AKROMIDĀ®

A3 GF 25 3 black (3094)

PA66 GF25

AKROMIDĀ® A3 GF 25 3 black (3094) is a 25% glass fibre reinforced, nucleated polyamide 6.6 with high stiffness and strength

Modulus

8.500MPa

Strength

160MPa

Impact

50kJ/mĀ²

AKROMIDĀ® A3 GF 25 3 black (3094) is a 25% glass fibre reinforced, nucleated polyamide 6.6 with high stiffness and strength

AKROMIDĀ®

Preliminary

S3 GF 30 4 black (3429)

PA610 GF30

AKROMIDĀ® S3 GF 30 4 black (3429) is a 30% glass fibre reinforced and hydrolysis stabilised polyamide 6.10 with high stiffness and strength as well as lower moisture absorption and very high chemical resistance.

Modulus

8.600MPa

Strength

160MPa

Impact

110kJ/mĀ²

AKROMIDĀ® S3 GF 30 4 black (3429) is a 30% glass fibre reinforced and hydrolysis stabilised polyamide 6.10 with high stiffness and strength as well as lower moisture absorption and very high chemical resistance.

AKROMIDĀ®

C3 GF 60 1 black (4659)

PA66 + PA6 GF60

AKROMIDĀ® C3 GF 60 1 black (4659) is a 60% glass fibre reinforced, heat stabilised polyamide 6.6/6 - Blend.

Modulus

21.300MPa

Strength

270MPa

Impact

96kJ/mĀ²

AKROMIDĀ® C3 GF 60 1 black (4659) is a 60% glass fibre reinforced, heat stabilised polyamide 6.6/6 - Blend.

AKROTEKĀ®

PK-HM black (4953)

PK

AKROTEKĀ® PK-HM black (4953) - Polyketon, Tribology, friction and wear, chemical resistance

Modulus

1.500MPa

Strength

60MPa

Impact

180kJ/mĀ²

AKROTEKĀ® PK-HM black (4953) - Polyketon, Tribology, friction and wear, chemical resistance

AKROMIDĀ®

Preliminary

T5 8 black (6454)

PPA

AKROMIDĀ® T5 8 black (6454) - PPA, unreinforced, food contact, kitchen and household appliances, fitting, ACS, WRAS, NSF 61, EU 10/2011, FDA

Modulus

3.800MPa

Strength

75MPa

Impact

40kJ/mĀ²

AKROMIDĀ® T5 8 black (6454) - PPA, unreinforced, food contact, kitchen and household appliances, fitting, ACS, WRAS, NSF 61, EU 10/2011, FDA

AKROMIDĀ®

UL

B3 1 black (6528)

PA6

AKROMIDĀ® B3 1 black (6528) is an unreinforced, heat stabilised polyamide 6

Modulus

3.600MPa

Strength

85MPa

Impact

180kJ/mĀ²

AKROMIDĀ® B3 1 black (6528) is an unreinforced, heat stabilised polyamide 6

PRECITEĀ®

Preliminary

K GF 15 natural (7439)

PBT-PET- GF 15

PRECITE K GF 15 natural (7439) is a 15% glass fibre reinforced PBT/PET blend with high strength and improved surface finish.

Modulus

6.000MPa

Strength

115MPa

Impact

30kJ/mĀ²

PRECITE K GF 15 natural (7439) is a 15% glass fibre reinforced PBT/PET blend with high strength and improved surface finish.

165666780

AKROMIDĀ®

B3 GF 50 1 black (20008)PA6 GF50

AKROMIDĀ® B3 GF 50 black (20008) is a 50% glass fiber reinforced polyamide 6. It is characterised by a very high stiffness and strength. Furthermore, the material is heat stabilised and therefore perfectly suitable for technical parts in industrial engineering and in the automotive industry, e.g. strut bearings.

Features

heat stabilised 130

Properties

Modulus

17.000MPa

Strength

210MPa

Impact

100kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
17000 MPa
11000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
210 MPa
140 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
16500 MPa
11000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
330 MPa
230 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
3 %
5 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
100 kJ/mĀ²
100 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
18 kJ/mĀ²
23 kJ/mĀ²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
270 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
220 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 Ā°C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
185 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 Ā°C

Coefficient of linear thermal expansion

ISO 11359-1/2

23Ā°C to 80Ā°C | parallel
23Ā°C to 80Ā°C | transverse
0,11 10ā»ā“/K
0,94 10ā»ā“/K

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
160 - 175 Ā°C
130 - 150 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
650 Ā°C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,56 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,3 -1,6 %

Water absorption

ISO 62

23Ā°C, saturated
4,5 - 5,1 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,4 - 0,6 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
conditioned
1013 ā„¦ x cm
1010 ā„¦ x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
1012 ā„¦
1010 ā„¦

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more