AKROMIDĀ®

Preliminary

B28 GF 15 natural (6940)

PA6 GF 15

AKROMID B28 GF 15 natural (6940) - PA 6, glass fiber reinforced, easy flow, good surface, bus fire standard ECE R 118.03, medium stiffness and strength.

Modulus

5.300MPa

Strength

120MPa

Impact

39kJ/mĀ²

AKROMID B28 GF 15 natural (6940) - PA 6, glass fiber reinforced, easy flow, good surface, bus fire standard ECE R 118.03, medium stiffness and strength.

AKROTEKĀ®

Preliminary

PK-VM GF 15 8 black (6991)

PK GF15

AKROTEKĀ® PK-VM GF 15 8 black (6991) - Polyketon, 15% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

Modulus

4.500MPa

Strength

95MPa

Impact

55kJ/mĀ²

AKROTEKĀ® PK-VM GF 15 8 black (6991) - Polyketon, 15% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

AKROLOYĀ®

PA GF 50 white (5137)

PA66+PA6I/6T GF50

AKROLOYĀ® PA GF 50 white (5137) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

Modulus

20.000MPa

Strength

250MPa

Impact

105kJ/mĀ²

AKROLOYĀ® PA GF 50 white (5137) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

AKROLOYĀ®

PA GF 20 black (5485)

PA66+PA6I/6T GF20

AKROLOYĀ® PA GF 20 black (5485) is a 20% glass fibre reinforced, semi-aromatic polyamide blend with average stiffness and strength, even in conditioned state.

Modulus

7.000MPa

Strength

145MPa

Impact

40kJ/mĀ²

AKROLOYĀ® PA GF 20 black (5485) is a 20% glass fibre reinforced, semi-aromatic polyamide blend with average stiffness and strength, even in conditioned state.

AKROTEKĀ®

PK-VM ICF 15 black (6074)

PK CF15

AKROTEKĀ® PK-VM ICF 15 black (6074) is a 15% carbon fibre reinforced polyketon with good sliding properties.

Modulus

9.000MPa

Strength

90MPa

Impact

30kJ/mĀ²

AKROTEKĀ® PK-VM ICF 15 black (6074) is a 15% carbon fibre reinforced polyketon with good sliding properties.

AKROTEKĀ®

PK-VM GF 50 8 black (6936)

PK GF50

AKROTEKĀ® PK-VM GF 50 8 black (6939) - Polyketon, 50% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

Modulus

14.000MPa

Strength

170MPa

Impact

50kJ/mĀ²

AKROTEKĀ® PK-VM GF 50 8 black (6939) - Polyketon, 50% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

AKROTEKĀ®

PK-VM GF 30 8 natural (6983)

PK GF30

AKROTEKĀ® PK-VM GF 30 8 natural (6983) - Polyketon, 30% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

Modulus

8.200MPa

Strength

130MPa

Impact

60kJ/mĀ²

AKROTEKĀ® PK-VM GF 30 8 natural (6983) - Polyketon, 30% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

165666780

AKROMIDĀ®

A3 CF 30 5 black (7488)PA66 CF30

AKROMIDĀ® A3 CF 30 5 black (7488) is a 30% carbon fibre reinforced, high temperature stabilised polyamide 6.6 with elevated mechanical properties and good sliding properties.

Features

heat stabilised 160

Properties

Modulus

26.000MPa

Strength

285MPa

Impact

90kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
26000 MPa
17500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
285 MPa
200 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2 %
3,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
23000 MPa
17000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
400 MPa
300 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
90 kJ/mĀ²
110 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
40Ā°C | d.a.m.
-
10 kJ/mĀ²
13 kJ/mĀ²
8 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
254 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
260 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,26 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,8 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
104 ā„¦ x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
104 ā„¦

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more