 natural (2471) is a 25% glass fibre reinforced polyamide 6 with high stiffness and strength and light inherent color
8.500MPa
160MPa
85kJ/mĀ²
AKROMIDĀ® B3 GF 25 natural (2471) is a 25% glass fibre reinforced polyamide 6 with high stiffness and strength and light inherent color
AKROMIDĀ®
A3 GFM 25/15 1 black (3335)
PA66 (GF25+MD15)
AKROMIDĀ® A3 GFM 25/15 1 black (3335) is a 25% glass fibre reinforced, 15% mineral filled, heat stabilised polyamide 6.6 with good surface and dimensional stability
10.000MPa
150MPa
50kJ/mĀ²
AKROMIDĀ® A3 GFM 25/15 1 black (3335) is a 25% glass fibre reinforced, 15% mineral filled, heat stabilised polyamide 6.6 with good surface and dimensional stability
AKROMIDĀ®
C3 GF 60 1 black (4659)
PA66 + PA6 GF60
AKROMIDĀ® C3 GF 60 1 black (4659) is a 60% glass fibre reinforced, heat stabilised polyamide 6.6/6 - Blend.
21.300MPa
270MPa
96kJ/mĀ²
AKROMIDĀ® C3 GF 60 1 black (4659) is a 60% glass fibre reinforced, heat stabilised polyamide 6.6/6 - Blend.
AKROLOYĀ®
PA GF 40 natural (6413)
PA66+PA6I/6T GF40
AKROLOYĀ® PA GF 40 natural (6413) is a 40% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.
13.000MPa
235MPa
95kJ/mĀ²
AKROLOYĀ® PA GF 40 natural (6413) is a 40% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.
AKROLOYĀ®
PA GF 30 black (6415)
PA66+PA6I/6T GF30
AKROLOYĀ® PA GF 30 black (6415) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.
9.800MPa
200MPa
65kJ/mĀ²
AKROLOYĀ® PA GF 30 black (6415) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.
AKROMIDĀ®
AKROMIDĀ® T9 GF 15 S1 black (7820) is a 15% glass fibre reinforced, cold impact strength polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
Features
Properties
5.000MPa
120MPa
73kJ/mĀ²
ISO 527-2
ISO 527-2
ISO 527-2
ISO 179-1/1eU
ISO 179-1/1eA
ISO 75
ISO 75
ISO 11357-2
ISO 11357-3
UL 94
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.