AKROMID® S3 GF 30 4 black (3429) is a 30% glass fibre reinforced and hydrolysis stabilised polyamide 6.10 with high stiffness and strength as well as lower moisture absorption and very high chemical resistance.

Modulus

8.600MPa

Strength

160MPa

Impact

110kJ/m²

AKROMID^®

B3 black (2502)

PA6

AKROMID® B3 black (2502) is an unreinforced polyamide 6.

Modulus

3.600MPa

Strength

85MPa

Impact

180kJ/m²

AKROMID® B3 black (2502) is an unreinforced polyamide 6.

AKROMID^®

B3 GF 60 black (2497)

PA6 GF60

AKROMID® B3 GF 60 black (2497) is a 60% glass fibre reinforced polyamide 6 with very high rigidity and strength

Modulus

21.000MPa

Strength

240MPa

Impact

90kJ/m²

AKROMID® B3 GF 60 black (2497) is a 60% glass fibre reinforced polyamide 6 with very high rigidity and strength

AKROMID^®

C3 GF 60 1 black (4659)

PA66 + PA6 GF60

AKROMID® C3 GF 60 1 black (4659) is a 60% glass fibre reinforced, heat stabilised polyamide 6.6/6 - Blend.

Modulus

21.300MPa

Strength

270MPa

Impact

96kJ/m²

AKROMID® C3 GF 60 1 black (4659) is a 60% glass fibre reinforced, heat stabilised polyamide 6.6/6 - Blend.

AKROMID^®

A3 GF 25 3 black (3094)

PA66 GF25

AKROMID® A3 GF 25 3 black (3094) is a 25% glass fibre reinforced, nucleated polyamide 6.6 with high stiffness and strength

Modulus

8.500MPa

Strength

160MPa

Impact

50kJ/m²

AKROMID® A3 GF 25 3 black (3094) is a 25% glass fibre reinforced, nucleated polyamide 6.6 with high stiffness and strength

1 66 67 6880

AKROMID^®

C28 GFM 10/20 5 XTC black (7367)PA66+PA6 (GF10+MD20)

AKROMID® C28 GFM 10/20 5 XTC black (7367) is a 10% glass fiber and 20% mineral reinforced, easy flowing polyamide 6.6/6 blend. It is characterised by excellent temperature resistance as well as a very high surface quality. Furthermore, the material impresses with low warpage, resulting in high dimensional stability. It is therefore perfectly suitable for parts in industrial engineering and in the automotive industry, e.g. under the hood, which are exposed to high temperatures.

Features

heat stabilised 230

surface modified

low warpage

easy flow

Properties

Modulus

9.500MPa

Strength

120MPa

Impact

40kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.

1 mm/min | conditioned

9500 MPa

6000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.

5 mm/min | conditioned

120 MPa

80 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.

5 mm/min | conditioned

2,5 %

7 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.

2 mm/min | conditioned

8500 MPa

4300 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.

2 mm/min | conditioned

180 MPa

110 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.

2 mm/min | conditioned

3 %

8 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.

23°C | conditioned

40 kJ/m²

60 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.

23°C | conditioned

4 kJ/m²

6 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa

225 °C

Melting temperature

ISO 11357-3

DSC, 10K/min

245 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel

23°C to 80°C | transverse

0,3 10⁻⁴/K

0,98 10⁻⁴/K

Flammability

Burning rate

UL 94

1,6 mm Wall thickness

HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness

General properties

Density

ISO 1183

23°C

1,38 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.

1,7 %

Molding shrinkage

ISO 294-4

flow

transverse

0,4 - 0,6 %

0,7 - 0,9 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Find the right compound

C28 GFM 10/20 5 XTC black (7367)PA66+PA6 (GF10+MD20)

Mechanical Properties

Tensile modulus

Tensile stress at break

Tensile strain at break

Flexural modulus

Flexural strength

Flexural strain at break

Charpy impact strength

Charpy notched impact strength

Thermal Properties

Temperature of deflection under load HDT/A

Melting temperature

Coefficient of linear thermal expansion

Flammability

Burning rate

Burning rate (<100 mm/min)

General properties

Density

Humidity absorption

Molding shrinkage

Do you have any questions? We are happy to help.

Find the right compound

C28 GFM 10/20 5 XTC black (7367).css-117ixes{line-height:1.5;display:block;margin-top:var(--chakra-space-2);font-weight:var(--chakra-fontWeights-normal);font-size:var(--chakra-fontSizes-sm);color:var(--chakra-colors-kisPrimaryTextLight-700);}PA66+PA6 (GF10+MD20)

Mechanical Properties

Tensile modulus

Tensile stress at break

Tensile strain at break

Flexural modulus

Flexural strength

Flexural strain at break

Charpy impact strength

Charpy notched impact strength

Thermal Properties

Temperature of deflection under load HDT/A

Melting temperature

Coefficient of linear thermal expansion

Flammability

Burning rate

Burning rate (<100 mm/min)

General properties

Density

Humidity absorption

Molding shrinkage