AKROTEK®

Preliminary

PK-VM GF 60 natural (8684)

PK GF60

AKROTEK® PK-VM GF 60 natural (8684) - Polyketon, 60% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

17.500MPa

Strength

180MPa

Impact

70kJ/m²

AKROTEK® PK-VM GF 60 natural (8684) - Polyketon, 60% glass fibre reinforced, chemical and hydrolysis resistance

AKROMID®

A3 1 L black (4652)

PA66 + PP

AKROMID® A3 1 L black (4652) - unreinforced PA6.6/PP-Blend lightweight, cost reduced

Modulus

2.300MPa

Strength

54MPa

Impact

180kJ/m²

AKROMID® A3 1 L black (4652) - unreinforced PA6.6/PP-Blend lightweight, cost reduced

AKROMID®

A3 1 L natural (4800)

PA66 + PP

AKROMID® A3 1 L natural (4800) - unreinforced PA6.6/PP-Blend lightweight, cost reduced

Modulus

2.300MPa

Strength

55MPa

Impact

180kJ/m²

AKROMID® A3 1 L natural (4800) - unreinforced PA6.6/PP-Blend lightweight, cost reduced

AKROLOY®

Preliminary

PA GF 40 natural (6413)

PA66+PA6I/6T GF40

AKROLOY® PA GF 40 natural (6413) is a 40% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

Modulus

13.000MPa

Strength

235MPa

Impact

95kJ/m²

AKROLOY® PA GF 40 natural (6413) is a 40% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

AKROMID®

Preliminary

B28 GF 15 natural (6940)

PA6 GF 15

AKROMID B28 GF 15 natural (6940) - PA 6, glass fiber reinforced, easy flow, good surface, bus fire standard ECE R 118.03, medium stiffness and strength.

Modulus

5.300MPa

Strength

120MPa

Impact

39kJ/m²

AKROMID B28 GF 15 natural (6940) - PA 6, glass fiber reinforced, easy flow, good surface, bus fire standard ECE R 118.03, medium stiffness and strength.

AKROTEK®

PK-VM GF 30 8 natural (6983)

PK GF30

AKROTEK® PK-VM GF 30 8 natural (6983) - Polyketon, 30% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

Modulus

8.200MPa

Strength

130MPa

Impact

60kJ/m²

AKROTEK® PK-VM GF 30 8 natural (6983) - Polyketon, 30% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

AKROMID®

Preliminary

B3 GF 30 5 black (8536)

PA6 GF30

AKROMID® B3 GF 30 5 black (8536) - PA6, 30% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.

Modulus

9.500MPa

Strength

170MPa

Impact

60kJ/m²

AKROMID® B3 GF 30 5 black (8536) - PA6, 30% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.

167686980

AKROMID®

Internal

B3 GF 15 S1 black (3228)PA6-I GF15

AKROMID® B3 GF 15 S1 black (3228) is a 15% glass fiber reinforced, impact modified Polyamide 6. It is characterised by medium stiffness and strength as well as a higher impact strength compared to a standard PA 6 GF 15. It also has good surface properties. The material is therefore perfectly suitable for toughness demanding but high integrated parts with a good surface appearance in the automotive, electro, and furniture industry.

Features

impact modified

Properties

Modulus

5.500MPa

Strength

110MPa

Impact

70kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
5500 MPa
3100 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
110 MPa
75 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
4 %
10 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
5300 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
175 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
70 kJ/m²
95 kJ/m²
50 kJ/m²
45 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
6 kJ/m²
14 kJ/m²
6 kJ/m²
5 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
200 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
222 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel
23°C to 80°C | transverse
0,3 10⁻⁴/K
1,3 10⁻⁴/K

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,22 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,3 %

Molding shrinkage

ISO 294-4

flow
transverse
0,2 - 0,4 %
0,6 - 0,8 %

Rheological Properties

MVR

ISO 1133

275°C/5kg
45 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more