AKROMIDĀ®

A3 GF 40 1 L black (4671)

PA66+PP GF40

AKROMIDĀ® A3 GF 40 1 L black (4671) - PA6.6/PP-Blend, 40% glass fibre reinforced, lower density, cost reduced, zinc chloride

Modulus

11.800MPa

Strength

170MPa

Impact

80kJ/mĀ²

AKROMIDĀ® A3 GF 40 1 L black (4671) - PA6.6/PP-Blend, 40% glass fibre reinforced, lower density, cost reduced, zinc chloride

AKROTEKĀ®

PK-VM ICF 15 black (6074)

PK CF15

AKROTEKĀ® PK-VM ICF 15 black (6074) is a 15% carbon fibre reinforced polyketon with good sliding properties.

Modulus

9.000MPa

Strength

90MPa

Impact

30kJ/mĀ²

AKROTEKĀ® PK-VM ICF 15 black (6074) is a 15% carbon fibre reinforced polyketon with good sliding properties.

AKROTEKĀ®

PK-HM 8 natural (6145)

PK

AKROTEKĀ® PK-HM 8 natural (6145) - Polyketon, unreinforced, Tribology, friction and wear, chemical resistance, EU 10/2011, FDA 21 CFR

Modulus

1.400MPa

Strength

60MPa

Impact

180kJ/mĀ²

AKROTEKĀ® PK-HM 8 natural (6145) - Polyketon, unreinforced, Tribology, friction and wear, chemical resistance, EU 10/2011, FDA 21 CFR

PRECITEĀ®

Preliminary

E GF 20 natural (7301)

PET GF 20

PRECITEĀ® E GF 20 natural (7301) - PET, 20% glass fibre, good stiffness, good toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

7.800MPa

Strength

145MPa

Impact

40kJ/mĀ²

PRECITEĀ® E GF 20 natural (7301) - PET, 20% glass fibre, good stiffness, good toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

AKROMIDĀ®

Preliminary

A3 black (7557)

PA66

AKROMIDĀ® A3 black (7557) is an unreinforced, UV stabilised polyamide 6.6.

Modulus

3.200MPa

Strength

80MPa

Impact

180kJ/mĀ²

AKROMIDĀ® A3 black (7557) is an unreinforced, UV stabilised polyamide 6.6.

AKROMIDĀ®

B3 GF 35 S1 natural (920)

PA6-I GF35

AKROMIDĀ® B3 GF 35 S1 natural (920) is a 35% glass fibre reinforced, cold impact strength polyamide 6 with high stiffness and strength and light inherent color

Modulus

11.000MPa

Strength

190MPa

Impact

80kJ/mĀ²

AKROMIDĀ® B3 GF 35 S1 natural (920) is a 35% glass fibre reinforced, cold impact strength polyamide 6 with high stiffness and strength and light inherent color

AKROMIDĀ®

UL
Preliminary

B3 GF 30 1 HU LA black (2862)

PA6 GF30

AKROMIDĀ® B3 GF 30 1 HU LA black (2862) - PA 6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB, laser markable, automotive, E&E, industry.

Modulus

10.300MPa

Strength

185MPa

Impact

95kJ/mĀ²

AKROMIDĀ® B3 GF 30 1 HU LA black (2862) - PA 6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL listed HB, laser markable, automotive, E&E, industry.

166676880

AKROMIDĀ®

B3 GFM 15/25 black (1312)PA6 (GF15+MD25)

AKROMIDĀ® B3 GFM 15/25 black (1312) is a 15% glass fibre reinforced, 25% mineral filled polyamide 6 with good surface and dimensional stability

Features

surface modified
low warpage

Properties

Modulus

8.000MPa

Strength

120MPa

Impact

50kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
8000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
120 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
3 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
7000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
190 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
50 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
4 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
190 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
216 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
222 Ā°C

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
160 - 175 Ā°C
130 - 150 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,45 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,8 %

Water absorption

ISO 62

23Ā°C, saturated
6,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 %
0,9 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
1012 ā„¦ x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1015 ā„¦

Comparative tracking index

IEC 60112

Test liquid A
400 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more