HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
558 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

PRECITE®

Preliminary

P3 GF 30 S1 natural (6853)

PBT-GF 30

PRECITE® P3 GF 30 S1 natural (6853) is a 30% glass fibre reinforced, impact modified, medium viscous poly(butylene terephthalate) (PBT) with high stiffness and strength and lower density compared to neat PBT.

Modulus

9.500MPa

Strength

135MPa

Impact

85kJ/m²

PRECITE® P3 GF 30 S1 natural (6853) is a 30% glass fibre reinforced, impact modified, medium viscous poly(butylene terephthalate) (PBT) with high stiffness and strength and lower density compared to neat PBT.

PRECITE®

Preliminary

E GF 20 natural (7301)

PET GF 20

PRECITE® E GF 20 natural (7301) - PET, 20% glass fibre, good stiffness, good toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

7.800MPa

Strength

145MPa

Impact

40kJ/m²

PRECITE® E GF 20 natural (7301) - PET, 20% glass fibre, good stiffness, good toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

AKROTEK®

PK-VM GF 10 grey (7344)

PK GF10

AKROTEK® PK-VM GF 10 grey (7344) - Polyketon, 10% glass fiber reinforced, chemical resistance, RAL 7044

Modulus

3.600MPa

Strength

65MPa

Impact

50kJ/m²

AKROTEK® PK-VM GF 10 grey (7344) - Polyketon, 10% glass fiber reinforced, chemical resistance, RAL 7044

AKROMID®

Preliminary

NEXT 5.6 3 GF 30 S3 black (8444)

PA56 GF30

AKROMID® NEXT 5.6 3 GF 30 S3 black (8444) - partly bio-based and HMD-free PA 5.6, 30 % GF, impact modified, high strength and stiffness.

Modulus

8.600MPa

Strength

180MPa

Impact

96kJ/m²

AKROMID® NEXT 5.6 3 GF 30 S3 black (8444) - partly bio-based and HMD-free PA 5.6, 30 % GF, impact modified, high strength and stiffness.

AKROMID®

B28 GF 30 S3 black (8438)

PA6-I GF30

AKROMID® B28 GF 30 S3 black (8438) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

Modulus

9.000MPa

Strength

155MPa

Impact

100kJ/m²

AKROMID® B28 GF 30 S3 black (8438) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

AKROMID®

B3 GF 20 black (2491)

PA6 GF20

AKROMID® B3 GF 20 black (2491) is a 20% glass fibre reinforced polyamide 6 with medium stiffness and strength

Modulus

6.800MPa

Strength

150MPa

Impact

73kJ/m²

AKROMID® B3 GF 20 black (2491) is a 20% glass fibre reinforced polyamide 6 with medium stiffness and strength

AKROMID®

A3 CF 20 black (3132)

PA66 CF20

AKROMID® A3 CF 20 black (3132) is a 20% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties

Modulus

15.000MPa

Strength

200MPa

Impact

40kJ/m²

AKROMID® A3 CF 20 black (3132) is a 20% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties

167686980

AKROMID®

S3 1 black (3317)PA610

AKROMID® S3 1 black (3317) is a nonreinforced and heat stabilised polyamide 6.10 with lower moisture absorption and high chemical resistance.

Features

heat stabilised 130
reduced moisture

Properties

Modulus

2.400MPa

Strength

70MPa

Impact

180kJ/m²

Sustainability

Biobased carbon content

60 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
2400 MPa
1200 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
70 MPa
50 MPa

Tensile strain at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
4,5 %
20 %

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
> 50 %
> 50 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
1900 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
100 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
no break
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
4 kJ/m²
12 kJ/m²
4 kJ/m²

Ball indentation hardness

ISO 2039-1

358N/30s | d.a.m.
125 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
55 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
150 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,08 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,7 %

Molding shrinkage

ISO 294-4

flow
transverse
1,6 %
1,8 %

Rheological Properties

MVR

ISO 1133

275°C/2,16kg
10 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more