AKROLOYĀ®

PA GF 20 black (5485)

PA66+PA6I/6T GF20

AKROLOYĀ® PA GF 20 black (5485) is a 20% glass fibre reinforced, semi-aromatic polyamide blend with average stiffness and strength, even in conditioned state.

Modulus

7.000MPa

Strength

145MPa

Impact

40kJ/mĀ²

AKROLOYĀ® PA GF 20 black (5485) is a 20% glass fibre reinforced, semi-aromatic polyamide blend with average stiffness and strength, even in conditioned state.

AKROMIDĀ®

UL

B3 1 black (6528)

PA6

AKROMIDĀ® B3 1 black (6528) is an unreinforced, heat stabilised polyamide 6

Modulus

3.600MPa

Strength

85MPa

Impact

180kJ/mĀ²

AKROMIDĀ® B3 1 black (6528) is an unreinforced, heat stabilised polyamide 6

AKROMIDĀ®

A3 GK 30 6 black (6670)

PA66 GK30

AKROMIDĀ® A3 GK 30 6 black (6670) - 30% glass bead, inorganic high temperature stabilised, polyamide 6.6, low warpage, high surface appearance

Modulus

4.600MPa

Strength

86MPa

Impact

20kJ/mĀ²

AKROMIDĀ® A3 GK 30 6 black (6670) - 30% glass bead, inorganic high temperature stabilised, polyamide 6.6, low warpage, high surface appearance

PRECITEĀ®

Preliminary

P3 GF 30 S1 natural (6853)

PBT-GF 30

PRECITEĀ® P3 GF 30 S1 natural (6853) is a 30% glass fibre reinforced, impact modified, medium viscous poly(butylene terephthalate) (PBT) with high stiffness and strength and lower density compared to neat PBT.

Modulus

9.500MPa

Strength

135MPa

Impact

85kJ/mĀ²

PRECITEĀ® P3 GF 30 S1 natural (6853) is a 30% glass fibre reinforced, impact modified, medium viscous poly(butylene terephthalate) (PBT) with high stiffness and strength and lower density compared to neat PBT.

AKROTEKĀ®

PK-VM GF 50 8 black (6936)

PK GF50

AKROTEKĀ® PK-VM GF 50 8 black (6939) - Polyketon, 50% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

Modulus

14.000MPa

Strength

170MPa

Impact

50kJ/mĀ²

AKROTEKĀ® PK-VM GF 50 8 black (6939) - Polyketon, 50% glass fiber, Tribology, friction and wear, chemical resistance, food contact, EU 10/2011, FDA

AKROMIDĀ®

Preliminary

A3 black (7557)

PA66

AKROMIDĀ® A3 black (7557) is an unreinforced, UV stabilised polyamide 6.6.

Modulus

3.200MPa

Strength

80MPa

Impact

180kJ/mĀ²

AKROMIDĀ® A3 black (7557) is an unreinforced, UV stabilised polyamide 6.6.

AKROLOYĀ®

PA GF 60 black (7789)

PA66+PA6I/6T GF60

AKROLOYĀ® PA GF 60 black (7789) is a 60% glass fibre reinforced, easyflow, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

Modulus

21.400MPa

Strength

290MPa

Impact

100kJ/mĀ²

AKROLOYĀ® PA GF 60 black (7789) is a 60% glass fibre reinforced, easyflow, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

164656680

AKROMIDĀ®

A3 CF 30 5 black (7488)PA66 CF30

AKROMIDĀ® A3 CF 30 5 black (7488) is a 30% carbon fibre reinforced, high temperature stabilised polyamide 6.6 with elevated mechanical properties and good sliding properties.

Features

heat stabilised 160

Properties

Modulus

26.000MPa

Strength

285MPa

Impact

90kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
26000 MPa
17500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
285 MPa
200 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2 %
3,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
23000 MPa
17000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
400 MPa
300 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
90 kJ/mĀ²
110 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
40Ā°C | d.a.m.
-
10 kJ/mĀ²
13 kJ/mĀ²
8 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
254 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
260 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,26 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,8 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
104 ā„¦ x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
104 ā„¦

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more