Description

AKROMIDĀ®

B3 GF 25 natural (2471)

PA6 GF25

AKROMIDĀ® B3 GF 25 natural (2471) is a 25% glass fibre reinforced polyamide 6 with high stiffness and strength and light inherent color

Modulus

8.500MPa

Strength

160MPa

Impact

85kJ/mĀ²

AKROMIDĀ® B3 GF 25 natural (2471) is a 25% glass fibre reinforced polyamide 6 with high stiffness and strength and light inherent color

AKROMIDĀ®

B3 GF 60 black (2497)

PA6 GF60

AKROMIDĀ® B3 GF 60 black (2497) is a 60% glass fibre reinforced polyamide 6 with very high rigidity and strength

Modulus

21.000MPa

Strength

240MPa

Impact

90kJ/mĀ²

AKROMIDĀ® B3 GF 60 black (2497) is a 60% glass fibre reinforced polyamide 6 with very high rigidity and strength

AKROMIDĀ®

S3 1 black (3317)

PA610

AKROMIDĀ® S3 1 black (3317) is a nonreinforced and heat stabilised polyamide 6.10 with lower moisture absorption and high chemical resistance.

Modulus

2.400MPa

Strength

70MPa

Impact

180kJ/mĀ²

AKROMIDĀ® S3 1 black (3317) is a nonreinforced and heat stabilised polyamide 6.10 with lower moisture absorption and high chemical resistance.

AKROMIDĀ®

C3 GF 60 1 black (4659)

PA66 + PA6 GF60

AKROMIDĀ® C3 GF 60 1 black (4659) is a 60% glass fibre reinforced, heat stabilised polyamide 6.6/6 - Blend.

Modulus

21.300MPa

Strength

270MPa

Impact

96kJ/mĀ²

AKROMIDĀ® C3 GF 60 1 black (4659) is a 60% glass fibre reinforced, heat stabilised polyamide 6.6/6 - Blend.

AKROMIDĀ®

Preliminary

B3 GF 30 5 black (8536)

PA6 GF30

AKROMIDĀ® B3 GF 30 5 black (8536) - PA6, 30% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.

Modulus

9.500MPa

Strength

170MPa

Impact

60kJ/mĀ²

AKROMIDĀ® B3 GF 30 5 black (8536) - PA6, 30% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.

AKROLOYĀ®

PA GF 50 white (5137)

PA66+PA6I/6T GF50

AKROLOYĀ® PA GF 50 white (5137) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

Modulus

20.000MPa

Strength

250MPa

Impact

105kJ/mĀ²

AKROLOYĀ® PA GF 50 white (5137) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

AKROMIDĀ®

Preliminary

NEXT G3 GF 30 1 L CI natural (8377)

PA6.9 + PP GF30

AKROMIDĀ® NEXT G3 GF 30 1 L CI natural (8377) - PA 6.9/PP blend, bio-based, certified, low moisture absorption, weight reduction.

Modulus

8.000MPa

Strength

125MPa

Impact

65kJ/mĀ²

AKROMIDĀ® NEXT G3 GF 30 1 L CI natural (8377) - PA 6.9/PP blend, bio-based, certified, low moisture absorption, weight reduction.

166676880

AKROMIDĀ®

B3 GF 30 S1 natural (1383)PA6-I GF30

AKROMIDĀ® B3 GF 30 S1 natural (1383) is a 30% glass fiber reinforced, impact modified Polyamide 6. It is characterised by high stiffness and strength as well as a higher impact strength compared to a standard PA 6 GF 30. The material is therefore perfectly suitable for industrial applications and for housings and covers in the automotive industry. The material has a light inherent color.

Features

impact modified

Properties

Modulus

7.500MPa

Strength

125MPa

Impact

110kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
7500 MPa
4200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
125 MPa
70 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
6 %
13 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
6400 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
190 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
10Ā°C | d.a.m.
-
20Ā°C | d.a.m.
-
30Ā°C | d.a.m.
-
40Ā°C | d.a.m.
-
110 kJ/mĀ²
135 kJ/mĀ²
112 kJ/mĀ²
117 kJ/mĀ²
117 kJ/mĀ²
115 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
10Ā°C | d.a.m.
-
20Ā°C | d.a.m.
-
30Ā°C | d.a.m.
-
40Ā°C | d.a.m.
-
35 kJ/mĀ²
40 kJ/mĀ²
25 kJ/mĀ²
25 kJ/mĀ²
25 kJ/mĀ²
20 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
200 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
222 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,28 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,3 - 1,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.