AKROMID®

B3 ICF 20 LF black (6695)

PA6 CF20

AKROMID® B3 ICF 20 LF black (6695) is a 20 % carbon fiber reinforced, conductive PA6.

Modulus

15.000MPa

Strength

175MPa

Impact

50kJ/m²

AKROMID® B3 ICF 20 LF black (6695) is a 20 % carbon fiber reinforced, conductive PA6.

PRECITE®

Preliminary

P3 GF 40 natural (6943)

PBT GF 40

PRECITE® P3 GF 40 natural (6943) is a 40% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

Modulus

13.500MPa

Strength

175MPa

Impact

70kJ/m²

PRECITE® P3 GF 40 natural (6943) is a 40% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

AKROLOY®

Preliminary

PA GF 60 LA black (8168)

PA66 + PA6I/6T GF60

AKROLOY® PA GF 60 LA black (8168) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

Modulus

21.400MPa

Strength

275MPa

Impact

95kJ/m²

AKROLOY® PA GF 60 LA black (8168) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

AKROMID®

Preliminary

NEXT G3 GF 30 1 L CR black (8314)

PA6.9 + PP GF30

AKROMID® NEXT G3 GF 30 1 L CI black (8314) - PA 6.9/PP blend, bio-based, certified, low moisture absorption, weight reduction.

Modulus

8.000MPa

Strength

125MPa

Impact

65kJ/m²

AKROMID® NEXT G3 GF 30 1 L CI black (8314) - PA 6.9/PP blend, bio-based, certified, low moisture absorption, weight reduction.

AKROMID®

Preliminary

NEXT U3 ICF 20 1 black (8232)

PA11 CF20

AKROMID® NEXT U3 ICF 20 1 black (8232) - PA11 made of renewable raw materials, recycled carbon fibre, low density, Fused Filament Fabrication

Modulus

9.300MPa

Strength

110MPa

Impact

60kJ/m²

AKROMID® NEXT U3 ICF 20 1 black (8232) - PA11 made of renewable raw materials, recycled carbon fibre, low density, Fused Filament Fabrication

AKROMID®

B3 GF 25 natural (2471)

PA6 GF25

AKROMID® B3 GF 25 natural (2471) is a 25% glass fibre reinforced polyamide 6 with high stiffness and strength and light inherent color

Modulus

8.500MPa

Strength

160MPa

Impact

85kJ/m²

AKROMID® B3 GF 25 natural (2471) is a 25% glass fibre reinforced polyamide 6 with high stiffness and strength and light inherent color

AKROMID®

A3 1 L black (4652)

PA66 + PP

AKROMID® A3 1 L black (4652) - unreinforced PA6.6/PP-Blend lightweight, cost reduced

Modulus

2.300MPa

Strength

54MPa

Impact

180kJ/m²

AKROMID® A3 1 L black (4652) - unreinforced PA6.6/PP-Blend lightweight, cost reduced

165666780

AKROMID®

A3 GF 30 4 black (3571)PA66 GF30

AKROMID® A3 GF 30 4 black (3571) is a 30% glass fiber reinforced polyamide 6.6. It is characterised by high stiffness and strength. Furthermore, the material is hydrolysis and chemically stabilised and therefore perfectly suitable for e.g. cooling systems in the automotive industry.

Features

hydrolysis / chemically stabilised

Properties

Modulus

11.500MPa

Strength

210MPa

Impact

80kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
11500 MPa
6800 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
210 MPa
140 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,5 %
7 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
10000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
310 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
4,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
80 kJ/m²
100 kJ/m²
65 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
12 kJ/m²
20 kJ/m²
9 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
250 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
260 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
205 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,37 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,7 - 0,9 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
conditioned
1013 Ω x cm
1010 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
1012 Ω
1010 Ω

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.