Deutsch

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa

Tensile Strengthin MPa

Charpy impact strengthin kJ/m²

AKROMID

392

PRECITE

AKROTEK

AKROLOY

AKROLEN

AKROMID

PA6.6

108

PA6

199

PA6.6/6

PPA

PA11

PA5.6

PA5.10

PA6.9

PA6.10

PA6.12

AKROLOY

PARA

PA6.6/PA6I-6T

PRECITE

PBT

PET

PBT/PET

PBT/ASA

AKROTEK

AKROLEN

Sustainability

recycled content

biomass balanced

Bio-based

Stabilisation

heat stabilised 130

188

heat stabilised 160

heat stabilised 230

hydrolysis / chemically stabilised

UV-stabilised

electrically neutral

Modification

flame retardant

impact modified

laser markable

laser transparent

surface modified

low warpage

reduced density

reduced moisture

antistatic/conductive

adhesion modified

tribological modified

Processing

easy flow

process improved

fluid injection (GIT/WIT/FIT)

3D printing / additive manufacturing

nucleated

Special Application Field

E&E

public transportation

lightweight construction

metal substitution

household appliances

Sports & leisure

radar applications

E-Mobility

glass fibre

395

unreinforced

carbon fibre

glass bead

glass fibre/glass bead

glass fibre/mineral

mineral

long glass fibre

glass fibre/carbon fibre

558 Compounds found

Recommended

Tensile Modulus

Tensile Strength

Charpy impact strength

Description

AKROMID^®

B3 GF 25 natural (2471)

PA6 GF25

AKROMID® B3 GF 25 natural (2471) is a 25% glass fibre reinforced polyamide 6 with high stiffness and strength and light inherent color

Modulus

8.500MPa

Strength

160MPa

Impact

85kJ/m²

AKROMID® B3 GF 25 natural (2471) is a 25% glass fibre reinforced polyamide 6 with high stiffness and strength and light inherent color

AKROMID^®

B3 GF 20 black (2491)

PA6 GF20

AKROMID® B3 GF 20 black (2491) is a 20% glass fibre reinforced polyamide 6 with medium stiffness and strength

Modulus

6.800MPa

Strength

150MPa

Impact

73kJ/m²

AKROMID® B3 GF 20 black (2491) is a 20% glass fibre reinforced polyamide 6 with medium stiffness and strength

AKROMID^®

B3 GF 40 1 natural (2466)

PA6 GF40

AKROMID® B3 GF 40 1 natural (2466) is a 40% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength and light inherent color

Modulus

12.800MPa

Strength

205MPa

Impact

100kJ/m²

AKROMID® B3 GF 40 1 natural (2466) is a 40% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength and light inherent color

AKROMID^®

B3 black (2502)

PA6

AKROMID® B3 black (2502) is an unreinforced polyamide 6.

Modulus

3.600MPa

Strength

85MPa

Impact

180kJ/m²

AKROMID® B3 black (2502) is an unreinforced polyamide 6.

AKROMID^®

B3 GF 60 natural (2476)

PA6 GF60

AKROMID® B3 GF 60 natural (2476) is a 60% glass fibre reinforced polyamide 6 with very high rigidity and strength and light inherent color

Modulus

21.000MPa

Strength

240MPa

Impact

90kJ/m²

AKROMID® B3 GF 60 natural (2476) is a 60% glass fibre reinforced polyamide 6 with very high rigidity and strength and light inherent color

AKROMID^®

B3 GF 60 black (2497)

PA6 GF60

AKROMID® B3 GF 60 black (2497) is a 60% glass fibre reinforced polyamide 6 with very high rigidity and strength

Modulus

21.000MPa

Strength

240MPa

Impact

90kJ/m²

AKROMID® B3 GF 60 black (2497) is a 60% glass fibre reinforced polyamide 6 with very high rigidity and strength

AKROMID^®

B3 1 natural (2499)

PA6

AKROMID® B3 1 natural (2499) is an unreinforced, heat stabilised polyamide 6 with light inherent color

Modulus

3.600MPa

Strength

85MPa

Impact

180kJ/m²

AKROMID® B3 1 natural (2499) is an unreinforced, heat stabilised polyamide 6 with light inherent color

1 64 65 6680

AKROMID^®

Internal

B28 GF 25 9 natural (6360)PA6 GF25

AKROMID® B28 GF 25 9 natural (6360) is a 25% glass fibre reinforced, processing optimised polyamide 6 with high rigidity and strength and light inherent color.

Properties

Modulus

8.000MPa

Strength

168MPa

Impact

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.

8000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.

168 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.

3,4 %

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min

220 °C

Flammability

Burning rate

UL 94

0,4 mm Wall thickness

0,8 mm Wall thickness

1,6 mm Wall thickness

3,2 mm Wall thickness

HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness

Protection Bus

ECE 118

Appendix 6, 7, 8

General properties

Density

ISO 1183

23°C

1,3 g/cm³

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.