PRECITE®

Preliminary

P3 GF 25 9 FR natural (8212)

PBT GF25 FR(40)

PRECITE® P3 GF 25 9 FR natural (8212) - PBT, 25% glass fiber, flame retardant, high stiffness and strength, good long-term heat-aging, E-Mobility, E&E industry.

Modulus

8.500MPa

Strength

123MPa

Impact

53kJ/m²

PRECITE® P3 GF 25 9 FR natural (8212) - PBT, 25% glass fiber, flame retardant, high stiffness and strength, good long-term heat-aging, E-Mobility, E&E industry.

AKROMID®

Preliminary

NEXT 5.6 3 GF 30 S3 black (8444)

PA56 GF30

AKROMID® NEXT 5.6 3 GF 30 S3 black (8444) - partly bio-based and HMD-free PA 5.6, 30 % GF, impact modified, high strength and stiffness.

Modulus

8.600MPa

Strength

180MPa

Impact

96kJ/m²

AKROMID® NEXT 5.6 3 GF 30 S3 black (8444) - partly bio-based and HMD-free PA 5.6, 30 % GF, impact modified, high strength and stiffness.

AKROMID®

B3 GF 40 1 natural (2466)

PA6 GF40

AKROMID® B3 GF 40 1 natural (2466) is a 40% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength and light inherent color

Modulus

12.800MPa

Strength

205MPa

Impact

100kJ/m²

AKROMID® B3 GF 40 1 natural (2466) is a 40% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength and light inherent color

AKROMID®

A3 GFM 25/15 1 black (3335)

PA66 (GF25+MD15)

AKROMID® A3 GFM 25/15 1 black (3335) is a 25% glass fibre reinforced, 15% mineral filled, heat stabilised polyamide 6.6 with good surface and dimensional stability

Modulus

10.000MPa

Strength

150MPa

Impact

50kJ/m²

AKROMID® A3 GFM 25/15 1 black (3335) is a 25% glass fibre reinforced, 15% mineral filled, heat stabilised polyamide 6.6 with good surface and dimensional stability

AKROMID®

S3 GF 30 4 natural (3552)

PA6.10

AKROMID® S3 GF 30 4 natural (3552) is a 30% glass fibre reinforced and hydrolysis stabilised polyamide 6.10 with high stiffness and strength as well as lower moisture absorption and very high chemical resistance

Modulus

8.600MPa

Strength

160MPa

Impact

110kJ/m²

AKROMID® S3 GF 30 4 natural (3552) is a 30% glass fibre reinforced and hydrolysis stabilised polyamide 6.10 with high stiffness and strength as well as lower moisture absorption and very high chemical resistance

AKROLOY®

Preliminary

PA GF 30 black (6415)

PA66+PA6I/6T GF30

AKROLOY® PA GF 30 black (6415) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.

Modulus

9.800MPa

Strength

200MPa

Impact

65kJ/m²

AKROLOY® PA GF 30 black (6415) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.

AKROTEK®

PK-VM 8 black (6466)

PK

AKROTEK® PK-VM 8 black (6466) - Polyketon, Tribology, friction and wear, chemical resistance, food, drinking water, EU 10/2011

Modulus

1.600MPa

Strength

60MPa

Impact

180kJ/m²

AKROTEK® PK-VM 8 black (6466) - Polyketon, Tribology, friction and wear, chemical resistance, food, drinking water, EU 10/2011

164656680

AKROLOY®

PA GF 50 8 black (6732)PA66+PA6I/6T GF50

AKROLOY® PA GF 50 8 black (6732) is a 50% glass fiber reinforced, semi-aromatic polyamide blend. It is characterised by lower moisture absorption compared to standard PA 6.6 compounds, thus convincing through very high stiffness and strength even in the conditioned state. The material is therefore perfectly suitable for technical applications with high demands for dimensional stability. Furthermore, it can be used as an alternative for aluminium and zinc diecast alloys. The compound fulfill FDA, EU10/2011 and ACS.

Features

reduced moisture

Regulatory

acseu102011fda

Properties

Modulus

17.500MPa

Strength

260MPa

Impact

105kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
17500 MPa
16000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
260 MPa
185 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,4 %
2,4 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
16500 MPa
15000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
385 MPa
285 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
2,8 %
2,9 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
105 kJ/m²
105 kJ/m²
95 kJ/m²
95 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
17 kJ/m²
17 kJ/m²
17 kJ/m²
17 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
245 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
185 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
255 °C

General properties

Density

ISO 1183

23°C
1,56 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,3 - 1,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,3 - 0,5 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more