AKROLOY®

Preliminary

PA GF 40 natural (6413)

PA66+PA6I/6T GF40

AKROLOY® PA GF 40 natural (6413) is a 40% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

Modulus

13.000MPa

Strength

235MPa

Impact

95kJ/m²

AKROLOY® PA GF 40 natural (6413) is a 40% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

AKROMID®

B3 ICF 20 LF black (6695)

PA6 CF20

AKROMID® B3 ICF 20 LF black (6695) is a 20 % carbon fiber reinforced, conductive PA6.

Modulus

15.000MPa

Strength

175MPa

Impact

50kJ/m²

AKROMID® B3 ICF 20 LF black (6695) is a 20 % carbon fiber reinforced, conductive PA6.

AKROMID®

Preliminary

B3 GF 30 5 black (8536)

PA6 GF30

AKROMID® B3 GF 30 5 black (8536) - PA6, 30% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.

Modulus

9.500MPa

Strength

170MPa

Impact

60kJ/m²

AKROMID® B3 GF 30 5 black (8536) - PA6, 30% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.

AKROMID®

B3 GF 35 S1 natural (920)

PA6-I GF35

AKROMID® B3 GF 35 S1 natural (920) is a 35% glass fibre reinforced, cold impact strength polyamide 6 with high stiffness and strength and light inherent color

Modulus

11.000MPa

Strength

190MPa

Impact

80kJ/m²

AKROMID® B3 GF 35 S1 natural (920) is a 35% glass fibre reinforced, cold impact strength polyamide 6 with high stiffness and strength and light inherent color

AKROMID®

B3 GF 60 1 natural (2468)

PA6 GF60

AKROMID® B3 GF 60 1 natural (2468) is a 60% glass fibre reinforced heat stabilised polyamide 6 with very high rigidity and strength and light inherent color.

Modulus

21.000MPa

Strength

240MPa

Impact

90kJ/m²

AKROMID® B3 GF 60 1 natural (2468) is a 60% glass fibre reinforced heat stabilised polyamide 6 with very high rigidity and strength and light inherent color.

AKROMID®

B3 GF 60 natural (2476)

PA6 GF60

AKROMID® B3 GF 60 natural (2476) is a 60% glass fibre reinforced polyamide 6 with very high rigidity and strength and light inherent color

Modulus

21.000MPa

Strength

240MPa

Impact

90kJ/m²

AKROMID® B3 GF 60 natural (2476) is a 60% glass fibre reinforced polyamide 6 with very high rigidity and strength and light inherent color

AKROLOY®

PA GF 20 black (5485)

PA66+PA6I/6T GF20

AKROLOY® PA GF 20 black (5485) is a 20% glass fibre reinforced, semi-aromatic polyamide blend with average stiffness and strength, even in conditioned state.

Modulus

7.000MPa

Strength

145MPa

Impact

40kJ/m²

AKROLOY® PA GF 20 black (5485) is a 20% glass fibre reinforced, semi-aromatic polyamide blend with average stiffness and strength, even in conditioned state.

166676880

AKROMID®

B28 GF 50 natural (4842)PA6 GF50

AKROMID® B28 GF 50 natural (4842) - is a 50% glass fiber reinforced polyamide 6. It is characterised by an improved flowability compared to a standard PA 6 GF 50. Furthermore, the material impresses with its high stiffness and strength. It is therefore perfectly suitable for technical applications in industrial engineering, in the furniture industry and in the automotive industry.

Features

easy flow

Properties

Modulus

16.500MPa

Strength

250MPa

Impact

110kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
16500 MPa
10500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
250 MPa
145 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
4,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
15000 MPa
10500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
350 MPa
240 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
110 kJ/m²
120 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
23 kJ/m²
26 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
220 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
185 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,56 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,3 - 1,6 %

Water absorption

ISO 62

23°C, saturated
4,5 - 5,1 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,4 - 0,6 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
conditioned
1013 Ω x cm
1010 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
1012 Ω
1010 Ω

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more