AKROMID®
A3 GFM 25/15 1 black (3335)
PA66 (GF25+MD15)
AKROMID® A3 GFM 25/15 1 black (3335) is a 25% glass fibre reinforced, 15% mineral filled, heat stabilised polyamide 6.6 with good surface and dimensional stability
10.000MPa
150MPa
50kJ/m²
AKROMID® A3 GFM 25/15 1 black (3335) is a 25% glass fibre reinforced, 15% mineral filled, heat stabilised polyamide 6.6 with good surface and dimensional stability
AKROTEK®
PK-HM black (4953)
PK
AKROTEK® PK-HM black (4953) - Polyketon, Tribology, friction and wear, chemical resistance
1.500MPa
60MPa
180kJ/m²
AKROTEK® PK-HM black (4953) - Polyketon, Tribology, friction and wear, chemical resistance
AKROMID®
B3 GF 40 1 black (2487)
PA6 GF40
AKROMID® B3 GF 40 1 black (2487) is a 40% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength.
12.800MPa
205MPa
100kJ/m²
AKROMID® B3 GF 40 1 black (2487) is a 40% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength.
AKROMID®
B3 GF 50 9 RM-M natural (3698)
PA6 + X GF50
AKROMID® B3 GF 50 9 RM-M natural (3698) is a 50% glass fibre reinforced, process improved polyamide 6 with very high stiffness and strength, limited moisture absorption and light inherent color.
16.000MPa
210MPa
70kJ/m²
AKROMID® B3 GF 50 9 RM-M natural (3698) is a 50% glass fibre reinforced, process improved polyamide 6 with very high stiffness and strength, limited moisture absorption and light inherent color.
AKROMID®
A3 CF 20 black (3132)
PA66 CF20
AKROMID® A3 CF 20 black (3132) is a 20% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties
15.000MPa
200MPa
40kJ/m²
AKROMID® A3 CF 20 black (3132) is a 20% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties
AKROMID®
B3 GF 60 1 natural (2468)
PA6 GF60
AKROMID® B3 GF 60 1 natural (2468) is a 60% glass fibre reinforced heat stabilised polyamide 6 with very high rigidity and strength and light inherent color.
21.000MPa
240MPa
90kJ/m²
AKROMID® B3 GF 60 1 natural (2468) is a 60% glass fibre reinforced heat stabilised polyamide 6 with very high rigidity and strength and light inherent color.
AKROMID®
S3 GF 30 4 natural (3552)
PA6.10
AKROMID® S3 GF 30 4 natural (3552) is a 30% glass fibre reinforced and hydrolysis stabilised polyamide 6.10 with high stiffness and strength as well as lower moisture absorption and very high chemical resistance
8.600MPa
160MPa
110kJ/m²
AKROMID® S3 GF 30 4 natural (3552) is a 30% glass fibre reinforced and hydrolysis stabilised polyamide 6.10 with high stiffness and strength as well as lower moisture absorption and very high chemical resistance
AKROMID®
AKROMID® NEXT G3 GF 30 1 L CR black (8314) is a 30% glass fiber reinforced PA 6.9/PP blend with high strength and stiffness. The partially bio-based grade is characterised by particularly low moisture absorption and high chemical resistance compared to classic PA 6 and PA 6.6. It is suitable for applications where weight reduction and sustainability are required. The material is certified according to REDcert². 33% of the fossil raw materials required for manufacturing this product were replaced by sustainable biomass-balanced PP (≙ allocation factor).
Features
Regulatory
Properties
8.000MPa
125MPa
65kJ/m²
ISO 527-2
ISO 527-2
ISO 527-2
ISO 179-1/1eU
ISO 179-1/1eA
ISO 11357-3
ISO 1183
ISO 1110
ISO 62
ISO 294-4
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.